Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

Effect of Non-Uniform Microstructure on Rolling Contact Fatigue Performance of Bainitic Rail Steel

The effect of microstructure evolution on the ratchetting-fatigue interaction of carbide-free bainite rail steels under different heat-treatment conditions

Effect of microstructure on wear and rolling contact fatigue behaviors of bainitic/martensitic rail steels

Study on fatigue wear competition mechanism and microstructure evolution on the surface of a bainitic steel rail

Evolution of microscopic characteristics of rolling contact fatigue coexisting with wear of U75V rail

Comparison of the damage and microstructure evolution of eutectoid and hypereutectoid rail steels under a rolling-sliding contact

Research progress on rolling contact fatigue damage of bainitic rail steel

Influence of stratified tribologically transformed structure layers on contact fatigue crack initiation of bainitic rail steel

Rail rolling contact fatigue formation and evolution with surface defects

On the Formation and Damage Mechanism of Rolling Contact Fatigue Surface Cracks of Wheel/rail under the Dry Condition

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Effect of Mechanical Properties of Rail and Wheel on Wear and Rolling Contact Fatigue

Consequences of thermite welding on the microstructure of the heat affected zone of a carbide-free bainitic steel rail

Microstructural evolution and performance change of a carburized nanostructured bainitic bearing steel during rolling contact fatigue process

Research on the damage mechanism of the rolling contact fatigue of a wheel–rail contact system under the influences of surface defects

Laboratory Study of the Rolling Contact Fatigue of High Manganese Steel Crossings

Study on wear and rolling contact fatigue behaviours of defective rail under different slip ratio and contact stress conditions

Assessment of microstructure- and inclusion-induced fatigue crack initiation in bainitic/martensitic rail steels: competing and synergistic effects

Rolling Contact Fatigue Wear Behavior of Carbide-free Bainitic Steel

Experimental study on wheel-rail rolling contact fatigue damage starting from surface defects under various operational conditions

A novel microstructure of carbide-free bainitic medium carbon steel observed during rolling contact fatigue