Abstract:Hexagonal NaY0.95Yb0.03Er0.F-02(4) microcrystals with different morphologies were prepared by hydro-thermal synthesis with three controlling methods, including addition of different amount of EDTA, addition of different surfactant including CTAB, P123 and SDBS and using different thermal solvents including water, ethanediol and polyethyleneglycol. The synthesis method can be described as following: trivalent nitrate stock solutions of 1 mol/L with ratio 0.95/0.03/0.02 of Y3+/Yb3+/Er3+ were prepared by dissolving the corresponding metal oxide in concentrated nitric acid at elevated temperatures and label as A. Certain concentration solution of EDTA, P123, CTAB, SDBS, NaF, and NH4HF2 were prepared as candidate. In a typical procedure, a certain amount of EDTA, CTAB, P123, and SDBS were added into 20 mL A sulution. After vigorous stirring for 30 min, certain mol NaF was added drop by drop, the pH value of solution was adjusted to 3.0 by the addition of 1 mol/L HF or NaOH, and then stirring continued for 30 mm. Then the emulsion mixture was moved to Teflon-lined autoclave and incubated in oven at 195 degrees C for 4 h. The products were washed by deionized water and ethanol three times respectively, and then dried in oven at 60 degrees C. Phase structure and crystal morphologies were characterized by XRD (X-ray powder diffraction), SEM (scanning electron microscope) and TEM (transmission electron microscope) methods. Analysis results indicate that the crystal growing direction changed from [001] to [100] and bond distances between F- and Y3+/ Yb3+/Er3+ were enlarged while bond distance between F- and Na+ was reduced with the increasing EDTA amount. The crystal morphology was not changed by adding CTAB surfactant compared with no surfactant adding sample, while microtubes were obtained when P123 was added as surfactant, and micrograins morphology mixed with some smaller hexagonal NaYF4 when SDBS was added as surfactant; crystal sizes and exposure lattice plane were also tuned with different thermal solvents. Crystal growing mechanism of different morphologies was discussed in the manuscripture. Upconversion (UC) luminescence emission spectra and decay time curves of different-morphological samples were obtained using Edinburgh instruments FSLP920 fluorescence spectrophotometer with 980 nm OPTEK OPO LASER excitation. The lifetimes of 521 and 541 nm emission were fitted by single exponential decay function. Luminescence property analysis results show the intensity and lifetime of spectra emission is interrelated with crystal morphology, the emission intensity is enhanced with reducing of the thickness of micrograins, and the intensity of the smallest microstick is the strongest among all the samples. The lifetime fitted results show the decay time constants and rising time constants are different of different-morphological NaY0.95Yb0.03Er0.02F4, indicating that their energy transfer models are different during UC emission. This manuscripture may be helpful for morphology-controllable synthesis of UC materials with super luminescence performance.

Crystalline Phase and Morphology Controlling to Enhance the Up-Conversion Emission from NaYF4:Yb,Er Nanocrystals

Synthesis, Phase Structure and Up-Conversion Luminescence of Nayf4:Yb3+, Er3+/Tm3+ Nanorods

Na+-Driven Nucleation of NaYF4:Yb,Er Nanocrystals and Effect of Temperature on Their Structural Transformations and Luminescent Properties

Controlled Synthesis And Morphology Dependent Upconversion Luminescence Of Nayf4 : Yb, Er Nanocrystals

Controllable hydrothermal synthesis of NaYbF4 and YbF3 with diverse morphologies and emission enhancement in β-NaYbF4: Er3+ upconversion micro-crystals via solvents codoping and Na+ dosage

Synthesis of Upconversion β-NaYF₄:Nd 3+ /Yb 3+ /Er 3+ Particles with Enhanced Luminescent Intensity through Control of Morphology and Phase.

One-dimensional Hexagonal-Phase NaYF4: Controlled Synthesis, Self-Assembly, and Morphology-Dependent Up-Conversion Luminescence Properties

Morphology Control and Upconversion Enhancement in NaYF4:Yb3+,Er3+ Crystals Via Ca2+ Ions Doping

A Synthesis and Up-Conversional Photoluminescence Study of Hexagonal Phase NaYF4:Yb,Er Nanoparticles

Additives and solvents-induced phase and morphology modification of NaYF 4 for improving up-conversion emission

Surfactant-tuned Phase Crystallinity and Morphologies of NaYF4:Yb3+,Er3+ Hexagonal Microstructures and Their Photoluminescence Properties

NaGdF4∶Yb3+,Ho3+and GdF3∶Yb3+,Ho3+Nanocrystals:Controlled Synthesis and Morphology Dependent Upconversion Luminescence

An Efficient and User-Friendly Method for the Synthesis of Hexagonal-Phase NaYF(4):Yb, Er/Tm Nanocrystals with Controllable Shape and Upconversion Fluorescence.

Phase transformation and morphology tuning of ?-NaYF4:Yb3+,Er3+ nanocrystals through K+ ions codoping

Phase and Morphology Evolution of NaGdF4:Yb,Er Nanocrystals with Power Density-Dependent Upconversion Fluorescence Via One-Step Microwave-Assisted Solvothermal Method

Hexadecylpyridinium Chloride Mediated Hydrothermal Synthesis of NaYF₄:Yb, Er Nanocrystal and Their Luminescent Properties

Synthesis of NaYF4 Microcrystals with Different Morphologies and Enhanced Up-Conversion Luminescence Properties.

Controlled Synthesis and Up-Conversion Emission of Rare-Earth Tri-Doped NaYF4 Nanocrystals under Femtosecond-Laser Excitation.

Synthesis of Different Morphology Er3+/Yb(3+)Codoped Hexagonal Nayf4 and Upconversion Luminescence Property Investigation

Hexagonal NaYF4:Yb3+/Er3+ Nano/micro-Structures: Controlled Hydrothermal Synthesis and Morphology-Dependent Upconversion Luminescence

Composition tuning the upconversion emission in NaYF4:Yb/Tm hexaplate nanocrystals.