Abstract:A series of P-promoted non-noble metal Cu-based catalysts without alkalis and Fischer-Tropsch elements were prepared by a complete liquid-phase method and tested for the synthesis of higher alcohols (C2+OH) from syngas in slurry bed reactor. The catalysts were characterized by XRD, 27Al-MAS-NMR, N2 adsorption, XPS, H2-TPR and NH3-TPD techniques. Results showed that the incorporation of an appropriate amount of phosphorus into the non-noble metal Cu-based catalyst could increase the surface Cu content, the amount of weak acid and improved the Cu+ reducibility, which promoted the synergistic effect between Cu and Al, and thus enhanced both stability and selectivity towards to higher alcohols formation. Activity results showed that the production of alcohols and hydrocarbons over this kind of catalyst followed A-S-F distributions, similar with conventional CuFe and CuCo based catalysts. The catalysts with Cu:Zn:Al:P=2:1:0.8:0.05 showed the best catalytic performance with long-term stability toward CO conversion and C2+OH selectivity (reaching 55%) during the lifetime test for 120h. It was speculated that AlOOH favored CO dissociation, and the synergism of Cu0, Cu+ and AlOOH was beneficial to the formation of higher alcohols. This work provided a new sight that alkalis and F-T elements were not indispensable for direct synthesis of higher alcohols from syngas over non-noble metal Cu-based catalysts.

Highly Selective Production of Long-chain Aldehydes, Ketones or Alcohols Via Syngas at a Mild Condition

Highly Efficient Selective Hydrogenation of Cinnamaldehyde to Cinnamyl Alcohol over CoRe/TiO2 Catalyst.

Tuning the selectivity of CO2 hydrogenation to alcohols by crystal structure engineering

Selective synthesis of mixed alcohols from syngas over catalyst Fe2O3/Al2O3 in slurry reactor

Theoretical investigation of the selectivity of alcohols and aldehydes on Co-based catalysts in syngas conversion

Highly Tunable Selectivity for Syngas‐Derived Alkenes over Zinc and Sodium‐Modulated Fe5C2 Catalyst

Direct Synthesis of Allyl Alcohol from Glycerol over CoFe Alloy

Edge-rich molybdenum disulfide tailors carbon-chain growth for selective hydrogenation of carbon monoxide to higher alcohols

Selective Hydrogenation of CO2 to Ethanol over Cobalt Catalysts

Highly Selective Conversion of Syngas to Higher Oxygenates over Tandem Catalysts

Synthesis of tetrahedrally coordinated CoO for higher alcohol synthesis directly from syngas

Accelerating C2+ Alcohols Synthesis from Syngas by Simultaneous Optimizations of CO Dissociation and Chain Growth over CuCo Alloy Catalyst

Long-chain Α-Olefins Production over Co-MnOx Catalyst with Optimized Interface

Direct Carbon Dioxide Hydrogenation to Long-Chain Α-Olefins over FeMnK Catalysts

Selectivity of Electrochemical CO2 Reduction Toward Ethanol and Ethylene: the Key Role of Surface-Active Hydrogen

Higher alcohols synthesis from syngas over P-promoted non-noble metal Cu-based catalyst

Highly Selective Production of C5-C12 Hydrocarbons over Efficient Ru/heteropoly-acid Catalysts

High Alcohols Synthesis via Fischer–Tropsch Reaction at Cobalt Metal/Carbide Interface

Targeted Design And Synthesis Of A Highly Selective Mo-Based Catalyst For The Synthesis Of Higher Alcohols

Ordered mesoporous NiMg bimetal oxides confined KMoS catalyst for selective CO hydrogenation into higher alcohols

Selective CO 2 hydrogenation to liquid fuels over Na-decorated FeMgMnOx catalyst with high carbon efficiency