Abstract:The novel bismuth-substituted rare earth iron garnet films were grown by the modified liquid phase epitaxy (LPE) technique for use as a 45degrees faraday rotator in optical isolators. First, single crystals of Y3Fe5O12(YIG), with a lattice, constant of 1.2378 nm, were grown by means of the Czochralski method. Using YIG instead of the conventional nonmagnetic garnet of Gd3Ga5O12(GGG) as a substrate, a film of BiYbIG was grown by means of the LPE method from Bi2O3-B2O3 fluxes. The structural, magnetic and magneto-optical properties of BiYbIG LPE film/YIG crystal composite were investigated using X-ray diffraction (XRD), electron probe microanalysis (EPMA), vibrating sample magnetometry (VMS) and near-infrared transmission spectrometry. The saturation magnetization 47piM(s) was estimated to be about 1200 G. The Faraday rotation spectrum was measured by the method of rotating analyzer ellipsometry (RAE) with the wavelength varied from 800 to 1700 nm. The resultant Bi0.37Yb2.63Fe5O12 LPE film/YIG crystal composite shows an increased Faraday rotation coefficient due to doping W, ions on the dodecahedral sites of the magnetic garnet without increasing absorption loss, therefore a good magneto-optic figure of merit, defined by the ratio of Faraday rotation and optical absorption loss, can achieved of 21.5 and 30.2degrees/dB at 1300 and 1550 nm wavelengths respectively at room temperature. Since Yb3+ ions and Y3+ ions provide the opposite contributes to the wideband and temperature characteristics of Faraday rotation, the values of Faraday rotation wavelength and temperature coefficients are reduced to 0.06%/nm and 0.007 degrees(.) degreesC(-1) at 1550 nm wavelength respectively.

Dysprosium Substituted Ce:YIG Thin Films for Temperature Insensitive Integrated Optical Isolator Applications

Silicon Integrated Dysprosium Substituted Ce:Yig Thin Films For Integrated Optical Isolator Applications

Dysprosium Substituted Ce:YIG Thin Films with Perpendicular Magnetic Anisotropy for Silicon Integrated Optical Isolator Applications

Mixed rare-earth iron garnet AYbBiIG single-crystals for high-performance optical isolation

Enhancing Temperature Stability of Ce: RIG Films Faraday Rotation through Magnetic Sublattice Control

Enhanced magneto-optical effect in Y1.5Ce1.5Fe5O12 thin films deposited on silicon by pulsed laser deposition

Silicon integrated nonreciprocal photonic devices using monolithically integrated magnetic oxides

Growth and Characterization of Magneto-Optical Single-Crystal Reybbiig with Temperature-Stabilized Faraday Rotation

Fabrication and performance optimization of novel (Tb0.9975R0.0025)3Sc2Al3O12 (R= Pr, Ho, Dy, Eu) magneto-optical transparent ceramics

Observation of Enhanced Faraday Effect in Eu-Doped Ce:YIG Thin Films

MAKING MAGNETO-OPTIC CE-SUBSTITUTED YIG THIN FILMS ON AMORPHOUS SILICA SUBSTRATE

Microstructures and Magnetic Properties of Single-Step Deposited Ce:YIG/YIG Bilayer Films with Different Layer Thickness Ratios

Bismuth-substituted yttrium iron garnet film/frystal composite for Faraday rotators

Highly Sensitive Optical Thermometer Based on Li+-doped Erbium Ytterbium Silicate Films

Study on wideband and temperature properties of TbybBiIg crystal in 1500 similar to 1620nm band

Magneto-optical Enhancement in Highly Poly-crystallized Ce Substituted YIG Thin Films by PLD

Interface-Mediated YIG/Ce:YIG Bilayers Structure with Enhanced Magneto-optical Properties via Pulsed Laser Deposition

Magnetic and Magneto-Optical Properties of Ceyig Thin Films Grown by Pulsed Laser Deposition on Quartz Substrates

Magneto‐Optical Bi:YIG Films with High Figure of Merit for Nonreciprocal Photonics

Fine-grained transparent Dy 2 O 3 ceramics fabricated from precipitated powders without sintering aids

Temperature-dependent optical dispersion of composite cerium oxide and barium zirconate single layers and multi-layers