Abstract:In this paper, the effect of Si content on the microstructure and mechanical properties of the Al–1.2Mg– x Si–1.2Cu–0.6Mn cast alloy was investigated. The study aimed to explore the optimal addition of Si element to improve the comprehensive properties of alloys. The microstructure, phase composition and fracture morphology of the alloy were determined through OM, SEM, EBSD and XRD analysis. The Si content in the alloy ranged from 0.48 to 2.4 wt.%. With the increase of Si content, the number of strengthening phases increases, which improves the comprehensive properties of the alloy. When the Si content is 0.8 wt.%, the eutectic Mg 2 Si transforms from rod-shaped to larger block shaped, and the formation of coarse Mg 2 Si phase limits the elongation of the alloy. When the Si content is 2.4 wt.%, fine Al 2 Cu phases are present in this alloy and coexist with Al(Fe,Mn)Si phases, while an increase in the Si content appears as partially accompanied by an incipient crystalline Si phase around the Al(Fe,Mn)Si phase. The alloy exhibits a maximum tensile strength, yield strength and elongation of 198.2 MPa, 101.2 MPa and 4.96%, respectively, with a hardness of 80.94 Hv. It consists of five alloy phases, mainly α-Al, Mg 2 Si, Al(Fe, Mn)Si eutectic phase, Q-AlCuMgSi eutectic phase and the beginning crystalline silicon phase formed due to the increased Si content. The Si content can improve alloy strength, but there is some damage to the toughness of the alloy. Higher silicon alloy content results in the formation of fine Al 2 Cu eutectic. This result makes it possible to achieve a higher level of strength with a reduced loss of ductility in the alloy.

The Effect of Mg/Si Ratio on the Microstructure and Tensile Properties of Twin-Roll-Casting Al-Mg-Si Alloys

Effect of Mg on Nucleation Process of Recrystallization in Al–Mg–Si/SiCp Composite

Effect of Mg and Si contents and TiC nanoparticles on the center segregation susceptibility of twin-roll cast Al-Mg-Si alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

The effect of the TiC-TiB 2 nanoparticles on the microstructure and mechanical properties of Al-Mn-Si strips fabricated by twin-roll casting

Effects of Zn Addition and Twin Roll Casting Process on the Microstructure, Texture, and Mechanical Properties of the Mg-Al-Mn-Ca Sheet

Improving element uniformity and mechanical properties of Al–Mg–Si alloy fabricated by twin roll casting with superheat melt treatment

Influence of Mg/Si Ratio on the Microstructure and Formability of 6061 Cast-rolled Sheets

Enhancing mechanical properties of twin-roll cast Al–Mg–Si–Fe alloys by regulating Fe-bearing phases and macro-segregation

Effect of Mg addition on microstructure and mechanical properties of Al-Si-Cu-Fe alloy with squeeze casting

Effect of Zn/Mg Ratio on Microstructure and Properties of Cold Extruded Al-xZn-2.4Mg-0.84Cu-0.2Zr-0.25Ti Aluminum Alloy

Effect of Σ3 grain boundaries on microstructure and properties of oriented Fe-6.5 wt%Si in twin-roll strip casting

Influences of different Zr/Sc ratios on microstructure and mechanical properties of Al-2Si alloy

Relationship between Microstructure Evolution and Tensile Properties of AlSi10Mg Alloys with Varying Mg Content and Solidification Cooling Rates

Effect of Mo on Segregation Behavior of Al-Mg-Si-Mn Alloy Produced by Twin-Roll Casting

The Effect of Si Content on the Microstructure and Mechanical Properties of Al–1.2Mg–xSi–1.2Cu–0.6Mn Cast Alloy

Effect of Al/Mn ratio on corrosion behavior of lean Mg-Zn-Ca-Al-Mn alloy processed by twin-roll casting

Effects of Al Concentration on Microstructure and Mechanical Properties of Mg-xAl-1Zn-1Si Alloy

Fe-bearing phase formation, microstructure evolution, and mechanical properties of Al-Mg-Si-Fe alloy fabricated by the twin-roll casting process

Synergistic effect of Gd and Sr on the microstructure and mechanical properties of Al–Si–Mg alloy

Effect of thickness ratio on microstructure evolution and coordinated behavior of Mg/Al composite plates in one-pass asymmetric rolling with differential temperature rolls