Locating Gases in Porous Materials : Cryogenic Loading of Fuel Related Gases Into a Sc-based MOF under Extreme Pressures
Jorge Sotelo,Christopher H. Woodall,Dave R. Allan,Eugene Gregoryanz,Ross T. Howie,Konstantin V. Kamenev,Michael R. Probert,Paul A. Wright,Stephen A. Moggach
2016-01-01
Abstract:An alternative approach to loading metal organic frameworks with gas molecules at high (kbar) pressures is reported. The technique, which uses liquefied gases as pressure transmitting media within a diamond anvil cell along with a single-crystal of a porous metal organic framework, is demonstrated to have considerable advantages over other gas-loading methods when investigating host-guest interactions. Specifically, loading the metal organic framework Sc2BDC3 with liquefied CO2 at 2 kbar reveals the presence of three adsorption sites, one previously unreported, and resolves previous inconsistencies between structural data and adsorption isotherms. A further study with supercritical CH4 at 3 – 25 kbar demonstrates hyperfilling of the Sc2BDC3 and two high pressure displacive and reversible phase transitions are induced as the filled MOF adapts to reduce the volume of the system. Understanding how guest molecules in metal-organic framework (MOFs) interact with each other and the framework they occupy upon adsorption is vital for the development and commercial application of MOFs, for example in carbon capture and gas sequestration technologies. Spectroscopic techniques, such as IR and solid state NMR are often used for probing these interactions. Crystallographic studies, both X-ray and neutron, utilizing various environmental cells have proven invaluable in determining the nature of host-guest interactions within MOFs and their guest-driven structural flexibility. This is particularly important in the many cases where the uptake behavior, which can include conformational changes in the framework itself, can be perturbed by the type and amount of guest adsorbed. One of the main reasons why so little data is available is that the experimental location of gas molecules in MOFs is challenging. The gas molecules are often disordered and exhibit thermal motion which is difficult to model crystallographically even when cooled close to the freezing temperature of the gas adsorbed. In-situ cells have been developed for collecting crystallographic data whilst exposing a MOF to a gaseous environment at tens, or even hundreds of bars of pressure in an effort to saturate the pores with gas molecules, though even here, the gas molecules are often difficult to observe experimentally. For these reasons, despite the intensive research in carbon capture technologies, relatively few crystallographic studies have been reported where CO2 molecules have been unambiguously located within MOFs. The use of condensed gases as pressure transmitting media (PTM) in diamond anvil cells is commonplace in the fields of condensed matter physics and high-pressure mineralogy due to their excellent hydrostatic properties at very high-pressures (> 10 GPa) relative to common liquid PTMs. He, Ar and Ne are typically used because they are chemically inert, whilst other gases have been studied for their diverse structural behavior. High temperature and pressure phases of CO2 and CH4 are of interest for understanding planetary interiors, for example, while the formation and decomposition of methane-hydrates, which are only stable at pressure, has been studied in great detail. Both CO2 and CH4 are of obvious industrial and environmental interest. Here, we present a high-pressure study of the MOF Sc2BDC3 (BDC = benzene-1,4-dicarboxylate) using both CO2 and CH4 as PTM. Recent work has demonstrated the active role that PTMs play in high-pressure studies of porous materials, where the ability of the PTM to penetrate the framework can be used to “hyperfill” the pores. For example, in a previous study of Sc2BDC3 using methanol as a PTM, the pores were hyperfilled with methanol molecules at 16 kbar, achieving a density 2.5 times larger than possible under ambient pressure conditions. Furthermore, a previous high-pressure study on the zeolitic imidazolate framework, ZIF-8 (Zn(MeIm)2, MeIm = 2methylimidazole), revealed a previously unobserved framework conformation, which has since been used to explain a step in its adsorption isotherm observed for a number of gases, and the increased loading capacity on increasing gas pressure. In the case of Sc2BDC3, gas cell structural work and isotherms by Miller et al. using both CO2 and CH4 revealed interesting features worthy of further investigation. Adsorption of CO2 into Sc2BDC3 at 1 bar and 235 K causes a phase transition, which results in a change in space group symmetry from Fddd to C2/c. The transition is characterized by a subtle rotation of one of the two symmetry independent BDC linkers upon exposure to CO2. This results in three symmetry independent linkers (Group 1, 2a and 2b) and gives rise to two crystallographically independent channels with one absorption site in each channel (Site 1 and Site 2, Figure 1a). Site 1 lies across two Group 2a linkers with host-guest C-H···O distances of ca. 2.9 Å and Site 2 is disordered over two positions and also has close C-H···O contacts that range from 2.78 to 2.98 Å. At [a] Mr. J. Sotelo, Dr. S. A. Moggach EaStChem School of Chemistry and Centre for Science at Extreme Conditions, University of Edinburgh, David Brewster road, Joseph Black Building, Edinburgh EH9 3FJ (UK) E-mail: smoggach@staffmail.ed.ac.uk [b] Dr. C.H. Woodall School of Engineering and Centre for Science at Extreme Conditions, University of Edinburgh, Peter Gurthrie Tait Road, Erskine Williamson Building, EH9 3FD (UK) [c] Dr. R. T. Howie School of Physics and Centre for Science at Extreme Conditions, University of Edinburgh, Peter Gurthrie Tait Road, Erskine Williamson Building, EH9 3FD (UK) [d] Dr. Michael R. Probert School of Chemistry, Newcastle University, Newcastle upon Tyne, NE1 7RU (UK) [e] Dr. D. R. Allan Diamond Light Source, Harwell Campus, Didcot, OX11 ODE (UK) [f] Prof. P. A. Wright EaStCHEM School of Chemistry, Purdie Building University of St. Andrews, St. Andrews KY16 9ST (UK) Supporting information for this article is given via a link at the end of the document