Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

The Oxidation Behavior of Multi-layered SiC Coated Graphite in Water Vapor Containing Environment

Oxidation Behavior of Dense SiC Coating in Water Vapor and Its Mixed Atmosphere with Air

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

A Multi-Layered SiC Coating to Protect Graphite Spheres from High Temperature Oxidation in Static Air

SiC/MoSi2-SiC-Si Oxidation Protective Coatings for HTR Graphite Spheres with Residual Si Optimized

Oxidation Behavior of SiCf/SiC Composites Modified by Layered-Y2Si2O7 in Wet Oxygen Environment

SiC Performance of Coated Fuel Particles under High-Temperature Atmosphere of Air

High Temperature Oxidation Behavior of SiC Coating Materials

Oxidation of SiC fibers in water vapor

The Stability of SiC Coating and SiO2/SiC Multilayer on the Surface of Graphite for HTGRs at Normal Service Condition

Corrosion of SiC layers on coated zirconia particles in wet atmosphere

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

Preparation and antioxidant mechanism of TiSi<sub>2</sub>-Si-SiC/SiC bilayer coating on matrix graphite

Oxidation mechanism of SiC coated layer in air atmosphere at 1400°C

Research on Microstructure and Oxidation Resistant Property of ZrSi2-SiC/SiC Coating on HTR Graphite Spheres

Thermal Stability Analysis of SiC/SiO2 Oxidation Resistant Coatings

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

Antioxidant performance and oxidation mechanism of a liquid silicon infiltration (LSI) SiC–Si coating at an ultra-high temperature of 1873 K

ZrSi2-SiC/SiC Anti-Oxidant Coatings Prepared on Graphite Spheres by Two-Step Pack Cementation Process

Non-Destruction Evaluation Method for Long-Term Oxidation Behavior of SiC/SiC Composites with Different Preforms in Wet Oxygen

Oxidation Behaviors of C–ZrB2–SiC Composite at 2100 °C in Air and O2