Abstract:TiO2 has been intensively investigated as an anode material for lithium-ion batteries (LIBs) in 1.0–3.0 V (vs Li+/Li). However, it is a challenge to realize its theoretical capacity (336 mAh g–1) in this limited potential range. Extending the potential range below 1.0 V would increase its capacity but usually at the expense of its cyclic stability owing to the sluggish ionic diffusion and unsatisfactory structural stability. Here, three-dimensional (3D) macroporous TiO2 microspheres with interconnected pores and nanocrystalline thin walls have been constructed through a scalable template-assisted spray drying method to overcome these obstacles. When applied to LIBs, high and stable discharge capacity (300 mAh g–1 at 0.1 A g–1) as well as superior cyclic stability (242 mAh g–1 after 1000 cycles at 1.0 A g–1) can be achieved under deep discharging/charging conditions (0.01–3.0 V vs Li+/Li). Furthermore, the 3D macroporous structure is well preserved under deep discharging/charging and the in situ X-ray diffraction (XRD) patterns and Raman spectra reveal the dominant pseudocapacitive contribution at low potentials (0.01–1.0 V). This work not only develops a facile method to synthesize macroporous metal oxides but also provides insight into the lithium storage mechanism of TiO2 under deep discharging/charging conditions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c02411?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c02411</a>.Additional experimental details; comparison of the electrochemical performances (Table S1); SEM image of APF templates (Figure S1); FTIR spectrum (Figure S2); TGA curve (Figure S3); XPS survey spectrum, high-resolution Ti 2p spectrum, and high-resolution O 1s spectrum (Figure S4); XRD patterns (Figure S5); SEM and TEM images (Figure S6); HRTEM image (Figure S7); high-resolution C 1s XPS spectra (Figure S8); SEM images (Figure S9); EIS spectra (Figure S10); lithium storage performances (Figure S11); cycling performance (Figure S12); capacitive contributions (Figure S13); and Raman spectra (Figure S14) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c02411/suppl_file/am1c02411_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Flower-like TiO<sub>2</sub> hollow microspheres with mixed-phases for high-pseudocapacitive lithium storage

Flower-like TiO2 hollow microspheres with mixed-phases for high-pseudocapacitive lithium storage

Crystalline SnO2 @ Amorphous TiO2 Core-Shell Nanostructures for High-Performance Lithium Ion Batteries

Fabrication of hollow TiO2 nanospheres for high-capacity and long-life lithium storage

Hierarchical Nanosheet-Constructed Yolk-Shell TiO₂ Porous Microspheres for Lithium Batteries with High Capacity, Superior Rate and Long Cycle Capability.

3D anatase TiO2 hollow microspheres assembled with high-energy {001} facets for lithium-ion batteries

TiO2 Microboxes with Controlled Internal Porosity for High‐Performance Lithium Storage

SiO@C/TiO2 nanospheres with dual stabilized architecture as anode material for high-performance Li-ion battery

Template-free construction of hollow TiO2 microspheres for long-life and high-capacity lithium storage

Constructing Three-Dimensional Macroporous TiO 2 Microspheres with Enhanced Pseudocapacitive Lithium Storage under Deep Discharging/Charging Conditions

Facile Synthesis and Electrochemical Characterization of Porous and Dense TiO2 Nanospheres for Lithium-Ion Battery Applications

Hollow TiO2–X Porous Microspheres Composed of Well-Crystalline Nanocrystals for High-Performance Lithium-Ion Batteries

Walnut-like Porous Core/Shell TiO2 with Hybridized Phases Enabling Fast and Stable Lithium Storage

Rational design of hollow Ti2Nb10O29 nanospheres towards High-Performance pseudocapacitive Lithium-Ion storage

TiO2 Modified Α-Fe2o3 Pompon-Like Hollow Sphere As the Anode Material for Lithium-Ion Batteries with Mixed Lithiation Mechanisms

Lithium Storage Performance of Hollow and Core/Shell TiO2 Microspheres Containing Carbon

TiO2hollow Spheres with Large Amount of Exposed (001) Facets for Fast Reversible Lithium Storage

Constructing Sub 10 Nm Scale Interfused TiO2/SiOx Bicontinuous Hybrid with Mutual-Stabilizing Effect for Lithium Storage.

Introduction of amorphous TiO2 coating layer to improve the lithium storage of SiO2 nanospheres anode

TiO2 Coated Si/C Interconnected Microsphere with Stable Framework and Interface for High-Rate Lithium Storage

Modified Preparation of Si@C@TiO2 Porous Microspheres As Anodes for High-Performance Lithium-Ion Batteries.