Superior temperature stability of electromechanical properties and resonant frequency in PYN-PZT piezoelectric ceramics
Xin Liu,Xiaodan Ren,Mingyang Tang,Yike Wang,Zhuo Xu,Yongke Yan
DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.09.076
IF: 5.7
2023-09-01
Journal of the European Ceramic Society
Abstract:In this study, the Pb(Yb1/2Nb1/2)O3 (PYN) relaxor with high Curie temperature (T C ~300°C) was incorporated into PbZrO3-PbTiO3 (PZ-PT) ceramics to form 0.1PYN-(1-x)PZ-xPT ternary ceramics, and their phase compositions were systematically investigated, providing the more detailed phase diagrams, dielectric, piezoelectric, and ferroelectric properties. Excellent piezoelectric performance (d 33 ~ 450 pC/N, d 33 ⁎ ~714pm/V), with high coercive field (E C ~17.5kV/cm) and T C (~398°C) were simultaneously achieved in the 0.1PYN-0.41PZ-0.49PT composition near the morphotropic phase boundary (MPB). The value of d 33×E C, which exhibits higher than commercial PZT ceramics, indicates its suitability for high-field excitation devices. Additionally, the temperature stability of the resonant frequency (f r) is qualitatively studied by analyzing the main factors influencing f r from a theoretical perspective. Superior stability is achieved in the 0.1PYN-0.38PZ-0.52PT composition (T C ~ 405°C) with tetragonal phase, and the temperature coefficient of resonant frequency (Δf r /f r 25°C) remains within 0.5% up to 300°C, far outperformance than previous reports.
materials science, ceramics