Synthesis and luminescence properties of oxyapatite-type ZnLa4(SiO4)3O:Eu3+ phosphor for high CRI w-LEDs, latent fingerprints, and security ink
Jiayun Kong,Haoran Su,Changlin Li,Siyu Cheng,Yu Wang,Yilian Ran,Yuxin Li,Yufan Shang,Shouan Xie,Ruijin Yu
DOI: https://doi.org/10.1016/j.ceramint.2023.09.278
IF: 5.532
2023-09-01
Ceramics International
Abstract:The Eu3+-doped oxyapatite-type ZnLa4(SiO4)3O (ZLSO) phosphors with a strong red emission were successfully synthesized. The pure phase of the phosphors with the hexagonal system was verified through X-ray diffraction. The band gap energy of the ZLSO was calculated using Materials Studio and measured using the diffuse reflection spectra. Attributed to the 7F0→5L6 transition of Eu3+ at 394 nm, the prepared phosphors showed a more intense emission at 614 nm than at 590 nm, due to their asymmetric position. The optimized doping concentration of the ZLSO:xEu3+ sample was 20 mol%, and the relevant mechanism of concentration quenching was dipole-quadrupole interaction. Notably, the ZLSO:Eu3+ phosphors exhibited preferable thermal stability, with an activation energy of 0.289 eV. The fabricated warm white light-emitting diodes (w-LEDs) with ZLSO:Eu3+ phosphors presented a high average colour rendering index (R a = 95, CCT = 5233 K). Meanwhile, the level 1–3 structures of latent fingerprints (LFPs) were distinctly displayed by ZLSO:Eu3+ samples, and security ink was successfully used to encrypt information. In , the highly efficient oxyapatite-type ZLSO:20 mol%Eu3+ phosphors have attractive application potential in multiple application fields, such as w-LEDs, LFPs, and security ink.
materials science, ceramics