Single Atomic Cerium Sites with a High Coordination Number for Efficient Oxygen Reduction in Proton-Exchange Membrane Fuel Cells
Mengzhao Zhu,Chao Zhao,Xiaokang Liu,Xiaolin Wang,Fangyao Zhou,Jing Wang,Yanmin Hu,Yafei Zhao,Tao Yao,Li-Ming Yang,Yuen Wu
DOI: https://doi.org/10.1021/acscatal.0c05503
IF: 12.9
2021-03-15
ACS Catalysis
Abstract:Fe–N–C electrocatalysts, as a representative of platinum group metal-free (PGM-free) catalysts, exhibit a comparable oxygen reduction reaction (ORR) activity but insufficient stability to that of commercial Pt/C in proton-exchange membrane fuel cells (PEMFCs), due to the unavoidable Fenton's reactions. Herein, we report a hard-template approach to synthesize the rare-earth single-cerium-atom-doped metal–organic frameworks with a hierarchically macro–meso–microporous structure. Spherical aberration correction electron microscopy confirms the atomic dispersion of Ce sites. Additionally, X-ray absorption spectroscopy (XAS) was employed to further verify the coordination environment of Ce sites, which were stabilized by four-coordinated nitrogen atoms and six-oxygen atoms (Ce–N<sub>4</sub>/O<sub>6</sub>). The Ce sites were embedded in a hierarchically macro–meso–microporous N-doped carbon (Ce SAS/HPNC) catalyst, which exhibits a half-wave potential of 0.862 V in ORR and the highest power density of 0.525 W cm<sup>–2</sup> under 2.0 bar H<sub>2</sub>/O<sub>2</sub> in the fuel cell test.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c05503?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c05503</a>.Discussions of material synthesis and characterization, electrochemical measurements, and computational methods, figures of TEM and SEM images, diameter distribution histograms, EDS elemental mapping images, HAADF-STEM images, XRD patterns, Raman spectra, XPS spectra, C K-edge XANES and N K-edge XAS spectra, EXAFS fitting curves, FT-EXAFS spectra, ORR performance, corresponding Tafel plots from RDE polarization curves, and life test of fuel cells, and tables of structural parameters and performance comparison (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c05503/suppl_file/cs0c05503_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, physical