Abstract:A high Fe content easily produces Fe-rich phases with a harmful morphology, resulting in a huge detrimental effect on the properties and recycling ability of Al-Si alloys. Therefore, finding ways to effectively transform Fe-rich phases to form a beneficial phase or shape is of great significance. Accordingly, Al-Si-based alloys with Fe contents ranging from 0.1 wt.% to 2.0 wt.% were modified by different Mn additions. Moreover, experiments combined with simulations were utilized to comprehensively analyze the mechanism of Mn on the morphology and microstructural evolution of Fe-rich phases from different perspectives. The current findings determine that adding different Fe contents changes the phase-transition reactions in alloys. Without Mn, and by increasing the Fe content from 0.1 wt.% to 2.0 wt.%, the Fe-rich phases gradually convert from a skeleton-shaped α-Al8Fe2Si (<0.25 wt.%) to β-Al9Fe2Si2 with a fibrous (0.5 wt.%), needle-like (1.0 wt.%) and plate-like shape without curvatures (2.0 wt.%). The maximum length and mean aspect ratio increase from 12.01 μm to 655.66 μm and from 1.96 to 84.05, while the mean curvature decreases from 8.66 × 10−2 μm−1 to 8.25 × 10−4 μm−1. The addition of 0.35 wt.% Mn promotes a new Chinese-character and petal-shaped α-Al15(FeMn)3Si2, with an atomic ratio of Fe and Mn of 1:1 when the Fe content is lower than 0.5 wt.%, while it transforms to β-Al15(FeMn)3Si2 with an atomic ratio of 5:1, presenting as a refined plate-like shape with a certain curvature, as the Fe content increases to 2.0 wt.%. Mn alters the phase reactions and increases the threshold of the Fe content required for β-Al15(FeMn)3Si2, limiting the formation and growth of them simultaneously in time and space. The enrichment of Mn atoms and solute diffusion at the growth front of β-Al15(FeMn)3Si2, as well as the strong atomic-binding ability, can deflect the growth direction of β-Al15(FeMn)3Si2 for it to have a certain curvature. Additionally, the enriched Mn atoms easily form α-Al15(FeMn)3Si2 and cause the long β-Al15(FeMn)3Si2 to be broken and refined to further reduce the damages caused to the alloy's performance. Ultimately, the maximum length and mean aspect ratio can be effectively reduced to 46.2% and 42.0%, respectively, while the mean curvature can be noticeably increased by 3.27 times with the addition of Mn.

High-ductility AA6061 Alloys Produced by Combination of Sub-Rapid Solidification and Cr-alloying

Fe-bearing phase formation, microstructure evolution, and mechanical properties of Al-Mg-Si-Fe alloy fabricated by the twin-roll casting process

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

Modification and refinement of Fe-containing phases, mechanical properties and strengthening mechanisms in Al–Fe alloys via Cr alloying and continuous rheo-extrusion

Triple the ductility of as-cast Al–Si alloys by phase-selective recrystallization

Revealing the influence of Fe on Fe-rich phases formation and mechanical properties of cast Al-Mg-Mn-Fe alloys

Achievement of High Strength and Ductility in Al–Si–Cu–Mg Alloys by Intermediate Phase Optimization in As-Cast and Heat Treatment Conditions

Enhanced comprehensive performance via alloying and rheo-diecasting in a semi-solid Al–Si–Fe–Mg–Cu–Sr alloy

Enhancing mechanical properties of twin-roll cast Al–Mg–Si–Fe alloys by regulating Fe-bearing phases and macro-segregation

Evolution behavior of Fe and Fe-rich phases in high-Fe concentration Al-Si-Mg alloy with Mn, Cr, and Co alloyed

Enhanced strength-ductility synergy in a rheo-diecasting semi-solid aluminum alloy

Effects of metalloid Si on the microstructure and mechanical properties of Fe36Ni36Cr10Mo1Al17-XSiX alloys

Simultaneously enhance the tensile strength and ductility of dual-phase Fe37Ni36Cr10Al17 alloy via phase-selective recrystallization and aging

Microstructure and mechanical properties of Al-Mg-Si alloy fabricated by a short process based on sub-rapid solidification

Improving the ductility of high-strength multiphase NiAl alloys by introducing multiscale high-entropy phases and martensitic transformation

Designing Ultrastrong and Thermally Stable FeCrAl Alloys with the Fine-Grained Structure

Study on Microstructure and Mechanical Properties of Al-Mg-Si-Cu Aluminium Alloy with High Ductility

The roles of solidification cooling rate and (Mn,Cr) alloying elements in the modification of β-AlFeSi and hardness evolvements in near-eutectic Al-Si alloys

Enhancing High Temperature Mechanical Properties Via Modulating B2 Phase with Al Contents in FeCrNiAlx(x=0.63,0.71,0.77) High Entropy Alloys

Enhanced tensile strength and ductility of an Al-6Si-3Cu alloy processed by room temperature rolling

Optimizing the Morphology and Solidification Behavior of Fe-Rich Phases in Eutectic Al-Si-Based Alloys with Different Fe Contents by Adding Mn Elements