Abstract:Diphenyl carbonate (DPC) and diphenyl ketone (DPK) were used as diluents to prepare microporous polyvinylidene fluoride (PVDF) membranes via thermally induced phase-separation (TIPS) method. The liquid - liquid phase-separation phenomena were found in PVDF/DPC and PVDF/DPK systems during the thermally induced phase-separation processes. The monotectic points of PVDF/DPC and PVDF/DPK systems appeared at PVDF concentration approximately 30 and 56 %(wt), respectively. This suggested that PVDF membrane with a bicontinuous or cellular structure could be obtained when the PVDF concentration was less than the point values. The effects of polymer concentration and quenching temperature on the membrane structure, porosity, and tensile strength were also investigated. The results showed that low polymer concentration and high quenching temperature led to a large pore size membrane. The tensile strength of the membrane increased with the increase of the polymer concentration, but the porosity of the membrane decreased. On condition that the PVDF concentration was higher than monotectic points, only polymer crystallization occurred and a typical compact spherulitic structures were obtained. Moreover, a binary diluent of DPK and secondary solvent such as 1,2-propylene glycol (PG) was used to replace the single diluent in TIPS process. The phase diagram for the PVDF/binary diluent of DPK and PG system was measured in the range of the PG/DPK mass ratio changing from 0 to 2/3. Then the effects of the PG/DPK mass ratio and the PVDF concentration on membrane cross-section structures and tensile strength were also investigated. The results showed that the addition of PG brought about a shift of the cloud point curve to a higher temperature and the extension of the liquid-liquid phase separation region to a higher polymer concentration. Therefore a bicontinuous cross-section structure was obtained when the PG/DPK mass ratio was 3/7 and the polymer concentration was 30 wt%. As an increase of the PG/DPK mass ratio, the tensile strength increased gradually at a fixed PVDF concentration. Moreover, for the same PG/DPK mass ratio, the cross-section microstructure changed from a bicontinuous or a cellular structure to a spherulitic structure, and the tensile strength increased drastically as the polymer concentration increased from 20 wt% to 50 wt%. According to the properties of diluents, the industrial scale production line with a twin-screw extruder of microporous PVDF hollow fiber membranes was established and a series of different type hollow fiber membranes were prepared for the corresponding applications of pressure-driven modulus, submersed modulus and membrane bio-reactor modulus. At the same time, the full recycle of diluents was almostly actualized by using a series of unit opertaions such as extraction, distillation, delamination, sedimentation and drying processes. It means there is no waste emission in the preparation of PVDF membranes or it is a green process.

Effects of Co-Diluent on the Pore Structure, Patterning Fidelity, and Properties of Membranes Fabricated by Lithographically Templated Thermally Induced Phase Separation

Preparation of Porous PVDF Membrane Via Thermally Induced Phase Separation with Diluent Mixture of DBP and DEHP

Patterning Flat-Sheet Poly(vinylidene Fluoride) Membrane Using Templated Thermally Induced Phase Separation

Preparation of High Density Polyethylene/polyethylene- Block -Poly(ethylene Glycol) Copolymer Blend Porous Membranes Via Thermally Induced Phase Separation Process and Their Properties

Influence of additives on phase separation process of PVDF solution and membrane morphology

Fabrication of Hydrophilic and Sponge-Like PVDF/brush-like Copolymer Blend Membranes Using Triethylphosphate As Solvent

Preparation of porous PVdF membrane via thermally induced phase separation using sulfolane

Effect of the Casting Solvent on the Crystal Characteristics and Pervaporative Separation Performances of P(Vdf-Co-Hfp) Membranes

The Effect of Diluent Mixture with Upper Critical Solution Temperature on Membrane Formation Process, Microstructure, and Performance of PVDF Hollow Fiber Membrane by TIPS Process

Preparation of PVDF Membranes via TIPS Method: The Effect of Mixed Diluents on Membrane Structure and Mechanical Property

Green preparation of polyvinylidene fluoride microfiltration membranes via thermally indueced phase separation method using diphenyl carbonate and diphenyl ketone as diluents

Computer simulation and experimental verification of morphology and gas permeability of poly(4-methyl-1-pentene) membranes: effects of polymer chain and diluent extractant

Wide Liquid-Liquid Phase Separation Region Enhancing Tensile Strength of Poly(vinylidene Fluoride) Membranes Via TIPS Method with a New Diluent

Controlling the inner surface pore and spherulite structures of PVDF hollow fiber membranes in thermally induced phase separation using triple-orifice spinneret for membrane distillation

Thermally Induced Phase Separation of Poly(vinylidene Fluoride)/diluent Systems: Optical Microscope and Infrared Spectroscopy Studies

Dissipative Particle Dynamics Study and Experimental Verification on the Pore Morphologies and Diffusivity of the Poly (4-Methyl-1-pentene)-diluent System Via Thermally Induced Phase Separation: the Effect of Diluent and Polymer Concentration

Effects of diluent content on the crystallization behavior and morphology of polyethylene membrane fabricated via thermally induced phase separation process

Membrane formation of poly(vinylidene fluoride)/poly(methyl methacrylate)/diluents via thermally induced phase separation

Fabrication of PVDF ultrafiltration membrane using modified thermally induced phase separation: The role of amphiphilic and hydrophilic non-solvents

Influence of Dope Viscosity on the Fabrication of Pvdf Hollow Fiber Membranes with Single Skin Layer

Structure and Performance of Polyacrylonitrile Membranes Prepared Via Thermally Induced Phase Separation