Abstract:This study focused on the numerical simulation of the distribution of residual stress in yttria-stabilized zirconia (YSZ) coatings prepared with atmospheric plasma spraying (APS). We particularly investigated the stress distribution around the interface between the top coat and bond coat. During thermal spray deposition, droplets and particles deposit on the substrate in a complex manner, causing interface waviness and non-uniform stress distribution. Therefore, residual stress is an important consideration when preparing thermal barrier coatings (TBCs). Residual stresses directly affect the performance of bond coats (BCs) and ceramic top coats (TCs). To accurately evaluate residual stress, we considered interface waviness and the thickness of the ceramic top coat and conducted a detailed analysis of stress distribution. The results show that compressive stress exists at the TC/BC interface, which may be caused by the mismatch in the thermal expansion coefficient between the YSZ top coat and the substrate, potentially leading to coating delamination. Moreover, the residual stress at the TC/BC interface significantly increases with an increasing YSZ thickness. When the top-coat thickness exceeds 300 μm, stress concentration and failure of the coating are likely to occur. Meanwhile, the optimized thermal spray experiment results confirm that the residual stress at the BC/YSZ interface of the thermal barrier coating is tensile stress, with a maximum value of 155 MPa, which is consistent with the finite element calculation results. Furthermore, the failure modes of TBCs with rough interface conditions are discussed in detail. Our research provides important guidance for TBC design and optimizing their performance.

OS0805 Effect of Residual Stress on Nonlinear Response of Plasma-Sprayed Thermal Barrier Coatings

Effects of Residual Stress on the Mechanical Properties of Plasma-Sprayed Thermal Barrier Coatings

Experimental Investigation of Residual Thermal Stress in Thermal Barrier Coating (Tbc)

OS13F106 Progress of the Residual Stress Measuring Techniques of Thermal Barrier Coatings

Microstructure and Surface Residual Stress of Plasma Sprayed Nanostructured and Conventional ZrO2‐8wt%Y2O3 Thermal Barrier Coatings

Effect of Top-Coat Thickness and Interface Fluctuation on the Residual Stress in APS-TBCs

Simulation of Residual Stresses and Their Effects on Thermal Barrier Coating Systems Using Finite Element Method

Numerical and Experimental Investigation of Residual Stress in Thermal Barrier Coatings During Aps Process

Experimental and Simulation Analysis of the Evolution of Residual Stress Due to Expansion Via CMAS Infiltration in Thermal Barrier Coatings

Stress States in Plasma-Sprayed Thermal Barrier Coatings Upon Temperature Cycling: Combined Effects of Creep, Plastic Deformation, and TGO Growth

Relationship Between Lamellar Structure and Elastic Modulus of Thermally Sprayed Thermal Barrier Coatings with Intra-splat Cracks

Assessment of Stress Characteristic and Interfacial Delamination in Thermal Barrier Coatings Considering the Connected Crack Network

Residual Stress Measurement of Thermal Barrier Coatings

Substrate-constrained Effect on the Stiffening Behavior of Lamellar Thermal Barrier Coatings

Comparative Study of the Residual Stress in Plasma Sprayed Nanostracture and Conventional Structure Coatings

Thermal Stress in Fabrication of Thermal Barrier Coatings

A Theoretical Model for Predicting Residual Stress Generation in Fabrication Process of Double-Ceramic-Layer Thermal Barrier Coating System

Strain/sintering Co-Induced Multiscale Structural Changes in Plasma-Sprayed Thermal Barrier Coatings

Stress States and Crack Behavior in Plasma Sprayed TBCs Based on a Novel Lamellar Structure Model with Real Interface Morphology

Effect of Oxide Growth on the Stress Development in Double-Ceramic-layer Thermal Barrier Coatings