Abstract:Increasing studies have demonstrated excellent tribological properties of graphene as lubricant additive. Thus, extended explanations of the relationship between microstructure and tribological properties are needed. This paper reported the effects of thickness and particle size of graphene on its frictional performance, using a ball-on-plate tribotester under reciprocating condition. Graphene with few-layer (G2) or multi-layer (G10) structure was added to PAO4 as lubricant additive. The particle of G10 was further separated through centrifugation into two types, large size G10 (G10L) and small size G10 (G10S). G10S exhibits excellent reduction in friction (37%) and wear (47%) relative to the neat base oil, indicating the superior tribological properties of graphene with more layers and smaller particle size. Wear scar analysis shows that the surface lubricated with G10 is flatter and glossier than that of G2. It can be hypothesized that the interlaminar shear slip is more likely to occur in multi-layer graphene, leading to better friction reduction and wear resistance performance. Graphene with smaller particle size is not only less prone to structural defects and wrinkles, but also more easily adsorbed onto the sliding surface to form a lubricating film, providing enhanced wear and frictional performance. The present work suggests that the thickness and size may have direct influence on the tribological properties of graphene, providing theoretical and experimental guidance for the application of graphene as lubricant additive.

Tribological properties of graphene quantum dot hybrid polyethylene glycol lubricated molybdenum disulfide films

Tribological properties of bismaleimide-based self-lubricating composite enhanced by MoS2 quantum dots/graphene hybrid

Enhancement of Friction Performance Enabled by a Synergetic Effect Between Graphene Oxide and Molybdenum Disulfide

The Application of Nano-MoS2 Quantum Dots as Liquid Lubricant Additive for Tribological Behavior Improvement

Tribochemical mechanism of superlubricity in graphene quantum dots modified DLC films under high contact pressure

Tribological properties of graphene-modified with ionic liquids and carbon quantum dots/ bismaleimide composites

Synergistic lubricating effect of graphene/ionic liquid composite material used as an additive

Enhancement of Friction Performance of Fluorinated Graphene and Molybdenum Disulfide Coating by Microdimple Arrays

Self-organized transfer film-induced ultralow friction of Graphene/MoWS4 heterostructure nanocomposite

Tribological properties of graphene oxide and polyethylene glycol composites under dry friction and oil lubrication conditions

Synergistic lubricating behaviors of graphene and MoS 2 dispersed in esterified bio-oil for steel/steel contact

Preparation and tribological behaviors of poly (ether ether ketone) nanocomposite films containing graphene oxide nanosheets

Effects of Thickness and Particle Size on Tribological Properties of Graphene as Lubricant Additive

Polyethylene glycol derived carbon quantum dots nanofluids: An excellent lubricant for diamond-like carbon film/bearing steel contact

Preparation and tribological properties of Mo/MoS2-Pb-PbS composite films

Laser irradiation-induced laminated graphene/MoS2 composites with synergistically improved tribological properties

Water-Soluble Graphene Quantum Dots as High-Performance Water-Based Lubricant Additive for Steel/Steel Contact

The Tribological Properties of Solid Lubrication Graphite Coatings Prepared by a Sol-Gel Method

Graphene-induced reconstruction of the sliding interface assisting the improved lubricity of various tribo-couples

Modified graphene as novel lubricating additive with high dispersion stability in oil

Black Phosphorus Quantum Dots in Aqueous Environments as Lubricants