Abstract:Hexagonal NaY0.95Yb0.03Er0.F-02(4) microcrystals with different morphologies were prepared by hydro-thermal synthesis with three controlling methods, including addition of different amount of EDTA, addition of different surfactant including CTAB, P123 and SDBS and using different thermal solvents including water, ethanediol and polyethyleneglycol. The synthesis method can be described as following: trivalent nitrate stock solutions of 1 mol/L with ratio 0.95/0.03/0.02 of Y3+/Yb3+/Er3+ were prepared by dissolving the corresponding metal oxide in concentrated nitric acid at elevated temperatures and label as A. Certain concentration solution of EDTA, P123, CTAB, SDBS, NaF, and NH4HF2 were prepared as candidate. In a typical procedure, a certain amount of EDTA, CTAB, P123, and SDBS were added into 20 mL A sulution. After vigorous stirring for 30 min, certain mol NaF was added drop by drop, the pH value of solution was adjusted to 3.0 by the addition of 1 mol/L HF or NaOH, and then stirring continued for 30 mm. Then the emulsion mixture was moved to Teflon-lined autoclave and incubated in oven at 195 degrees C for 4 h. The products were washed by deionized water and ethanol three times respectively, and then dried in oven at 60 degrees C. Phase structure and crystal morphologies were characterized by XRD (X-ray powder diffraction), SEM (scanning electron microscope) and TEM (transmission electron microscope) methods. Analysis results indicate that the crystal growing direction changed from [001] to [100] and bond distances between F- and Y3+/ Yb3+/Er3+ were enlarged while bond distance between F- and Na+ was reduced with the increasing EDTA amount. The crystal morphology was not changed by adding CTAB surfactant compared with no surfactant adding sample, while microtubes were obtained when P123 was added as surfactant, and micrograins morphology mixed with some smaller hexagonal NaYF4 when SDBS was added as surfactant; crystal sizes and exposure lattice plane were also tuned with different thermal solvents. Crystal growing mechanism of different morphologies was discussed in the manuscripture. Upconversion (UC) luminescence emission spectra and decay time curves of different-morphological samples were obtained using Edinburgh instruments FSLP920 fluorescence spectrophotometer with 980 nm OPTEK OPO LASER excitation. The lifetimes of 521 and 541 nm emission were fitted by single exponential decay function. Luminescence property analysis results show the intensity and lifetime of spectra emission is interrelated with crystal morphology, the emission intensity is enhanced with reducing of the thickness of micrograins, and the intensity of the smallest microstick is the strongest among all the samples. The lifetime fitted results show the decay time constants and rising time constants are different of different-morphological NaY0.95Yb0.03Er0.02F4, indicating that their energy transfer models are different during UC emission. This manuscripture may be helpful for morphology-controllable synthesis of UC materials with super luminescence performance.

Morphology Control and Upconversion Enhancement in NaYF4:Yb3+,Er3+ Crystals Via Ca2+ Ions Doping

Hexagonal NaYF4:Yb3+/Er3+ Nano/micro-Structures: Controlled Hydrothermal Synthesis and Morphology-Dependent Upconversion Luminescence

Controlled Synthesis of Β-Nayf4:Yb3+/er3+ Microstructures with Morphology- and Size-Dependent Upconversion Luminescence

Effect of Ca~(2+) Doping on the Upconversion Luminescence of Hexagonal NaYF_4∶Yb,Er Microcrystals

Crystalline Phase and Morphology Controlling to Enhance the Up-Conversion Emission from NaYF4:Yb,Er Nanocrystals

Controlled Synthesis And Morphology Dependent Upconversion Luminescence Of Nayf4 : Yb, Er Nanocrystals

Morphology control and upconversion luminescence enhancement of Na1-xLixY.78-yLuyF4:Er.02Yb.2 microcrystals by doping ions with different valences

Simultaneous Morphology Control and Upconversion Fluorescence Enhancement of Nayf4:Yb,Er Crystals Through Alkali Ions Doping

Controllable hydrothermal synthesis of NaYbF4 and YbF3 with diverse morphologies and emission enhancement in β-NaYbF4: Er3+ upconversion micro-crystals via solvents codoping and Na+ dosage

Synthesis of Different Morphology Er3+/Yb(3+)Codoped Hexagonal Nayf4 and Upconversion Luminescence Property Investigation

Synthesis of Upconversion β-NaYF₄:Nd 3+ /Yb 3+ /Er 3+ Particles with Enhanced Luminescent Intensity through Control of Morphology and Phase.

Synthesis of NaYF4 Microcrystals with Different Morphologies and Enhanced Up-Conversion Luminescence Properties.

Controlled Growth along Circumferential Edge and Upconverting Luminescence of Β-Nayf4: 20%yb3+, 1%er3+ Microcrystals

Enhanced Upconversion Luminescence and Controllable Phase/shape of NaYF4:Yb/Er Crystals Through Cu2+ Ion Doping

Enhanced upconversion luminescence and controllable phase/shape of NaYF<sub>4</sub>:Yb/Er crystals through Cu<sup>2+</sup> ion doping

Tin-(IV) dopant-controlled synthesis of Yb3+/Er3+:NaGdF4 nanocrystals: Morphology transformation and intensified upconversion performance

Controlled-synthesis and up-conversion luminescence of NaY F4 : Yb, Er phosphors

Effects of Ca2+ Doping on Upconversion Luminescence Intensity and Crystal Field Asymmetry of Β-Nayf4:Yb3+/er3+ Microcrystals

Influence of Cr 3+ ions doping on growth and upconversion luminescence properties of β-NaYF 4 :Yb 3+ /Er 3+ microcrystals

Controllable Synthesis and Upconversion Luminescenceof NaYF4:Yb3+, Er3+ Nanocrystals

Phase transformation and morphology tuning of ?-NaYF4:Yb3+,Er3+ nanocrystals through K+ ions codoping