Additive and High-Temperature Processing Boost the Photovoltaic Performance of Nonfullerene Organic Solar Cells Fabricated with Blade Coating and Nonhalogenated Solvents
Youzhan Li,He Liu,Jiang Wu,Hao Tang,Hailong Wang,Qingqing Yang,Yingying Fu,Zhiyuan Xie
DOI: https://doi.org/10.1021/acsami.0c23035
2021-02-19
Abstract:Benefitting from narrow band gap nonfullerene acceptors, continually increasing power conversion efficiency (PCE) endows organic solar cells (OSCs) with great potential for commercial application. Fabricating high-performance OSCs with potential for large-scale coating and nonhalogenated solvent processing is a necessity. Herein, we have proposed the use of nonhalogenated solvents combined with high-temperature blade coating to prepare a PM6 (poly[(2,6-(4,8-bis(5-(2-ethylhexyl-3-fluoro)thiophen-2-yl)benzo[1,2-b:4,5-b′]dithiophene))-alt-(5,5-(1′,3′-di-2-thienyl-5′,7′-bis(2-ethylhexyl)benzo[1′,2′-c:4′,5′-c′]dithiophene-4,8-dione)]):Y6 (2,2′-((2Z,2′Z)-((12,13-bis(2-ethylhexyl)-3,9-diundecyl-12,13-dihydro-[1,2,5]thiadiazolo[3,4-e]thieno[2″,3′′:4′,5′]thieno[2′,3′:4,5]pyrrolo[3,2-g]thieno[2′,3′:4,5]thieno[3,2-b]indole-2,10-diyl)bis(methanylylidene))bis(5,6-difluoro-3-oxo-2,3-dihydro-1H-indene-2,1-diylidene)))blend active layer. The resultant OSCs deliver a PCE of 15.51% when the PM6:Y6 active layer is blade-coated at 90 °C in nonhalogenated <i>o</i>-xylene (<i>o</i>-XY) host solvent containing 1,2-dimethylnaphthalene (DMN) additive. It is found that high-temperature blade coating and nonhalogenated solvent additive DMN can suppress excessive aggregation of Y6 and enhance the crystallinity of PM6 and Y6 by regulating the dynamic process of active layer formation. Finally, an optimized blend morphology with nanofibrous phase separation and enhanced crystallinity are achieved for the PM6:Y6 active layer prepared with high-temperature blade coating and nonhalogenated <i>o</i>-XY:DMN solvents, which not only shortens the film-drying time but also leads to increased charge generation, transport, and collection efficiency. The 1.00 cm<sup>2</sup> OSCs prepared with high-temperature blade coating and nonhalogenated solvents exhibit a high PCE of 13.87%. This approach shows great potential for large-area fabrication of OSCs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c23035?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c23035</a>.Normalized absorption spectra, TEM images, and AFM height and phase images of the films prepared under different processing conditions; illuminated <i>J</i>–<i>V</i> characteristics, dependence of <i>V</i><sub>OC</sub> and <i>J</i><sub>SC</sub>, <i>E</i><sub>g</sub>, <i>V</i><sub>OC</sub>, and <i>E</i><sub>loss</sub> of the OSCs prepared at different processing conditions; <i>J</i><sup>1/2</sup>–<i>V</i> characteristics of hole-only and electron-only devices prepared under different processing conditions; summarized solubility parameters (δ) of materials and solvents, interaction parameters (χ), and the calculation formula and boiling points of solvents; detailed photovoltaic parameters for the large-area (1.00 cm<sup>2</sup>) OSCs prepared under different processing conditions (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c23035/suppl_file/am0c23035_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology