Crystal growth and characterization of a mixed laser crystal: Nd-doped Gd0.89La0.1NbO4

Shoujun Ding,Qingli Zhang,Wenpeng Liu,Jianqiao Luo,Fang Peng,Xiaofei Wang,Guihua Sun,Dunlu Sun

DOI: https://doi.org/10.1039/c7ra05380k

IF: 4.036

2017-01-01

RSC Advances

Abstract:A Nd:GdLaNbO4 crystal was grown successfully by the Czochralski method and a CW laser was realized with a slope efficiency of 34.2%.

What problem does this paper attempt to address?

Crystal growth and characterization of a mixed laser crystal: Nd-doped Gd0.89La0.1NbO4

Shoujun Ding,Qingli Zhang,Wenpeng Liu,Jianqiao Luo,Fang Peng,Xiaofei Wang,Guihua Sun,Dunlu Sun

DOI: https://doi.org/10.1039/c7ra05380k

IF: 4.036

2017-01-01

RSC Advances

Abstract:Herein, a Nd-doped GdLaNbO4 (Nd: GLNO) single crystal has been grown successfully using the Czochralski method. The segregation coefficient of Nd3+ ions in the Nd: GLNO crystal is measured to be 0.71. The X-ray power diffraction patterns of the Nd: GLNO crystal confirm that the as-grown crystal has the same crystal structure as pure GdNbO4. The structural parameters of the as-grown crystal are obtained via an X-ray Rietveld refinement method. The absorption spectrum, fluorescence spectrum, and fluorescence decay curve of Nd: GLNO were obtained at room temperature. The small emission cross-section at 1065 nm and long fluorescence lifetime of Nd3+ ions (176.4 mu s) indicate that the Nd: GLNO crystal is suitable for generating an ultrashort pulse laser. A maximum continuous wave (CW) laser output power of 957 mW is achieved at 1.06 mm, corresponding to an optical-to-optical conversion efficiency of 30.3% and slope efficiency of 34.2%. All the obtained results imply that this crystal is a novel mixed niobate-based laser host suitable for laser diode pumps.
Crystal Growth, Spectral Properties and Continuous Wave Laser Operation of New Mixed Nd:GdYNbO4 Laser Crystal

Shoujun Ding,Qingli Zhang,Fang Peng,Wenpeng Liu,Jianqiao Luo,Renqin Dou,Guihua Sun,Xiaofei Wang,Dunlu Sun

DOI: https://doi.org/10.1016/j.jallcom.2016.12.263

IF: 6.2

2016-01-01

Journal of Alloys and Compounds

Abstract:A new mixed laser crystal Nd:Gd0.69Y0.3NbO4 (Nd:GYNO) with high quality was grown successfully by Czochralski method. Its structure parameters are obtained by the X-ray Rietveld refinement method. The effective segregation coefficient of Nd3+ ions is 0.61 in GYNO host. The maximum absorption cross section at 809 nm and peak emission cross section at 1065.6 nm of Nd: GYNO crystal are 11.6 x 10(-20) and 20.5 x 10(-20) cm(2), respectively. The fluorescence lifetime of F-4(3/2) manifold for Nd3+ in Nd:GYNO crystal is fitted to be 156 mu s. Diode-pumped continuous-wave laser operations at 1.06 mu m with Nd: GYNO crystals cut perpendicular to crystallographic a, b, and c axes (denoted as a-, b-c-cut, respectively) were demonstrated. A maximum output power of 0.98 W was obtained with c-cut crystal, corresponding to an optical-to-optical conversion efficiency of 31.3% and a slope efficiency of 30.4%. All these results imply that the Nd: GYNO crystal has great potential application in low and even moderate lasers. (C) 2016 Elsevier B.V. All rights reserved.
Crystal Growth, Defects, and Mechanical and Spectral Properties of a Novel Mixed Laser Crystal Nd:GdYNbO4

Shoujun Ding,Wenpeng Liu,Qingli Zhang,Fang Peng,Jianqiao Luo,Renqin Dou,Guihua Sun,Dunlu Sun

DOI: https://doi.org/10.1007/s00339-016-0672-9

2016-01-01

Applied Physics A

Abstract:A mixed laser crystal of Nd-doped GYNO crystal was grown successfully by Czochralski method. The crystal belongs to monoclinic system with space group I2/a, the structural parameters are obtained by the X-ray Rietveld refinement method. The defects and dislocations along three crystallographic orientations were studied by using the chemical etching method with the phosphoric acid etchant. The mechanical properties (including hardness, yield strength, fracture toughness, and brittle index) of the crystal were estimated by Vickers hardness test. The transmission spectrum was measured at room temperature, and the absorption peaks were assigned. Spectral properties of the as-grown crystal were investigated by Judd–Ofelt theory, and the Judd–Ofelt intense parameters Ω2,4,6 were obtained to be 9.674 × 10−20, 2.092 × 10−20, and 4.061 × 10−20 cm2, respectively.
Crystal Growth, Structure, Defects, Mechanical and Spectral Properties of Nd-0.01:Gd0.89La0.1NbO4 Mixed Crystal

Shoujun Ding,Qingli Zhang,Jianqiao Luo,Wenpeng Liu,Wancheng Lu,Jinrui Xu,Guihua Sun,Dunlu Sun

DOI: https://doi.org/10.1007/s00339-017-1227-4

2017-01-01

Abstract:A novel mixed laser crystal of Nd:GdLaNbO4 (Nd:GLNO) was grown successfully by conventional Czochralski method. The unit cell parameters were obtained by Rietveld refinement method. The density of the as-grown crystal was measured by Archimedean buoyancy method and calculated in theory. Absorption spectrum of Nd:GLNO crystal was recorded at room temperature, and 11 absorption peaks were assigned. The defects of Nd:GLNO crystal were revealed by using chemical etching method with phosphoric acid as etchant. The mechanical properties (including hardness, yield strength, elastic stiffness constant, fracture toughness and brittleness index) were systemically estimated based on Vickers hardness test. All these obtained results play a quite important role in further investigation of Nd:GLNO crystal.
Growth, thermal properties, and LD-pumped 1066 nm laser performance of Nd^3+ doped Gd/YTaO_4 mixed single crystal

Fang Peng,Huajun Yang,Qingli Zhang,Jianqiao Luo,Dunlu Sun,Wenpeng Liu,Guihua Sun,Renqin Dou,Xiaofei Wang,Xue Xing

DOI: https://doi.org/10.1364/OME.5.002536

2015-01-01

Optical Materials Express

Abstract:A new laser crystal Nd:Gd0.69Y0.3TaO4 (Nd:GYTO) with high quality was grown by Czochralski method. The physical properties, including temperature dependent density, specific heat, thermal expansion coefficient, and thermal conductivity, were systematically characterized. The maximum absorption cross section at 809 nm and the stimulated emission cross section at 1066.6 nm are 6.886 x 10(-20) cm(2) and 22 x 10(-20) cm(2), respectively. The fluorescence lifetime is measured to be 182.4 mu s. Up to 2.37 W of continuous wave (CW) laser operating at 1066.5 nm has been successfully realized, corresponding to an optical conversion efficiency of 36.5% and a slope efficiency of 38%. Compared with Nd:GdTaO4, Nd:GYTO shows an enhancement of the laser performance. These results demonstrate that Nd:Gd0.69Y0.3TaO4 is a novel laser crystal with low symmetry and has great potential as low to moderate power lasers. (C) 2015 Optical Society of America
Spectroscopic Properties of Nd: Gd0.89La0.1NbO4 Mixed Laser Crystal

Shoujun Ding,Qingli Zhang,Dunlu Sun,Fang Peng,Wenpeng Liu,Jianqiao Luo,Guihua Sun

DOI: https://doi.org/10.1016/j.jlumin.2018.04.042

IF: 3.6

2018-01-01

Journal of Luminescence

Abstract:A Nd-doped niobate mixed laser crystal of Nd-0.01:Gd0.89La0.1NbO4 (Nd:GLNO) has been grown successfully by Czochralski method. The absorption spectrum, fluorescence spectrum and fluorescence decay curve of Nd: GLNO crystal were measured at room temperature. The spectral parameters of Nd:GLNO crystal were obtained based on Judd-Ofelt (J-O) theory calculation. The three intensity parameters Omega(t)(t= 2, 4, 6) were calculated to be 6.61, 1.43 and 3.31x10(-20) cm(2), respectively. On the base of the Ot calculation, the branching ratios, spontaneous radiative probabilities, radiative lifetime and fluorescence quantum efficiency of the F-4(3/2) level have been evaluated. Compared with other Nd-doped niobate laser crystal, Nd:GLNO shows a special spectral properties due to the large structure disorder caused by La3+. All the results demonstrate that this crystal is a specific low symmetrical laser material different from other niobates family crystals such as Nd:GdNbO4 (Nd:GNO) and Nd:YNbO4 (Nd:YNO) and can be considered as a promising laser material suitable for laser diode pumping.
Basic Properties of a New Nd-doped Laser Crystal: Nd:GdNbO4

Shoujun DING,Qingli ZHANG,Wenpeng LIU,Jianqiao LUO,Dunlu SUN

DOI: https://doi.org/10.1007/s12200-017-0715-7

2017-01-01

Frontiers of Optoelectronics

Abstract:A Nd-doped GdNbO4 single crystals have been grown successfully using the Czochralski technique. The chemical etching method was employed to study the defects in the structural morphology of Nd:GdNbO4 crystal with phosphoric acid etchant. Mechanical properties (such as hardness, yield strength, fracture toughness, and brittle index) of the as-grown crystal were systematically estimated on the basis of the Vickers hardness test for the first time. The transmission spectrum of Nd:GdNbO4 was measured in the wavelength range of 320–2400 nm at room temperature, and the absorption peaks were assigned. Results hold great significance for further research on Nd:GdNbO4.
Thermal, defects, mechanical and spectral properties of Nd-doped GdNbO 4 laser crystal

Shoujun Ding,Qingli Zhang,Jianqiao Luo,Wenpeng Liu,Xiaofei Wang,Guihua Sun,Xiuli Li,Dunlu Sun

DOI: https://doi.org/10.1007/s00339-017-0928-z

2017-01-01

Applied Physics A

Abstract:A Nd-doped GdNbO 4 crystal was grown successfully by Czochralski method. Its monoclinic structure was determined by X-ray diffraction; the unit-cell parameters are a = 5.38 Å, b = 11.09 Å, c = 5.11 Å, and β = 94.56°. The morphological defects of Nd:GdNbO 4 crystal were investigated using the chemical etching with the phosphoric acid etchant. For a new crystal, the physical properties are of great importance. The hardness and density of Nd:GdNbO 4 were investigated first. Thermal properties of Nd:GdNbO 4 , including thermal expansion coefficient and specific heat, were measured along a-, b- , and c -crystalline axes. Thermal properties indicate that the Nd:GdNbO 4 pumped along c -axis can reduce the thermal lensing effect effectively. The specific heat is 0.53 J g −1 K −1 at 300 K, indicating a relatively high damage threshold of Nd:GdNbO 4 . The transmission and emission spectrum of Nd:GdNbO 4 were measured, and the absorption peaks were assigned. The strongest emission peak of Nd:GdNbO 4 is located at 1065.3 nm in the spectral range of 850–1420 nm excited by 808 nm laser. The refractive index of Nd:GdNbO 4 was calculated with the transmission spectrum and fitted with Sellmeier equation. All these obtained results is of great significance for the further research of Nd:GdNbO 4 .
Basic Properties of A New Nd-Doped Laser Crystal: Nd: Gdnbo4

Shoujun Ding,Qingli Zhang,Wenpeng Liu,Jianqiao Luo,Dunlu Sun

DOI: https://doi.org/10.1007/s12200-017-0715-7

2017-01-01

Frontiers of Optoelectronics

Abstract:A Nd-doped GdNbO4 single crystals have been grown successfully using the Czochralski technique. The chemical etching method was employed to study the defects in the structural morphology of Nd:GdNbO4 crystal with phosphoric acid etchant. Mechanical properties (such as hardness, yield strength, fracture toughness, and brittle index) of the as-grown crystal were systematically estimated on the basis of the Vickers hardness test for the first time. The transmission spectrum of Nd:GdNbO4 was measured in the wavelength range of 320–2400 nm at room temperature, and the absorption peaks were assigned. Results hold great significance for further research on Nd:GdNbO4.
Growth and Characterization of Niobate Laser Crystals

Shoujun Ding,Qingli Zhang,Wenpeng Liu,Jianqiao Luo,Dunlu Sun

DOI: https://doi.org/10.1364/fio.2017.jtu3a.3

2017-01-01

Abstract:In this work, the growth and characterization of a series of Nd-doped niobate laser crystals have been reviewed, including Nd:YNbO4, Nd:GdNbO4 and Nd:GdYNbO4. The excellent laser properties make them to be used in many fields.
Growth, Spectral Properties and LD Pumped Laser Performances of Cr,Nd:GSAG Crystal

Jin-rui XU,Qing-li ZHANG,Fang PENG,Xiao-fei WANG,Ren-qin DOU,Jian-qiao LUO,Gui-hua SUN,Shou-jun DING,Dun-lu SUN

DOI: https://doi.org/10.3969/j.issn.1000-985X.2017.09.001

2017-01-01

Abstract:Cr,Nd:GSAG is one type of laser crystal with high performances , but there are few research on its lasing properties by LD pumping .In this work, a Cr,Nd:GSAG crystal was grown by Czochralaki method , its chemical composition , structure and lasing performances were investigated .By measuring the X-ray rocking curve of (111) crystallographic plane of Cr ,Nd:GSAG crystal, the full at half maximum ( FWHM) of the diffraction peak is 0.055°.Its atomic structural parameters and temperature factors were obtained by Rietveld refinement to X-ray diffraction data .The strongest absorption peak of Cr ,Nd:GSAG crystal locates at 808.6 nm and the absorption cross section is 3.38 ×10 -20 cm2 .The strongest emission peak of Cr ,Nd:GSAG crystal under 808 nm excitation locates at 1060 nm and the stimulated emission cross section is 6.04 ×10 -20 cm2 .The fluorescence lifetime of laser upper level 4 F3/2 was measured to be 274 μs.A 1060 nm laser output was achieved by 808 nm LD pumping in the continuous-wave mode .The maximum output power of 0.513 W is obtained with an incident pump power of 8.88 W, corresponding to a slope efficiency of 6.73% and an optical-to-optical conversion efficiency of 5.78%.Besides, energy transfer mechanism between Cr 3+and Nd3+in Cr,Nd:GSAG crystal was discussed .
A Optimized Diode-Pumped Continuous-Wave Laser with Novel Nd:GdLaNbO4 Mixed Crystal

Haiyue Sun,Yufei Ma,Shoujun Ding,Zhenfang Peng,Fang Peng,Qingli Zhang

DOI: https://doi.org/10.1016/j.ijleo.2018.10.176

IF: 3.1

2018-01-01

Optik

Abstract:A diode-pumped continuous-wave (CW) laser with a novel Nd:GdLaNbO4 mixed crystal at 1065 nm was demonstrated. The influence of various parameters on CW output performance was investigated theoretically and experimentally, including the transmission of output mirror, the resonance length and the focusing radius of pump light. When the resonator length was 40 mm and the focusing radius of pump light was 256 μm, the maximum output power of 3.06 W was obtained with optimum output mirror transmission of 20% at absorbed pump power of 12.24 W. The corresponding slope efficiency was 29.1%.
Growth and Characterization of Nd-doped Disordered Ca3Gd2(BO3)4 Crystal

Z. B. Pan,H. J. Zhang,H. H. Yu,M. Xu,Y. Y. Zhang,S. Q. Sun,J. Y. Wang,Q. Wang,Z. Y. Wei,Z. G. Zhang

DOI: https://doi.org/10.1007/s00340-011-4737-3

2011-01-01

Abstract:A high-quality disordered Nd3+:Ca3Gd2(BO3)4 (Nd3+:CGB) laser crystal was grown by the Czochralski method. The space group and effective segregation coefficient of Nd3+ were determined to be Pnma and 1.06, respectively. The thermal properties, including the average linear thermal expansion coefficient, thermal diffusivity, specific heat, and thermal conductivity were systematically measured for the first time. It was found that the thermal conductivity increases with increasing temperature, indicating glasslike behavior. The polarized spectral properties of the crystal were investigated, including the polarized absorption spectra, polarized fluorescence spectra, and fluorescence decay. The spectroscopic parameters of Nd3+ ions in Nd3+:CGB crystal have been obtained based on Judd–Ofelt theory. The anisotropy of the spectral properties for different polarized directions was discussed. Additionally, the continuous-wave (CW) laser performance at 1.06 μm was demonstrated for the first time. The maximum output power of 603 mW was achieved with corresponding optical conversion efficiency of 8.33% and slope efficiency of 9.95%.
Growth, Structure, and Spectroscopic Properties of a Disordered Nd:SrLaGaO4 Laser Crystal

Shanshan Fang,Ling Liang,Wei Wang,Yiyang Lin,Yijian Sun,Guoliang Gong,Chaoyang Tu,Herui Wen

DOI: https://doi.org/10.3390/cryst14020174

IF: 2.7

2024-02-09

Crystals

Abstract:A disordered Nd:SrLaGaO4 (Nd:SLG) laser crystal was successfully grown via the Czochralski (CZ) technique. The crystal structure, refractive index, polarized absorption spectra, and stimulated emission spectra were measured. The spectroscopic properties were studied intensively with the Judd–Ofelt (J-O) theory. The maximum absorption cross sections of π- and σ-polarization at 806 nm were calculated to be 3.73 × 10−20 and 4.05 × 10−20 cm2, corresponding to FWHMs of 6.00 and 6.10 nm, respectively. The maximum emission cross sections of π- and σ-polarization at 1076 nm were 3.97 × 10−20 and 4.12 × 10−20 cm2, with FWHMs of 30.21 and 19.44 nm, respectively. The decay life of the Nd3+:4F3/2 energy level was fitted to be 0.152 ms, and the fluorescence quantum efficiency was 72.72%. The inhomogeneous broadening in spectra benefiting from the disordered structure indicates the Nd:SLG crystal is a promising gain medium for ultrafast laser and tunable laser generations in the near infrared region.

materials science, multidisciplinary,crystallography
Growth, Nonlinear Optical and Self-Frequency-Doubled Properties of Lagdcob and Nd:Lagdcob Single Crystals

Yanqing Liu,Fapeng Yu,Zhengping Wang,Xinguang Xu,Xian Zhao

DOI: https://doi.org/10.1016/j.jallcom.2015.05.165

IF: 6.2

2015-01-01

Journal of Alloys and Compounds

Abstract:High optical quality La0.09Gd0.91Ca4O(BO3)(3) and Nd0.03La0.08Gd0.89Ca4O(BO3)(3) crystals, grown by Czo-chralski (Cz) pulling method, were investigated for their nonlinear optical (NLO) and laser properties. These crystals were found to possess moderate birefringence (0.0320 at 1064 nm), wide transparency (320-2300 nm) and large effective nonlinear effects (d(eff) similar to 1.2 pm/V), which were suitable for green laser generation. The second-harmonic-generation (SHG) phase matching (PM) properties, including PM curve, deff, angular acceptance and walk-off angle were investigated. Both of the calculations and experiments have indicated that the 1064 nm optimum PM direction which has maximum d(eff) (similar to 1.2 pm/V) and SHG conversion efficiency (57.1%) locate in the second octant, i.e. (113.5 degrees, 48.6 degrees). Pumped by the 0.8 mu m AlGaAs laser diodes (LD), the self-frequency-doubling (SFD) performance of Nd0.03La0.08Gd0.89Ca4O(BO3)(3) crystal was evaluated, where as much as 115 mWgreen light at 546 nm was obtained with a (113 degrees, 48.9 degrees)-cut, 6 mm long and uncoated Nd0.03La0.08Gd0.89Ca4O(BO3)(3) sample. (C) 2015 Elsevier B.V. All rights reserved.
Growth, Spectral Properties, and Diode-Pumped Laser Operation of a Nd3+-doped LaMgAl11O19 Crystal.

Yuxin Pan,Shidong Zhou,Jiawei Wang,Bin Xu,Jian Liu,Qingsong Song,Jie Xu,Dongzhen Li,Peng Liu,Xiaodong Xu,Jun Xu

DOI: https://doi.org/10.1364/ao.57.009657

IF: 1.9

2018-01-01

Applied Optics

Abstract:A Nd3+-doped LaMgAl11O19 (Nd:LMA) crystal was grown by the Czochralski method. Room temperature polarized absorption spectra, fluorescence spectra, and fluorescence lifetime of the Nd:LMA crystal were measured and analyzed. The Judd-Ofelt parameters Ω2,4,6 were calculated to be 1.21×10-20, 3.63×10-20, and 2.35×10-20 cm2, respectively. The absorption and emission cross sections were calculated. Using a 790-nm diode laser as pump source, continuous-wave laser operation of an a-cut Nd:LMA crystal has been demonstrated with a maximum output power of 1.71 W and slope efficiency of 40.4% for a 1055 nm laser. Low-gain laser operation at 1082 nm is also realized with a maximum output power of 1.46 W and slope efficiency of 34.5%.
Study on the growth and Raman spectra of the Nd:Gd2Ga5O12 crystal

Dunlu Sun,Qingli Zhang,Xia Zhang,ShuFang Shao,ChangJiang Gu,Aihua Wang,Haihe Jiang,Shaotang Yin

2007-01-01

Abstract:The Nd-GGG crystal was grown successfully by the Czochralski method, and its structure was studied by laser Micro-Raman spectra. The Raman peaks and fluorescence peaks were discerned by using two excitation wavelengths (Ar+ 325 nm and 514.5 nm), the appeared fluorescence peaks were analyzed the tetrahedral, octahedral and dodecahedral structure of Nd:GGG crystal were contacted with the Raman peaks, and the vibration modes were also recognized. The obtained results are helpful to research the structure of solid-liquid boundary layer during the Nd:GGG growth and the change rule of the growth unit in the boundary layer.
Growth and Self-Frequency Doubling Laser Output of Nd : Ca4Gd0.275Y0.725O(BO3)3 Crystal

HJ Zhang,XL Meng,CQ Wang,L Zhu,XS Liu,CM Dong,RP Cheng,XM Liu,RH Wang,SJ Zhang,YT Chow,LK Sun

DOI: https://doi.org/10.1016/s0022-0248(99)00882-9

IF: 1.8

2000-01-01

Journal of Crystal Growth

Abstract:In this letter, Nd:Ca4Gd0.275Y0.725O(BO3)3 (Nd:GdYCOB) single crystal with good optical quality and large size has been grown by the Czochralski method. The absorption and fluorescence spectra have been measured. The self-frequency doubling (SFD) laser output of Nd:GdYCOB at 0.53μm has been demonstrated when a Nd:GdYCOB crystal sample with dimensions of 3mm×3mm×7mm (the phase-matched angle is θ=78.8°, Φ=90°) is pumped by a cw Ti:sapphire laser.
Diode-pumped Continuous-Wave and Passively Q-switched Nd: GdLaNbO4 Laser

Shanchun Zhang,Yufei Ma,Xiaoxu Liu,Shoujun Ding,Xin Yu,Qingli Zhang

DOI: https://doi.org/10.1364/ome.8.000983

2018-01-01

Optical Materials Express

Abstract:A diode-pumped passively Q-switched 1065 nm laser with a novel Nd:Gd0.89La0.1NbO4 mixed crystal was demonstrated for the first time to the best of our knowledge. First, the crystal characteristics were investigated. In the continuous-wave (CW) operation, when the absorbed pump power was 12.24 W, the maximum CW output power of 3.06 W was obtained with the optimum transmission (20%) of the output plane coupler. In the passively Q-switched situation, when Cr4+:YAG crystal with an initial transmission of 90% served as the Q-switched saturable absorber, the maximum repetition rate, pulse peak power and minimum pulse width were 24.5 kHz, 1.13 kW and 32 ns, respectively, at the absorbed pump power of 12.24 W. (C) 2018 Optical Society of America under the terms of the OSA Open Access Publishing Agreement.
Growth, Characterization, and Efficient Continuous-Wave Laser Operation in Nd,Gd:CaF 2 Single-Crystal Fibers

Zhonghan Zhang,Shaozhao Wang,Xiaoyue Feng,Qinghui Wu,Xiaobo Qian,Anhua Wu,Jie Liu,Bingchu Mei,Liangbi Su

DOI: https://doi.org/10.1021/acs.cgd.0c00024

2020-08-31

Abstract:Nd,Gd:CaF2 single-crystal fibers (SCFs) of various Nd3+ and Gd3+ concentrations were grown by a modified temperature gradient technique (TGT) using a home-designed multi-microchannel crucible. Powder and Laue X-ray diffraction measurements indicated the SCFs consist of pure monocrystalline CaF2 phase. Distributions of rare earth dopants in SCFs are proven to be uniform by both EDS and spectroscopic measurements. Laser diode (LD) pumped continuous-wave (CW) laser output at ∼1.06 μm spectral region of a highest slope efficiency of 42% and a maximum output power of 1.49 W were achieved. Comparison of laser performances between Nd,Gd:CaF2 SCFs and bulk crystal was analyzed, indicating the potential of fluoride SCFs in high-power laser applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.cgd.0c00024?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.cgd.0c00024</a>.Details of multi-microchannel graphite crucible used in the growth of Nd,Gd:CaF2 SCFs, raw spectroscopic data of absorption measurements to determine the axial distribution of Nd3+, an example of data treatment of absorption spectra for analysis of Nd3+ distribution, measured or calculated data from absorption spectra of Nd3+ in samples fabricated from a Nd,Gd:CaF2 SCF (<a class="ext-link" href="/doi/suppl/10.1021/acs.cgd.0c00024/suppl_file/cg0c00024_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, multidisciplinary,materials science,crystallography

Crystal growth and characterization of a mixed laser crystal: Nd-doped Gd<sub>0.89</sub>La<sub>0.1</sub>NbO<sub>4</sub>

Crystal growth and characterization of a mixed laser crystal: Nd-doped Gd0.89La0.1NbO4

Crystal Growth, Spectral Properties and Continuous Wave Laser Operation of New Mixed Nd:GdYNbO4 Laser Crystal

Crystal Growth, Defects, and Mechanical and Spectral Properties of a Novel Mixed Laser Crystal Nd:GdYNbO4

Crystal Growth, Structure, Defects, Mechanical and Spectral Properties of Nd-0.01:Gd0.89La0.1NbO4 Mixed Crystal

Growth, thermal properties, and LD-pumped 1066 nm laser performance of Nd^3+ doped Gd/YTaO_4 mixed single crystal

Spectroscopic Properties of Nd: Gd0.89La0.1NbO4 Mixed Laser Crystal

Basic Properties of a New Nd-doped Laser Crystal: Nd:GdNbO4

Thermal, defects, mechanical and spectral properties of Nd-doped GdNbO 4 laser crystal

Basic Properties of A New Nd-Doped Laser Crystal: Nd: Gdnbo4

Growth and Characterization of Niobate Laser Crystals

Growth, Spectral Properties and LD Pumped Laser Performances of Cr,Nd:GSAG Crystal

A Optimized Diode-Pumped Continuous-Wave Laser with Novel Nd:GdLaNbO4 Mixed Crystal

Growth and Characterization of Nd-doped Disordered Ca3Gd2(BO3)4 Crystal

Growth, Structure, and Spectroscopic Properties of a Disordered Nd:SrLaGaO4 Laser Crystal

Growth, Nonlinear Optical and Self-Frequency-Doubled Properties of Lagdcob and Nd:Lagdcob Single Crystals

Growth, Spectral Properties, and Diode-Pumped Laser Operation of a Nd3+-doped LaMgAl11O19 Crystal.

Study on the growth and Raman spectra of the Nd:Gd2Ga5O12 crystal

Growth and Self-Frequency Doubling Laser Output of Nd : Ca4Gd0.275Y0.725O(BO3)3 Crystal

Diode-pumped Continuous-Wave and Passively Q-switched Nd: GdLaNbO4 Laser

Growth, Characterization, and Efficient Continuous-Wave Laser Operation in Nd,Gd:CaF 2 Single-Crystal Fibers