Alkylamine-Grafted Molybdenum Disulfide Nanosheets for Enhanced Dispersion Stability and Lubricity Properties
Guxia Wang,Changxing Yang,Qingyan Bai,Kun Guan,Yue Shang,Dan Li,Shengwei Guo
DOI: https://doi.org/10.1021/acs.langmuir.3c01699
IF: 3.9
2023-08-24
Langmuir
Abstract:The unique structure and ultralow interlayer shear strength give molybdenum disulfide (MoS<sub>2</sub>) materials a broad prospect for energy savings, economic benefits, and extended operating life of lubrication systems. Herein, we prepared an effective integration strategy to prepare novel small-sized and chemically grafted MoS<sub>2</sub> to solve the problems of poor dispersibility and easy agglomeration of MoS<sub>2</sub>. The MoS<sub>2</sub> powder was stripped and oxidized to generate active centers using acid oxidation and high-speed ultrasonic crushing to obtain two different types of alkylamine chemically, covalently grafted, oxidized MoS<sub>2</sub> nanosheets as lubricant additives to achieve friction reduction and antiwear. The chemical changes and structural characteristics of different types of alkylamine molecules upon covalent interaction with oxidized MoS<sub>2</sub> were investigated in detail by FTIR, XPS, TGA, XRD, and TEM analyses. The results showed that the alkylamine-grafted MoS<sub>2</sub> oxide nanosheets had good dispersion in 15# industrial white oil, and friction experiments confirmed that the alkylamine-grafted MoS<sub>2</sub> oxide (MoS<sub>2</sub>-O-OLA) nanosheets exhibited better friction and wear resistance such that, compared with pure 15# industrial white oil, the 0.02 wt % MoS<sub>2</sub>-O-OLA nanosheets could significantly reduce friction (36.2%) and wear (22.4%). The field-emission scanning electron microscopy (FESEM) and EDS analyses of the wear surface showed that MoS<sub>2</sub>-O-OLA nanosheets play an important role in improving tribological properties by generating interlayer slippage at the steel ball contact interface, thereby forming surface protection and a uniform oil film.
chemistry, multidisciplinary, physical,materials science