Abstract:Magnetic nanoparticles and thin films exhibiting a large magnetic anisotropy energy density (MAE) have attracted enormous attention over the last years due to their potential use in magnetic data storage or sensing applications. FePt alloy nanoparticles and films have a huge MAE in the chemically ordered L10 phase. This ordered phase is typically obtained by annealing the as-prepared chemically disordered fcc FePt nanoparticles at temperatures above 600°C. Besides standard colloidal approaches [1], such fcc FePt nanoparticles can be fabricated by a micellar technique resulting in regular arrays on various substrates [2,3]. This approach offers the advantage that the interparticle distance can be tuned between 20-100 nm. Due to the larger separation particle agglomeration can be avoided during the annealing induced transformation into the L10 phase. Moreover, the particles are magnetostatically decoupled. We investigated the formation of the L10 phase for 2-10 nm FePt particles as a function of the annealing temperature and time on Si/SiOx substrates. Hysteresis loops at T = 15K reveal strongly enhanced coercive field after an annealing step at 700°C for 30 min compared to the as-prepared particles. The effective MAE is found to be 1-2×10 J/m using simple Stoner-Wohlfarth modeling that is a factor of 3-5 smaller than the FePt bulk MAE. In order to correlate the magnetic properties to the structure of the particles we performed transmission electron microscopy (TEM) investigations of FePt particles on both, Si/SiOx and MgO(001) substrates. Basically, the lowered MAE could originate from defective crystal structures, imperfect ordering of Feand Pt-planes (chemical ordering parameter), and/or inhomogeneous segregation of Fe/Pt within the particles. The applied TEM methods included conventional TEM (bright-field, dark-field, electron diffraction), spherical aberration corrected high resolution imaging and scanning TEM (Z-contrast). It was found that most particles contain defects such as stacking faults and multiple twins (Figure 1). Calculated TEM images based on various models of FePt nanoparticles (Figure 2) were generated and compared to experimental images especially to analyze and to determine the chemical ordering parameter of the L10 phase, crystal structure and defects.

Observation of L1-like Chemical Ordering in a Decahedral FePt Nanoparticle by Cs-corrected High Resolution Transmission Electron Microscopy

Observation Of L1(0)-Like Chemical Ordering In A Decahedral Fept Nanoparticle By C-S-Corrected High Resolution Transmission Electron Microscopy

Observation of L1[subscript]0-like Chemical Ordering in a Decahedral FePt Nanoparticle by C[subscript]s-corrected High Resolution Transmission Electron Microscopy

Chemical order-disorder nanodomains in Fe3Pt bulk alloy

Structure Investigation of the Fe on Cu(110) Surface

The Structure of FePc on Cu(100)

In-situ Atomic-Scale Visualization of Ordering Transformations in Pt-Fe Nanoalloys

Ordering and Curie temperatures of FePt nanoparticles

Observation and Elimination of Broken Symmetry in L1 FePt Nanostructures

Au composition dependent order-disorder transitions of Fe−Pt intermetallic compounds: experiments and thermodynamic analysis

Composition-dependent Ordering Transformations in Pt-Fe Nanoalloys

Observation of an Electronic Order along [110] Direction in FeSe

Structural and Magnetic Investigations on FePt Nanoparticles

Enhanced L10 Ordering and (001) Orientation in Fept: Ag Nanocomposite Films by Monatomic Layer Deposition

Size-dependent Ordering and Curie Temperatures of FePt Nanoparticles

The disorder-order transition of FeCuPt nanoparticles with various Cu content

Ferromagnetic Stability in Fe Nanodot Assemblies on Cu(111) Induced by Indirect Coupling Through the Substrate

Chemical Orderings in CuCo Nanoparticles: Topological Modeling Using DFT Calculations

Revealing Surface Restraint-Induced Hexagonal Pd Nanocrystals via In Situ Transmission Electron Microscopy

Local Chemical Strain in PtFe Alloy Nanoparticles

Improving the ordering and coercivity of L10-FePt nanoparticles by introducing PtAg metastable phase