Formation Mechanism of Tisi Phase and Silicide Kinds on Microstructure and Mechanical Properties for Ti-5al-5mo-5cr-3nb-2zr Alloyed by Silicon
Shichen Sun,Hongze Fang,Yili Li,Xiaofu Zhang,Ruirun Chen,Jingjie Guo
DOI: https://doi.org/10.2139/ssrn.4216149
2022-01-01
SSRN Electronic Journal
Abstract:To investigate formation mechanism of TiSi phase and evaluate the effect of silicide kinds on microstructure and mechanical properties, Ti-5Al-5Mo-5Cr-3Nb-2Zr- x Si (Ti- x Si, wt.%, x = 0, 0.2, 0.4, 0.6, 0.8) alloys were melted by vacuum arc melting. Results show that the microstructure is composed of grain boundary α phase (α GB ), secondary α phase (α s ), primary α phase (α p ) and residual β phase when the silicon content is less than 0.2 wt.%. When the silicon content increases from 0.4 to 0.8 wt.%, the content of Ti 5 Si 3 phase decreases. The content of TiSi phase increases, the size of it increases from 40 nm to 0.8 μm. Ti 5 Si 3 precipitates in the transformed microstructure of β phase and TiSi is distributed in the α GB phase. The excess silicon atoms occupy the interstitial space in the cell of α titanium because of the high silicon addition and interface energy, and then form the TiSi phase. With the increase of silicon content, the tensile strength increases from 1068.1 to 1168.6 MPa. The tensile strain and fracture toughness increase at 0~0.2 wt.% and then decrease at 0.4~0.8 wt.%, reach the highest values in Ti-0.2Si of 7.1% and 66.4 MPa·m 1/2 , respectively. The strength is improved due to the solid solution of Si, precipitation of Ti 5 Si 3 and the strengthening effect caused by the difference of crystal plane spacing between TiSi and α GB phase. More content of silicide lead to the gradual transformation from intergranular ductile fracture to intergranular brittle fracture.