Medium-entropy (me,ti)0.1(zr,hf,ce)0.9o2 (me= Y and Ta): Promising Thermal Barrier Materials for High-Temperature Thermal Radiation Shielding and CMAS Blocking
Shuaihang Qiu,Huimin Xiang,Fu-Zhi Dai,Hailong Wang,Muzhang Huang,Chunlei Wan,Qing Meng,Jiangtao Li,Xiaohui Wang,Yanchun Zhou
DOI: https://doi.org/10.1016/j.jmst.2022.01.019
2022-01-01
Journal of Material Science and Technology
Abstract:With continuous enhancement of gas-turbine inlet temperature and rapid increase of radiant heat trans-fer,thermal barrier coating(TBC)materials with a combination of low thermal conductivity and good high-temperature thermal radiation shielding performance play vital roles in ensuring the durability of metallic blades.However,yttria-stabilized zirconia(YSZ),as the state-of-the-art TBC and current industry standard,is unable to meet such demands since it is almost translucent to high-temperature thermal ra-diation.Besides,poor corrosion resistance of YSZ to molten calcia-magnesia-alumina-silicates(CMAS)also impedes its application in sand,dust,or volcanic ash laden environments.In order to improve the high-temperature thermal radiation shielding performance and CMAS resistance of YSZ and further reduce its thermal conductivity,two medium-entropy(ME)oxide ceramics,ME(Y,Ti)0.1(Zr,Hf,Ce)0.9O2 and ME(Ta,Ti)0.1(Zr,Hf,Ce)0.9O2,were designed and prepared by pressureless sintering of binary powder com-pacts in this work.ME(Y,Ti)0.1(Zr,Hf,Ce)0.9O2 presents cubic structure but a trace amount of secondary phase,while ME(Ta,Ti)0.1(Zr,Hf,Ce)0.9O2 displays a combination of tetragonal phase(81.6 wt.％)and cubic phase(18.4 wt.％).Both ME(Y,Ti)0.1(Zr,Hf,Ce)0.9O2 and ME(Ta,Ti)0.1(Zr,Hf,Ce)0.9O2 possess bet-ter high-temperature thermal radiation shielding performance than YSZ.Especially,the high-temperature thermal radiation shielding performance of ME(Ta,Ti)0.1(Zr,Hf,Ce)0.9O2 is superior to that of ME(Y,Ti)0.1(Zr,Hf,Ce)0.9O2 due to its narrower band gap and correspondingly higher infrared absorbance(above 0.7)at the waveband of 1 to 5 μm.The two ME oxides also display significantly lower thermal conductivity than YSZ and close thermal expansion coefficients(TECs)to YSZ and Ni-based superalloys.In addition,the two ME oxides possess excellent CMAS resistance.After attack by molten CMAS at 1250℃for 4 h,merely～2 μm thick penetration layer has been formed and the structure below the penetration layer is still intact.These results demonstrate that ME(Me,Ti)0.1(Zr,Hf,Ce)0.9O2(Me=Y and Ta),espe-cially ME(Ta,Ti)0.1(Zr,Hf,Ce)0.9O2,are promising thermal barrier materials for high-temperature thermal radiation shielding and CMAS blocking.