Abstract:This study investigated the effect of shear span-to-depth (a/d) ratio on the mechanical behavior of composite sandwich beams, composed of glass fiber reinforced polymer (GFRP) skins, balsa wood core, and GFRP ribs. Three-point bending tests were carried out on fifteen specimens to verify the effects of the a/d ratio, varying from 1 to 6, and GFRP ribs on the deflections, failure load, and failure modes of sandwich beams. Test results indicated that the a/d ratio plays a major role in beam deflections, which decreased 74-1418% as the a/d ratio varying from 1 to 6. All beams exhibited deflections at failure of span/124 to span/35. Specimens failed in balsa wood core shear failure while a/d < 4, whereas it failed in top skin compression failure when a/d ratio equal to 6. Increasing the GFRP ribs thickness from zero to 2.4 mm, the failure load of sandwich beams increased by 23-75%. Moreover, the ultimate moment increased by 70-323% as the a/d ratio increases from 1 to 6. In addition, for specimens with a/d equal to 4, the failure load and stiffness of sandwich structures with balsa wood core was 79-209% and 90-246% higher than those of specimens with different densities of light-weight foam core. A simplified analytical model accounting for the influence of GFRP ribs on stiffness and strength of the sandwich beam was developed and validated against experimental results. Analysis shows that flexure became more dominant as the a/d ratio increases. The shear deformation contribution of the balsa wood core is over 50% in beams with a/d < 3, while the value is only 20% for beams with a/d equal to 6. The proposed analytical model which accounts for the combined effect of the GFRP ribs agrees well with the experimental results.

Experimental Study on Composite Sandwich Beams with Longitudinal GFRP Webs

Flexural Performance of Sandwich Beams with Lattice Ribs and a Functionally Multilayered Foam Core

An Experimental Investigation of Static and Fatigue Behaviour of GFRP Sandwich Beams with a Web Reinforced Wood Core

Mechanical Performance of Foam-Filled Lattice Composite Panels in Four-Point Bending: Experimental Investigation and Analytical Modeling

Bending Performance of GFRP-wood Sandwich Beams with Lattice-Web Reinforcement in Flatwise and Sidewise Directions

Flexural Behavior of Composite Sandwich Beams with Different Kinds of GFRP Ribs in Flatwise and Edgewise Positions

Behavior of sandwich wall panels with GFRP face sheets and a foam-GFRP web core loaded under four-point bending

Flexural responses and pseudo-ductile performance of lattice-web reinforced GFRP-wood sandwich beams

Fatigue performance of foam-filled sandwich composite beams with web enhanced

EXPERIMENTAL INVESTIGATION ON FLEXURAL BEHAVIOR OF REINFORCED FOAM SANDWICH BEAMS WITH TWO-WAY LATTICE-WEB

Mechanical Performance of GFRP-profiled Steel Sheeting Composite Sandwich Beams in Four-Point Bending

Experimental Study on Sandwich Bridge Decks with GFRP Face Sheets and a Foam-Web Core Loaded under Two-Way Bending

Experimental Study on the Flexure Property of Bamboo-Wood-gfrp Sandwich Beams

Experimental research on flexural fatigue behavior of GFRP-Balsa sandwich beams

Effect of Shear Span-to-depth Ratio on the Mechanical Behavior of Composite Sandwich Beams with GFRP Ribs and Balsa Wood Core Materials

Effect of sustaining load level on flexural behavior of RC beams retrofitted with CFRP sheets

Flexural Behavior of Hybrid Composite Beams with a Bamboo Layer and Lattice Ribs

Flexural Fatigue Behavior and Life Prediction of Web Reinforced GFRP-balsa Sandwich Beams

Experimental and Theoretical Study of Sandwich Panels with Steel Facesheets and Gfrp Core

The Flexural Behaviour of Composite Sandwich Beams with a Lattice-Web Reinforced Wood Core

Structural behavior of load-bearing sandwich wall panels with GFRP skin and a foam-web core