Abstract:The precipitates in a Mg-7Gd-5Y-1Nd-0.5Zr alloy aged to peak-ageing plateau (aged at 210 degrees C from 18 h to 180 h) were studied using transmission electron microscopy (TEM), high-resolution TEM (HRTEM) and high-angle annular detector dark-field scanning transmission electron microscopy (HAADF-STEM). Precipitation at the peak-ageing plateau involves the formation of the beta' phase and a new type of plate-shaped phase precipitated along the (0 0 0 1)(alpha) habit plane. The ellipsoid morphology of beta' was illustrated according to [0 0 0 1](alpha) and [1 0 (1) over bar 0](alpha) zone axes observations. The orientation relationship between the beta' precipitates and matrix satisfies [0 0 1](beta')//[0 0 0 1](alpha) and (1 0 0)(beta')//(1 1 (2) over bar 0)(alpha), respectively. The TEM and HRTEM results indicate that the beta' precipitates have a base-centred orthorhombic structure with lattice parameters a = 0.64 nm, b = 2.22 nm and c = 0.52 nm. Further, atomic-scaled HAADF-STEM observations suggest a Mg7RE-type and not a Mg15RE-type structure for the beta' phase. The positive thermal stability of the alloy at 210 degrees C ageing is attributed to the coherent relationship with the matrix and the formation of an interlaced network of the beta' precipitates. Aside from the beta' phase, a large amount of precipitate particles were observed to form on the (0 0 0 1)(alpha) habit plane in the peak-aged samples. The new type of precipitates have a plate shape, of approximately 5 nm wide along the [1 0 (1) over bar 0](alpha) direction of the matrix and approximately 5 nm long along the [(2) over bar 1 1 0](alpha) direction. A completely coherent relationship with the matrix can also be observed. (c) 2013 Elsevier B.V. All rights reserved.

Co-precipitation on the Basal and Prismatic Planes in Mg–Gd–Ag–Zr Alloy Subjected to Over-Ageing

Precipitation Microstructure and Age-Hardening Response of an Mg–Gd–Nd–Zn–Zr Alloy

A Detailed HAADF-STEM Study of Precipitate Evolution in Mg–Gd Alloy

Precipitation hardening of an Mg–5Zn–2Gd–0.4Zr (wt. %) alloy

Precipitation in A Ag-Containing Mg-Y-Zn Alloy

Effect of Ageing Treatment on the Precipitation Behaviour of Mg–Gd–Y–Zn–Zr Alloy

On the Strengthening Precipitate Structures in Mg-Gd-Ag Alloy: an Atomic-Resolution Investigation Using Cs-corrected STEM

On the role of Ag in enhanced age hardening kinetics of Mg–Gd–Ag–Zr alloys

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Precipitation Behavior of Mg-7Gd-3Y-2Zn-0.5Zr Alloy during Isothermal Aging

Precipitation and Its Effect on Age-Hardening Behavior of As-Cast Mg–Gd–Y Alloy

Precipitation Processes During the Peak-Aged and Over-Aged Stages in an Mg-Gd-Y-Zr Alloy

Enhanced Precipitation-Hardening in Mg–Gd Alloys Containing Ag and Zn

Characterization and Strengthening Effect of Precipitate Microstructure in Mg-3nd-3gd-0.2zn-0.5zr Alloy Aged at 225 °C

Characterisation of Precipitates in a Mg–7Gd–5Y–1Nd–0.5Zr Alloy Aged to Peak-Ageing Plateau

Solute Segregation and Precipitation in a Creep-Resistant Mg–Gd–Zn Alloy

Precipitate Evolution in Mg−7Gd−3Y−1Nd−1Zn−0.5Zr Alloy During Isothermal Ageing at 240 °C

Precipitation and its effect on the mechanical properties of a cast Mg–Gd–Nd–Zr alloy

Precipitation Process in a Mg–Gd–Y Alloy Grain-Refined by Al Addition

On the Precipitation in an Ag-Containing Mg-Gd-Zr Alloy

Age-hardening Behavior and Precipitates of As-Cast Mg-3Zn-1.5Cu-0.6Zr Mg Alloy