Abstract:An anion exchange process using HBr is developed and used to achieve pure‐red emitting CsPbI3‐xBrx quantum dots, with 1‐dodecanethiol ligands used to suppress halide ion migration. The light‐emitting diodes based on the quantum dos show a stable electroluminescence peak at 637 nm, and a maximum external quantum efficiency of 21.8% with an average value of 20.4%. Perovskite‐based light‐emitting diodes (PeLEDs) with a mixed halide composition can be used to obtain the "pure red" emission, i.e., in the 620–650 nm range, required for high‐definition displays. However, fast halide ion migration induces phase separation in these materials under electric fields, resulting in poor spectral stability and low efficiency. Herein, a method for producing mixed halide CsPbI3‐xBrx quantum dots (QDs) is reported in which ion migration is suppressed. The mixed halide composition is first achieved by anion exchange between CsPbI3 QDs and hydrobromic acid (HBr), during that the bromine ions efficiently passivate the iodine vacancies of the QDs. The original oleic acid ligands are then exchanged for 1‐dodecanethiol (1‐DT), which suppresses halide ion migration via the strong binding of the sulfhydryl group with the QD surface. PeLEDs based on these QDs exhibit a pure‐red electroluminescence (EL) peak at 637 nm, a maximum external quantum efficiency (EQE) of 21.8% with an average value of 20.4%, a peak luminance of 2653 cd m−2, and low EQE decease with increasing luminance. The EL spectrum of these devices is stable even at 6.7 V and they have an EQE half‐life of 70 min at an initial luminance of 150 cd m−2.

Improved Efficiency of Red Perovskite Quantum Dots-Based Light-Emitting Diodes by Thickness Tuning of PEDOT:PSS

Improved performance of CsPbBr3 quantum-dot light-emitting diodes by bottom interface modification

Regulation of the Conductivity and Work Function of PEDOT:PSS Using MoO2 Nanocrystals to Achieve Efficient CsPbBrxI3-x Red Light Quantum Dot Light-Emitting Diodes

Nucleophilic Reaction‐Enabled Chloride Modification on CsPbI3 Quantum Dots for Pure Red Light‐Emitting Diodes with Efficiency Exceeding 26 %

Spectrally Stable and Efficient Pure Red CsPbI 3 Quantum Dot Light-Emitting Diodes Enabled by Sequential Ligand Post-Treatment Strategy

Regulation of the conductivity and work function of PEDOT:PSS using MoO2 nanocrystals to achieve efficient CsPbBr I3- red light quantum dot light-emitting diodes

Optimization of the carrier recombination and transmission properties in perovskite LEDs by doping poly (4-vinylpyridine) and graphene quantum dots made of chitin

Electron Delocalization in CsPbI 3 Quantum Dots Enables Efficient Light‐Emitting Diodes with Improved Efficiency Roll‐Off

Performance Enhancement of Perovskite Quantum Dot Light-Emitting Diodes via Management of Hole Injection

Synchronously Polishing the Lead-Rich Surface and Passivating Surface Defects of CsPb(Br/I)3 Quantum Dots for High-Performance Pure-Red PeLEDs

Improved Efficiency for Silicon‐Based Perovskite Light‐Emitting Diodes Via Interfacial Hydrophilic Modification

Improved Performance of Pure Red Perovskite Light-Emitting Devices Based on CsPb(Br1-xIx)3 with Variable Content of Iodine and Bromine.

Deep‐Red Perovskite Light‐Emitting Diodes with External Quantum Efficiency Exceeding 21% Enabled by Ligand‐Modulated Dimensionality Control

Passivating CsPbBrxI3_x Quantum Dots Via Modifiers Film to Achieve Efficient Red Light-Emitting Diodes

Spectrally Stable and Efficient Pure Red CsPbI3 Quantum Dot Light-Emitting Diodes Enabled by Sequential Ligand Post-Treatment Strategy

Passivating CsPbBr I3− quantum dots via modifiers film to achieve efficient red light-emitting diodes

Quasi‐2D CsPbBr X I 3− X Composite Thin Films for Efficient and Stable Red Perovskite Light‐Emitting Diodes

Suppressing Ion Migration of Mixed‐Halide Perovskite Quantum Dots for High Efficiency Pure‐Red Light‐Emitting Diodes

A Synergetic Codoping Strategy Enabling Performance Improvement of Pure‐Blue Perovskite Quantum Dots Light‐Emitting Diodes

Cs4PbI6 assisted zinc doping in pure red perovskite with improved electroluminescent performance

Strongly-Confined CsPbBr3 Perovskite Quantum Dots with Ultralow Trap Density and Narrow Size Distribution for Efficient Pure-Blue Light-Emitting Diodes