Abstract:The influence of Si addition on the microstructure and mechanical behavior of cast silicon stainless steel alloys was investigated. It was recognized that after incorporation of Si in the range of ∼ 2–6 wt%, microstructure changes significantly. It transforms from single-phase austenitic to duplex microstructure containing ferrite and austenite. In addition, TiC precipitates with angular and spherical morphology were observed in all the sample conditions. Uniaxial tensile tests suggested that the incorporation of Si improved the strength and ductility as long as the microstructure remains primarily austenitic. However, at much higher silicon content (∼6 wt%), microstructure transformed to duplex structure, followed by the drastic reduction in ductility and toughness. Overall, the alloy with ∼4 wt% Si exhibited comparatively better strength, ductility as well as toughness. The mechanical properties of the individual phases, characterized using nanoindentation, indicated that the hardness and modulus of the austenite phase improved significantly after Si incorporation up to ∼6 wt%. Concomitantly correlation between the mechanical properties and crystallographic orientation of grains was also established by performing post-nanoindentation EBSD analysis. The results indicated that the average hardness and modulus of each phase are significantly related to the crystallographic orientation of grains, i.e., it is highly anisotropic. Finally, the nanomechanical properties of the individual phases were utilized to predict and compare the bulk mechanical properties using the ECM model. A reliable quantitative comparison between nanomechanical and bulk mechanical properties of alloys with single-phase microstructure was obtained, whereas a more refined ECMs are required for envisaging the bulk characteristics of the materials with duplex microstructure.

Microstructure and mechanical properties of 2200 MPa grade ultra-high strength low alloy steels

Microstructure and mechanical properties of high-carbon Si-Al-rich steel by low-temperature austempering

Microstructure and mechanical properties of a low carbon carbide-free bainitic steel co-alloyed with Al and Si

Effect of Si Content on Microstructure and Properties of Low-Carbon Medium-Manganese Steel after Intercritical Heat Treatment

Mechanical Properties and Microstructures of A Novel Low Carbon High-Silicon Martensitic Steel

Microstructure and Mechanical Properties of Advanced High-Silicon Austempered Steel

Influence of Si Contents on Microstructures and Mechanical Properties of High Strength and Toughness 7050 Aluminum Alloys

Mechanical Properties of Plain Carbon Steels with Ultrafine (α+θ) Microstructures

Effect of Heat Treatment on Microstructure and Properties of Improved 40crni2si2mov Steel

Microstructure and Mechanical Properties of Low- and Medium-Carbon Si-Rich Low-Alloy Steels Processed by Austemping after Intercritical Annealing

Effect of Austenitizing Temperature and Retained Austenite on Mechanical Properties of 2200MPa Grade Ultra-High Strength Steels

Effects of Silicon on the Microstructure and Mechanical Properties of 15–15ti Stainless Steel

Microstructure and Mechanical Properties of Chromium-Alloyed Silicon Cast Steel

Influence of Silicon on Microstructure and Mechanical Properties of Fe-(4.5-7.0)%Si High-silicon Steel

Microstructure Regulation and Mechanical Properties of Low-Carbon Multiphase Steels

Effect of Austenitising Temperature on Microstructure and Mechanical Properties of 30si2crni4monb Ultrahigh Strength Steel

Effect of Nickel Content on Mechanical Properties of 2200 MPa Grade Ultra-High Strength Steels

Microstructural evolution and mechanical properties of 60Si2CrVNb spring steel under quenching-tempering heat treatment process

Influence of Si content on the microstructure and mechanical properties of silicon stainless steel

Microstructure and Properties of 1.6%C Ultra-high Carbon Steel

Effect of cooling rate on microstructure and mechanical properties of a low-carbon low-alloy steel