Abstract:Porous carbon materials are widely used in electrical double-layered capacitors for energy storage applications due to their abundant pores, high specific surface area and excellent electrochemical stability although their intrinsic electrical conductivity is generally low. Traditional high-temperature treatment was always adopted to boost the electrical conductivity of porous carbon materials by enhancing their graphitization degree, while this would always be accompanied by severe damage to pore structure and corresponding electrochemical performance. To solve the dilemma between boosting electrical conductivity and retaining pore structure, in this research, we proposed a low-temperature catalytic graphitization for hollow carbon spheres (HCSs) prepared by modified Stober method accompanied with a special pore structure tailoring strategy. By altering the timing of adding carbon source, followed by secondary pore-forming and catalytic graphitization, HCSs with thin and porous shell walls along with enhanced conductivity were synthesized. Compared with the untreated HCSs or high-temperature graphitized HCSs, HCSs fabricated by the aforementioned combined strategies exhibited enhanced pore volume, specific surface area (2160.1 m(2).g(-1), 165.3 % of the untreated group) and conductivity (16.44+0.05 S.cm(-2), 221.5% of the untreated group), demonstrating much better electrochemical performance as the mass specific capacitance reached 256.7 F.g(-1) and a volume specific capacitance reached 102.7 F.cm(-3) at a current density of 1 A.g(-1). Moreover, due to the largely promoted conductivity, the capacitance with the catalytic graphitized HCSs as the electrode material could be further boosted up to 273.4 F.g(-1) at 1 A.g(-1) by exempting the generally indispensable conductive agents and a high capacitance retention of 100.7 % was achieved after 5000 cycles at a relatively high current density of 10 A.g(-1). This could be attributed to local graphitization brought by dispersed catalyst particles instead of entire atom rearrangement during high-temperature graphitization which would result in severe pore vanishing. The synergy of low-temperature catalytic graphitization and secondary pore-forming might be a novel strategy in electrode material fabrication for advanced supercapacitors or other energy storage devices.

High Capacitive Storage Behavior of Hierarchically Porous Hollow‑carbon Spheres Derived from the Coupling of Template-Directing and Post-Activation Methodology

Synthesis of Hierarchical Porous Carbon from Metal Carbonates Towards High-Performance Lithium Storage

Controlled Preparation of Hollow and Porous Co9S8 Microplate Arrays for High-Performance Hybrid Supercapacitors

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Hierarchical Porous Carbon Guided by Constructing Organic-Inorganic Interpenetrating Polymer Networks to Facilitate Performance of Zinc Hybrid Supercapacitors

Cooking Carbon with Protic Salt: Nitrogen and Sulfur Self-Doped Porous Carbon Nanosheets for Supercapacitors

Structure Engineering in Interconnected Porous Hollow Carbon Spheres with Superior Rate Capability for Supercapacitors and Lithium-Sulfur Batteries

Improving the Pore-Ion Size Compatibility Between Poly(ionic Liquid)-Derived Carbons and High-Voltage Electrolytes for High Energy-Power Supercapacitors

Two Birds with One Stone: Hydrogel-Derived Hierarchical Porous Activated Carbon toward the Capacitive Performance for Symmetric Supercapacitors and Lithium-Ion Capacitors

Turn the dust into glory: Hierarchical porous carbon cubes derived from waste tire pyrolysis oil exhibits high capability in symmetric capacitors

Hierarchical porous carbon sheets derived on a MgO template for high-performance supercapacitor applications

Design and Fabrication of Hierarchically Porous Carbon with a Template-free Method

Tailoring Microstructure and Conductivity of Porous Hollow Carbon Spheres to Enhance Their Performance As Electrode Materials for Supercapacitors

Heteroatoms-doped hierarchical porous carbon with multi-scale structure derived from petroleum asphalt for high-performance supercapacitors

Combined contributions from multidimensional micropores and mesopores of hierarchical porous carbons for extraordinary Li-ion storage applications

An in-situ Blowing-etching strategy for preparation of Macro-meso-micro hierarchical porous carbon and its supercapacitive property

Facile synthesis of hierarchically porous carbon monolith without templating agent for various applications in energy and catalysis

Polytetrafluoroethylene-assisted removal of hard-template to prepare hierarchically porous carbon for high energy density supercapacitor with KI-additive electrolyte

A Facile Route to Synthesis of Hierarchically Porous Carbon via Micelle System for Bifunctional Electrochemical Application

In-Situ Molten Salt Template Strategy For Hierarchical 3d Porous Carbon From Palm Shells As Advanced Electrochemical Supercapacitors

Microporous tungsten oxide spheres coupled with Ti3C2Txnanosheets for high-volumetric capacitance supercapacitors