Effect of Ti-Hf-Zr-Cu-Ni high entropy alloy addition on laser beam welded joint of Ti2AlNb based intermetallic alloy

Mirza Zahid Hussain,Jiangtao Xiong,Jinglong Li,Farah Siddique,Lin Jie Zhang,Yajie Du,Xian Rong Zhou

DOI: https://doi.org/10.1016/j.jmst.2021.12.036

2022-01-01

Abstract:•In this study, LBW of Ti-22Al-27Nb was experimented through addition of an interlayer of the filler, Ti-Hf-Zr-Cu-Ni HEA, into the joint and a comparison between the LBWJs of Ti-22Al-27Nb either prepared with or without addition of the filler was established through microstructural analysis by corelating its impact on mechanical properties at room temperature. Followings are the highlights of this experimental work.•The addition of Ti-Hf-Zr-Cu-Ni HEA into FZ of LBWJ of Ti-22Al-27Nb activated heterogenous nucleation due to difference of chemical composition between the BM and the filler, resultantly, fine grained B2 phase with greater fraction of HAGBs was evolved in the FZ. Grain refinement and higher misorientation angle between GBs in the FZ contributed an increase in hardness, tensile strength and percentage elongation of HEA adulterated LBWJ of Ti-22Al-27Nb.•The average hardness of the FZ (343.5 HV) and UTS (1062 MPa) of the HEA added LBWJ was found in close agreement with that of BM, 345 HV and 1060 MPa, respectively.•The percentage elongation of the joint, prepared with an interlayer of HEA, was measured up to 11.2%, which was 83.6% of the BM.•The LBWJ of Ti-22Al-27Nb, prepared with the addition of HEA, fractured from the junction of FZ and HAZ in a ductile mode while the LBWJ prepared without addition of Ti-Hf-Zr-Cu-Ni filler was ruptured from FZ in quasi-cleavage mode.