Constructing Three-Dimensional Macroporous TiO 2 Microspheres with Enhanced Pseudocapacitive Lithium Storage under Deep Discharging/Charging Conditions

Ruhan He,Zhenhui Liu,Pan He,Wen Luo,Ruohan Yu,Xufeng Hong,Xuelei Pan,Qingqu Zhou,Liqiang Mai,Liang Zhou

DOI: https://doi.org/10.1021/acsami.1c02411

2021-04-01

Abstract:TiO₂ has been intensively investigated as an anode material for lithium-ion batteries (LIBs) in 1.0–3.0 V (<i>vs</i> Li⁺/Li). However, it is a challenge to realize its theoretical capacity (336 mAh g^–1) in this limited potential range. Extending the potential range below 1.0 V would increase its capacity but usually at the expense of its cyclic stability owing to the sluggish ionic diffusion and unsatisfactory structural stability. Here, three-dimensional (3D) macroporous TiO₂ microspheres with interconnected pores and nanocrystalline thin walls have been constructed through a scalable template-assisted spray drying method to overcome these obstacles. When applied to LIBs, high and stable discharge capacity (300 mAh g^–1 at 0.1 A g^–1) as well as superior cyclic stability (242 mAh g^–1 after 1000 cycles at 1.0 A g^–1) can be achieved under deep discharging/charging conditions (0.01–3.0 V <i>vs</i> Li⁺/Li). Furthermore, the 3D macroporous structure is well preserved under deep discharging/charging and the <i>in situ</i> X-ray diffraction (XRD) patterns and Raman spectra reveal the dominant pseudocapacitive contribution at low potentials (0.01–1.0 V). This work not only develops a facile method to synthesize macroporous metal oxides but also provides insight into the lithium storage mechanism of TiO₂ under deep discharging/charging conditions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c02411?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c02411</a>.Additional experimental details; comparison of the electrochemical performances (Table S1); SEM image of APF templates (Figure S1); FTIR spectrum (Figure S2); TGA curve (Figure S3); XPS survey spectrum, high-resolution Ti 2p spectrum, and high-resolution O 1s spectrum (Figure S4); XRD patterns (Figure S5); SEM and TEM images (Figure S6); HRTEM image (Figure S7); high-resolution C 1s XPS spectra (Figure S8); SEM images (Figure S9); EIS spectra (Figure S10); lithium storage performances (Figure S11); cycling performance (Figure S12); capacitive contributions (Figure S13); and Raman spectra (Figure S14) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c02411/suppl_file/am1c02411_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology