Abstract:Single hat sectioned hybrid beams composed of aluminum and Carbon Fiber Reinforced Polymeric materials (CFRP), intended for structural applications in the automotive and aviation sectors, have been studied from the point of their energy absorption capabilities when submitted to transverse low-velocity impact loading. Carbon fiber-epoxy composite prepregs were placed on the inside of the single hat sectioned aluminum sheet and completely cured in the autoclave under the recommended curing cycle. The bonding process between the aluminum sheet and composite layers was achieved by using 3M VHB™ 4930 double-sided acrylic foam tape. Bonding the aluminum and composite layers through adhesive tape eliminates the requirement of surface preparation of the aluminum layer through chemical etching or mechanical abrasion and thereby the strength of the metallic layer is not reduced due to the formation micropores during the chemical etching process. Results are shown in terms of load-displacement and damage morphologies diagrams; characteristic trends are compared and discussed. It was observed that the presence of viscoelastic adhesive tape material restricts the rupture (visual cracks) failure of the outer aluminum layer, resulting in the only impact-induced indentation for all impact energies. Numerical simulations were also performed to characterize and predict the failure mechanism of such hybrid beams when subjected to impact loading. Numerical predictions showed good correlation with experimental results for all impact histories at low and medium impact energies but a showed slight discrepancy for highest impact energy and were not able to successfully capture the system response in the unloading region. Current modeling does not consider damage healing or recovery with unloading and it is difficult to account for such change in material state. This study provides the low-velocity impact characteristics and collapse behavior of the hybrid hat sectioned beams under tensile and shear forces developed by impact loading by providing insight to their primary damage mechanisms relative to the impact energies. It was found that the primary damage of the specimen's changes from impact-induced indentation, minimal fiber breakage to partial perforation accompanied by larger indentation depth as the impact energy is increased from 6 to 12 J.

Failure Characteristics of Composite Metallic Foam Core Hat-Shaped Tubular T-joints under Static and Impact Loading

Failure of Single Hat-Shaped Thin-Walled Tubular Composite T-joints under Impact Loading

Experimental Investigation into Influences of Z-pin and Deltoid on Structural Properties and Damage Tolerance of CFRP T-joints

Quasi-static Axial Crushing and Transverse Bending of Double Hat Shaped CFRP Tubes

Bending behavior of single hat-shaped composite T-joints under out-of-plane loading for lightweight automobile structures:

Hail Impact Responses and Residual Tensile Properties of CFRP T-joints

Analysis of Torsional Failure and Bearing Capacity of Composite Thin-Walled Tubes Filled with Plastic Foam

Low-velocity Impact Performance of Composite-Aluminum Tubes Prepared by Mesoscopic Hybridization

Failure and Optimization of Composite-to-steel Adhesive Bonded Y-joints under Three-Point Bending

Deformation and Failure of Hybrid Composite Sandwich Beams with a Metal Foam Core under Quasi-Static Load and Low-Velocity Impact

Experimental investigation into dynamic axial impact responses of double hat shaped CFRP tubes

Low-Velocity Impact Characteristics of Hybrid Aluminum/CFRP Single Hat Sectioned Beam Adhesively Bonded Using Adhesive Tape

Bending Performance and Failure Mechanism of Cfrp/Al Hat-Shaped Thin-Walled Hybrid Beams

Transverse Bending and Axial Compressing Mechanical Characteristics of Carbon Fiber Reinforced Plastic Sandwich Laminated Square Tubes

On the mechanical performance and damage evolution of rivet-bonded composite T-joint under three-point bending: A combined experimental and numerical study

Failure Analysis and Local Geometric Parameter Design for Foam Core Sandwich T-joints

Quasi-static and low-velocity axial crushing of polyurethane foam-filled aluminium/CFRP composite tubes: An experimental study

The effect of impactor shape on the low-velocity impact behavior of hybrid corrugated core sandwich structures

Investigations on the Mechanical Properties of Composite T-Joints with Defects under Bending Loading

Energy Absorption and Failure Pattern of Hybrid Composite Tubes under Quasi-Static Axial Compression

Experimental Investigation into the Failure of CFRP T-joints under Ice Impact and Quasi-static Loadings