Abstract:Ti-Cr-V-based alloys have been utilized across various domains, including aerospace structural and functional materials and hydrogen storage materials. Investigating the phase relations in the Ti-Cr-V system is significant in supporting the material design for these applications. In the present work, the isothermal sections at 1000, 1100, and 1200 °C for the Ti-Cr-V system were precisely determined through a systematic investigation using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD). The phase region of Cr2Ti was entirely elucidated for the first time. As the temperature decreased from 1200 to 1000 °C, the V solubility range of Cr2Ti increased from 5.3 wt.% to 10.0 wt.%, while the Ti solubility range essentially remained constant at approximately 31.0–33.9 wt.%. In addition, it was suggested that the stable structure of Cr2Ti was C36 at 1200 °C and C15 at 1000 and 1100 °C. The present work will support thermodynamic re-assessment research.

Phase Equilibria of the Al-V-Cr Ternary System at 1000 and 1200 °C

Phase Equilibria Of The Al-Cr-Ta Ternary System At 1000 And 1200 Degrees C

Experimental Investigations of Phase Equilibria in the Ta-V-Cr Ternary System

Phase Equilibria of the Nb-V-Al Ternary System at 1100 and 1200 °C

Experimental Investigation of Phase Equilibria in the Ti-Cr-V System at 1000–1200 °C

Experimental Determination of Phase Equilibria in the Co-Cr-V Ternary System

Experimental Investigation and Thermodynamic Description of Phase Equilibria in the Al-Cr-Mo Ternary System

Phase relationship of the Ag–Zr–Cr system at 1000 and 750°C

Study On The Phase Equilibria Of The Al-Cr-Ti System At 1050 Degrees C

Phase Equilibria of the Al-Sc-Zr Ternary System at 500 °C

Phase Relationship Of The Ag-Z-Cr System At 1000 And 750 Degrees C

Study on the phase equilibria of the Al-Cr-Ti system at 1050 °C

Phase equilibria of the Ni-Cr-Y ternary system at 900 C

Phase Equilibria of the Ni-Al-Cr-Y Quaternary System and the Ni-Al-Y Ternary System at 900 °C

Experimental Investigation of Phase Equilibria in the Co-Cr-Nb System at 1000, 1100, and 1200 °C

Experimental Investigation of Phase Equilibria in the Co–W–Nb Ternary System

Phase equilibria in Co−Al−Re ternary system at 1100 and 1300 °C

Phase Equilibria in the Co-W-Zr Ternary System at 1200 and 1300 °C

Experimental Investigation of Phase Equilibria in the Ti-Fe-Cr Ternary System

Phase Equilibria of the Er-Al-Zr Ternary System at 500 °C

Phase Equilibria in the Fe-Al-Sn Ternary System