Abstract:The quest for lightweight and functional materials poses stringent requirements on mechanical performance of porous materials. However, the contradiction between high strength and elevated porosity of porous materials severely limits their application scenarios in emerging fields. Herein, high-strength multifunctional mullite-based porous ceramic monoliths were fabricated utilizing waste fly ash hollow microspheres (FAHMs) by the protein gelling technique. Owing to their unique shell-pore structure inspired by shell-protected biomaterials, the monoliths with porosity of 54.69%–70.02% exhibited a high compressive strength (32.3–42.9 MPa) which was 2–5 times that of mullite-based porous ceramics with similar density reported elsewhere. Moreover, their pore structure and properties could be tuned by regulation of the particle size and content of the FAHMs, and the resultant monoliths demonstrated superior integrated performances for multifunctional applications, such as broadband sound insulation, efficient thermal insulation, and high-temperature fire resistance (>1300 °C). On this basis, mullite-based porous ceramic lattices (porosity 68.28%–84.79%) with a hierarchical porous structure were successfully assembled by direct ink writing (DIW), which exhibited significantly higher compressive strength (3.02–10.77 MPa) than most other ceramic lattices with comparable densities. This unique shell-pore structure can be extended to other porous materials, and our strategy paves a new way for cost-effective, scalable and green production of multifunctional materials with well-defined microstructure.

Mullite Ceramic Foams with Tunable Pores from Dual-Phase Sol Nanoparticle-Stabilized Foams

Foam-gelcasting preparation and properties of high-strength mullite porous ceramics

Preparation and Characterization of Mullite Foam Ceramics with Porous Struts from White Clay and Industrial Alumina

Novel Mullite Ceramic Foams with High Porosity and Strength Using Only Fly Ash Hollow Spheres As Raw Material

Ultralight and Mechanically Robust SiC Foams with Interconnected Cellular Architecture

A Novel Method Based on Ultrastable Foam and Improved Gelcasting for Fabricating Porous Mullite Ceramics with Thermal Insulation–mechanical Property Trade-off

High-strength, multifunctional and 3D printable mullite-based porous ceramics with a controllable shell-pore structure

Ceramic foams with highly open channel structure from direct foaming method in combination with hollow spheres as pore-former.

Silica Foams With Ultra-Large Specific Surface Area Structured By Hollow Mesoporous Silica Spheres

Fabrication of Mullite-Corundum Foamed Ceramics for Thermal Insulation and Effect of Micro-Pore-foaming Agent on Their Properties

Aerogel‐like Ceramic Foams with Super‐high Porosity and Nanoscale Cell Wall from Sol Nanoparticles Stabilized Foams

Highly Porous and Mechanically Robust Al2O3-based Foams with Self-Wrinkled and Rough Aperture Surfaces Via Binary Colloidal Self-Assembly of Nanoparticle/gelation Network

Fabrication and Properties of Porous Mullite Ceramics from Directly Sintering Ceramic Microspheres

Highly Porous Alumina Cellular Ceramics Bonded by In-Situ Formed Mullite Prepared by Gelation-Assisted Al2O3–Si Particle-Stabilized Foams

A new mullite foamed ceramic prepared by direct-foaming methods in parallel with a mechanical activation technique

Fabrication of Porous Mullite Ceramics with High Porosity Using Foam-Gelcasting

Highly Porous and Hierarchical MgAl2O4 Ceramics with Improved Pore Connectivity Prepared from Gelled Particle-Stabilized Foams

Porous Mullite Ceramics with Low Thermal Conductivity Prepared by Foaming and Starch Consolidation

Microstructure and properties of highly porous mullite materials fabricated by direct foaming-gelcasting

Highly Porous Zirconia Ceramic Foams with Low Thermal Conductivity from Particle‐Stabilized Foams

Directly Growing Nanowire-Assembled Nanofibrous Ceramic Foams with Multi-Lamellar Structure Via Freeze-Casting Process