Modification of Nano-Eutectic Structure and the Relation on Hydrogen Storage Properties: A Novel Ti-V-Zr Medium Entropy Alloy

Shuting Zhang,Xin Ding,Ruirun Chen,Jiaxin Zhang,Yanqing Su,Shiping Wu,Jingjie Guo

DOI: https://doi.org/10.1016/j.ijhydene.2022.08.039

2022-01-01

SSRN Electronic Journal

Abstract:TiV-based alloys present desirable hydrogen storage properties owing to the formation of Body-centered cubic (BCC) solid solutions. However, the nanostructure that helps hydrogen absorption and desorption is hard to be designed and prepared in these alloys. In this study, Ti40Zr60-xVx (x = 20, 25, 30) alloys with hyperfine nano-eutectic structures of 50 -500 nm in lamellar space are prepared, and the nano-eutectic structures can be refined by increasing Zr content. Ti40Zr60-xVx alloy powder exhibits excellent activation and hydrogenation properties. The phase separation and nano-eutectic structure are formed due to the differences of atomic size in Ti40Zr60-xVx alloys. The highest total hydrogenation capacity of 2.4 wt% is obtained within 10 min at 200 degrees C under 1 MPa H2 by Ti40V35Zr25 alloy, surpassing that of Ti40Zr40V20 and Ti40Zr30V30 alloys of 2.2 wt% in 20min. Based on the Johnson-Mehl-Avrami-Kolmogorov (JMAK) model, lower energy is required for the hydrogenation of Ti40V35Zr25 alloy. Due to the formation of some stable hydrides, the Ti40Zr60-xVx alloys show lower reversible hydrogenation capacities. The spinodal decomposition in Ti40V35Zr25 alloy facilitates the formation of reticular eutectics, which provide high-density phase interfaces and produce "synergistic effect". As a result, the hydrogenation kinetic and capacity are enhanced significantly.(c) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.