Effect of Na/Ce Codoping on the Crystal Structure and Electrical Properties of BaBi8Ti7O27 Ferroelectric Ceramics

Wenying Fan,Xiangping Jiang,Xiaokun Huang,Xin Nie,Chao Chen,Jiajun Yuan
DOI: https://doi.org/10.1016/j.ceramint.2022.01.164
IF: 5.532
2022-01-01
Ceramics International
Abstract:Ba(1-x)(Na0.5Ce0.5)(x)Bi8Ti7O27 (BBIT:x(NC)) intergrowth bismuth layer-structured piezoelectric ceramics with enhanced piezoelectric and ferroelectric properties were synthesized by the traditional solid-state reaction process. Our systematic investigations show that the BBIT:x(NC) ceramics have a single intergrowth structure with an orthogonal phase. The reason of the internal bias field in BBIT:x(NC) ceramics was analyzed by atmosphere sintering, which was related to the defects of Na/Ce doped BBIT ceramics. Moreover, the electrical properties of Na/Ce co-doped BBIT ceramics were significantly improved. The sample with doping content x = 0.3 exhibits the most excellent piezoelectric constant d 33 of 21.8 pC/N and a high Curie temperature T-c of 541 degrees C, which may be attributed to the enhancement of ferroelectric polarization and lattice mismatch, respectively. In addition, the remnant polarization (2P(r)) was improved from 16.8 mu C/cm(2) to 20.2 mu C/cm(2), and the d(33) was 20.6 pC/N after annealing at 450 degrees C, indicating that the ceramic samples had good thermal stability. Our results suggest that BBIT: 0.3(NC) ceramics may be a promising candidate for high-temperature piezoelectric applications.
What problem does this paper attempt to address?