Effect of Ag Alloying on the Microstructure and Mechanical Properties of Laser Welded-Brazed Ti/Al Dissimilar Joints

Zhijie Zhang,Jian Huang,Chenwu Yao,Xing Zhang

DOI: https://doi.org/10.1016/j.msea.2022.143359

2022-01-01

SSRN Electronic Journal

Abstract:A novel method to fabricate Ag alloyed aluminum weld and Ti/Al interface zone by adding silver mesh interlayer in TA2/AA5150 dissimilar joints was proposed. Microstructures and mechanical properties of the Ti/Al joints with and without silver mesh were investigated. Aluminum grains in the weld without Ag was composed of the primary aluminum and the surrounding aluminum. It was resulted from the redistribution of Mg element during aluminum solidification. As laser power decreased, the undercooling and temperature gradient at the front of solidification interface increased and the nucleation rate of aluminum also increased. It caused that the aluminum grains transformed from the equiaxed dendrites to the columnar dendrites. Mg element in the aluminum weld with Ag was enriched by the MgAg phase and the MgAgAl phase. It made the primary aluminum disappear and the active Mg element decrease. Aluminum grains with Ag element was finer than grains without Ag. The growth of aluminum dendrites was inhibited by the MgAg phase. The texture in the aluminum weld with Ag was weakened and the dendrites were not fully developed compared with the weld without Ag. Mismatch of mechanical properties between Al3Ti and Al was decreased by Ag alloying. The optimal average shear strength of the joints increased from 147.7 MPa to 171.4 MPa assisted with the silver mesh.