Lead-free AgNbO3 anti-ferroelectric ceramics with an enhanced energy storage performance using MnO2 modification

Lei Zhao,Qing Liu,Shujun Zhang,Jing-Feng Li

DOI: https://doi.org/10.1039/c6tc03289c

IF: 6.4

2016-01-01

Journal of Materials Chemistry C

Abstract:Enhanced anti-ferroelectric properties and high recoverable energy densities from 2.5–2.9 J cm−3 were achieved in 0.1 wt% Mn-doped AgNbO3 ceramics over 20–180 °C.

What problem does this paper attempt to address?

Lead-Free Agnbo3 Anti-Ferroelectric Ceramics With An Enhanced Energy Storage Performance Using Mno2 Modification

Lei Zhao,Qing Liu,Shujun Zhang,Jing-Feng Li

DOI: https://doi.org/10.1039/c6tc03289c

IF: 6.4

2016-01-01

Journal of Materials Chemistry C

Abstract:Dielectric ceramic materials have been actively studied for advanced pulsed power capacitor applications. Despite the good properties obtained in lead-based ceramics, lead-free counterparts are highly desired due to environmental regulations. This study revealed the potential of AgNbO3 to be a promising lead-free ceramic for energy storage applications. AgNbO3 ceramics fabricated using a conventional solid-state reaction method under an O-2 atmosphere show a characteristic anti-ferroelectric (AFE) double hysteresis loop at an electric field of 4130 kV cm(-1), with a peak recoverable energy storage density (W-rec) of 1.6 J cm(-3) at 140 kV cm(-1). In addition, the incorporation of MnO2 into AgNbO3 can further increaseWrec, exceeding 2.3 J cm(-3) at 150 kV cm(-1) by the reduction of the remnant polarization, which is due to the enhanced AFE stability induced by the addition of MnO2. Of particular importance is that the 0.1 wt% MnO2-doped AgNbO3 ceramics were found to possess a good thermal stability with Wrec = 2.5-2.9 J cm(-3) over a temperature range of 20-180 8C at 150 kV cm(-1) and 1 Hz.
High energy density in Ag0.5Na0.5(Nb1-xTax)O3 antiferroelectric ceramics

Ye Tian,Lei Li,Yonghao Xu,Ming Ma,Chen Chen,Zixiong Sun,Liaona She,Guanjun Chen,Tong Wang,Wanyin Ge,Xiaoyong Wei,Li Jin

DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.04.049

IF: 5.7

2024-01-01

Journal of the European Ceramic Society

Abstract:There has been significant interest in AgNbO3-based antiferroelectric ceramics, recently, due to their ability to achieve high energy storage density (Wrec). However, fabricating their commercial products faces challenges due to chemically unstable and expensive Ag2O. To reduce Ag2O contents, we fabricated (Ag0.5Na0.5)(Nb1-xTax)O3 (ANNT100x) ceramics. The results reveal that Ta-substitution plays a dual role: inducing chemical pressure to compress the unit cell along spontaneous polarization direction, enhancing antiferroelectric stability; and increasing the band gap (Eg), boosting intrinsic breakdown strength (Eb). These crucial factors contribute to the enhanced Wrec achieved in ANNT50. Notably, ANNT50 ceramics fabricated by the rolling process exhibit higher Eb (=578kV/cm) than the conventional process, favoring the complete triggering of “double” polarization with significantly enhanced Wrec (= 6.5J/cm3). Discharge results indicate that the ceramic displays high power density (Pavg = 78MW/cm3) and discharge energy (Wdis = 5.86J/cm3), which can rival currently reported Ag(Nb, Ta)O3 ceramics.
High Energy Density in Ag 0.5 Na 0.5 (nb 1-X Ta X )O 3 Antiferroelectric Ceramics

Ye Tian,Lei Li,Yonghao Xu,Ming Ma,Chen,Zixiong Sun,Liaona She,Guanjun Chen,Tong Wang,Wanyin Ge,Xiaoyong Wei,Li Jin

DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.04.049

IF: 5.7

2024-01-01

Journal of the European Ceramic Society

Abstract:There has been significant interest in AgNbO 3 -based antiferroelectric ceramics, recently, due to their ability to achieve high energy storage density ( W rec ). However, fabricating their commercial products faces challenges due to chemically unstable and expensive Ag 2 O. To reduce Ag 2 O contents, we fabricated (Ag 0.5 Na 0.5 )(Nb 1- x Ta x )O 3 (ANNT100 x ) ceramics. The results reveal that Ta-substitution plays a dual role: inducing chemical pressure to compress the unit cell along spontaneous polarization direction, enhancing antiferroelectric stability; and increasing the band gap ( E g ), boosting intrinsic breakdown strength ( E b ). These crucial factors contribute to the enhanced W rec achieved in ANNT50. Notably, ANNT50 ceramics fabricated by the rolling process exhibit higher E b ( =578 kV/cm) than the conventional process, favoring the complete triggering of " double " polarization with significantly enhanced W rec ( = 6.5 J/cm 3 ). Discharge results indicate that the ceramic displays high power density ( P avg = 78 MW/cm 3 ) and discharge energy ( W dis = 5.86 J/cm 3 ), which can rival currently reported Ag (Nb, Ta)O 3 ceramics.
Silver Niobate Lead-Free Antiferroelectric Ceramics: Enhancing Energy Storage Density by B-Site Doping.

Lei Zhao,Jing Gao,Qing Liu,Shujun Zhang,Jing-Feng Li

DOI: https://doi.org/10.1021/acsami.7b17382

IF: 9.5

2017-01-01

ACS Applied Materials & Interfaces

Abstract:Lead-free dielectric ceramics with high recoverable energy density are highly desired to sustainably meet the future energy demand. AgNbO3-based lead-free antiferroelectric ceramics with double ferroelectric hysteresis loops have been proved to be potential candidates for energy storage applications. Enhanced energy storage performance with recoverable energy density of 3.3 J/cm3 and high thermal stability with minimal energy density variation (<10%) over a temperature range of 20-120 °C have been achieved in W-modified AgNbO3 ceramics. It is revealed that the W6+ cations substitute the B-site Nb5+ and reduce the polarizability of B-site cations, leading to the enhanced antiferroelectricity, which is confirmed by the polarization hysteresis and dielectric tunability. It is believed that the polarizability of B-site cations plays a dominant role in stabilizing the antiferroelectricity in AgNbO3 system, in addition to the tolerance factor, which opens up a new design approach to achieve stable antiferroelectric materials.
Lead‐Free Antiferroelectric Silver Niobate Tantalate with High Energy Storage Performance

Lei Zhao,Qing Liu,Jing Gao,Shujun Zhang,Jing-Feng Li

DOI: https://doi.org/10.1002/adma.201701824

IF: 29.4

2017-01-01

Advanced Materials

Abstract:Antiferroelectric materials that display double ferroelectric hysteresis loops are receiving increasing attention for their superior energy storage density compared to their ferroelectric counterparts. Despite the good properties obtained in antiferroelectric La‐doped Pb(Zr,Ti)O3‐based ceramics, lead‐free alternatives are highly desired due to the environmental concerns, and AgNbO3 has been highlighted as a ferrielectric/antiferroelectric perovskite for energy storage applications. Enhanced energy storage performance, with recoverable energy density of 4.2 J cm−3 and high thermal stability of the energy storage density (with minimal variation of ≤±5%) over 20–120 °C, can be achieved in Ta‐modified AgNbO3 ceramics. It is revealed that the incorporation of Ta to the Nb site can enhance the antiferroelectricity because of the reduced polarizability of B‐site cations, which is confirmed by the polarization hysteresis, dielectric tunability, and selected‐area electron diffraction measurements. Additionally, Ta addition in AgNbO3 leads to decreased grain size and increased bulk density, increasing the dielectric breakdown strength, up to 240 kV cm−1 versus 175 kV cm−1 for the pure counterpart, together with the enhanced antiferroelectricity, accounting for the high energy storage density.
High energy-storage performance of lead-free AgNbO3 antiferroelectric ceramics fabricated via a facile approach

Xiucai Wang,Weiqiang Cai,Ze Xiao,Guangguang Yang,Xinmei Yu,Jianwen Chen,Dongchu Chen,Qingfeng Zhang,Min Chen

DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.04.030

IF: 5.7

2021-08-01

Journal of the European Ceramic Society

Abstract:AgNbO3 lead free AFE ceramics are considered as one of the promising alternatives to energy storage applications. In the majority of studies concerning the preparation of AgNbO3 AFE ceramics, an oxygen atmosphere is required to achieve high performance, increasing the complexity of the fabrication process. Herein, a facile approach to preparing AgNbO3 ceramics in the ambient air was reported, in which the AgNbO3 ultrafine powder with stable perovskite structure was synthesized by hydrothermal method instead of the conventional ball milling process, leading to a lower temperature of phase formation and thus smaller grain size. The resulting ceramics sintered at 940 °C displayed high breakdown strength (216 kV/cm) and a recoverable energy density of 3.26 J/cm3 with efficiency of 53.5%. Also, the high thermal stability of recoverable energy density (with minimal variation of ≤20%) and efficiency (≤ 10%) over 30–150℃, enables AgNbO3 ceramics achieved to be a promising candidate for energy storage applications.

materials science, ceramics
Antiferroelectric‐ferroelectric phase transition in lead‐free AgNbO3 ceramics for energy storage applications

Jing Gao,Lei Zhao,Qing Liu,Xuping Wang,Shujun Zhang,Jing‐Feng Li

DOI: https://doi.org/10.1111/jace.15780

IF: 4.186

2018-01-01

Journal of the American Ceramic Society

Abstract:The high-energy storage density reported in lead-free AgNbO3 ceramics makes it a fascinating material for energy storage applications. The phase transition process of AgNbO3 ceramics plays an important role in its properties and dominates the temperature and electric field dependent behavior. In this work, the phase transition behavior of AgNbO3 ceramics was investigated by polarization hysteresis and dielectric tunability measurements. It is revealed that the ferrielectric (FIE) phase at room temperature possesses both ferroelectric (FE)-like and antiferroelectric (AFE)-like dielectric responses prior to the critical AFE-FE transition point. A recoverable energy storage density of 2J/cm(3) was achieved at 150kV/cm due to the AFE-FE transition. Based on a modified Laudau phenomenological theory, the stabilities among the AFE, FE and FIE phases are discussed, laying a foundation for further optimization of the dielectric properties of AgNbO3.
Enhanced energy storage properties of silver niobate antiferroelectric ceramics with A-site Eu3+ substitution and their structural origin

Peng Shi,Jin Liu,Yuechan Song,Wenwen Wu,Lina Liu,Xiaobin Zhou,Xiaoming Chen,Xiaojie Lou,Peng Liu

DOI: https://doi.org/10.1063/5.0200472

IF: 2.877

2024-03-25

Journal of Applied Physics

Abstract:AgNbO3 (AN)-based lead-free antiferroelectric ceramics are widely studied for their use as dielectric capacitor materials. In this study, Eu3+-doped AN ceramics were prepared and the results show that Eu3+ diffused into the AN lattice. The ceramics were formed by M1 and M2 phases coexisting at room temperature, as distinct from the M1 (M: monoclinic) phase of pure AN. Electrical properties and structural characterization showed that the antiferroelectric stability of the ceramics increases with the increase in Eu3+ levels. At room temperature, Ag0.94Eu0.02NbO3 ceramic exhibited a good energy storage density of 5.3 J/cm3 and a high efficiency of 71.9%. When the temperature rises from room temperature to 140 °C, the efficiency of the sample decreases from 80.4% to 67.1% and Wr decreases from 2.1 to 2.0 J/cm3, which indicates that the sample has good temperature stability. The time constant (t0.9) of this sample was less than 60 ns and the power density (PD) was 51.3 MW/cm3, indicating excellent charge–discharge capabilities. This novel ceramic is expected to be used as a new dielectric capacitor material for pulsed power supplies.

physics, applied
Superior energy storage performance realized in antiferroelectric 0.10 wt% MnO2-AgNbO3 ceramics via Bi-doping induced phase engineering

Jing Wang,Xuhui Fan,Zhen Liu,Kongjun Zhu,Hao Yuan,Zehan Zheng,Lei Zhao,Ji Zhang,Qibin Yuan,Jing-Feng Li

DOI: https://doi.org/10.1039/d3ta04605b

IF: 11.9

2023-10-05

Journal of Materials Chemistry A

Abstract:Dielectric capacitors based on antiferroelectric ceramics are promising for applications in advanced high-power electric and electronic devices, for which more efforts should be devoted to enhance the recoverable energy storage density and energy efficiency. In this work, a record-high recoverable energy storage density Wrec up to 9.0 J cm-3 and energy efficiency η of 90% are achieved in lead-free AgNbO3-based ceramics composed of antiferroelectric and paraelectric phases, which were realized by phase engineering via Bi-doping. Compared with pristine AgNbO3, the enhancement in recoverable energy storage density and energy efficiency reaches 621% and 241%, respectively. In addition, the breakdown strength Eb exceeds 650 kV cm-1 in 12 mol% Bi-doped 0.10 wt% MnO2-AgNbO3 ceramics, which greatly contributes to the exceptionally enhanced energy storage performance. The excellent performance could be retained at elevated temperatures, various frequencies and cycles. Moreover, the discharge energy density Wd in direct-current charge-discharge performance reaches 8.0 J cm-3, which is also superior to those reported in other lead-free dielectric energy storage ceramics. The strategy can provide an applicable method to optimize energy storage performance and other functionalities of dielectric materials.

materials science, multidisciplinary,chemistry, physical,energy & fuels
Aliovalent A-site engineered AgNbO3 lead-free antiferroelectric ceramics toward superior energy storage density

Nengneng Luo,Kai Han,Fangping Zhuo,Chao Xu,Guangzu Zhang,Laijun Liu,Xiyong Chen,Changzheng Hu,Huanfu Zhou,Yuezhou Wei

DOI: https://doi.org/10.1039/c9ta02053e

IF: 11.9

2019-01-01

Journal of Materials Chemistry A

Abstract:Aliovalent A-site engineering enables superior energy storage density in AgNbO3 lead-free antiferroelectric ceramics.
Enhanced energy storage properties and antiferroelectric stability of Mn-doped NaNbO3-CaHfO3 lead-free ceramics: Regulating phase structure and tolerance factor

Yang Yin,Jing-Ru Yu,Yu-Cheng Tang,Ai-Zhen Song,Huan Liu,Dong Yang,Jing-Feng Li,Lei Zhao,Bo-Ping Zhang

DOI: https://doi.org/10.1016/j.jmat.2021.11.013

IF: 8.589

2022-01-01

Journal of Materiomics

Abstract:NaNbO3-based ceramics usually show ferroelectric-like P-E loops at room temperature due to the irreversible transformation of the antiferroelectric orthorhombic phase to ferroelectric orthorhombic phase, which is not conducive to energy storage applications. Our previous work found that incorporating CaHfO3 into NaNbO3 can stabilize its antiferroelectric phase by reducing the tolerance factor (t), as indicated by the appearance of characteristic double P-E loops. Furthermore, a small amount of MnO2 addition effectively regulate the phase structure and tolerance factor of 0.94NaNbO(3)-0.06CaHfO(3) (0.94NN-0.06CH), which can further improve the stability of antiferroelectricity. The XRD and XPS results reveal that the Mn ions preferentially replace A-sites and then B-sites as increasing MnO2. The antiferroelectric orthorhombic phase first increases and then decreases, while the t shows the reversed trend, thus an enhanced antiferroelectricity and the energy storage density W-rec of 1.69 J/cm(3) at 240 kV/cm are obtained for 0.94NN-0.06CH-0.5%MnO2 (in mass fraction). With the increase of Mn content to 1.0 % from 0.5 %, the efficiency increases to 81 % from 45 %, although the energy storage density decreases to 1.31 J/cm(3) due to both increased tolerance factor and non-polar phase. (C) 2021 The Chinese Ceramic Society. Production and hosting by Elsevier B.V.
Enhanced energy storage density in Ca and Ta co‐doped AgNbO 3 antiferroelectric ceramics

Wenna Chao,Tongqing Yang,Yongxiang Li,Zhifu Liu

DOI: https://doi.org/10.1111/jace.17415

IF: 4.186

2020-09-01

Journal of the American Ceramic Society

Abstract:Ca and Ta co‐doped AgNbO3 antiferroelectric lead‐free ceramics were fabricated by rolling process technique, and improved energy storage properties were obtained. X‐ray diffraction and Raman spectra indicate a single perovskite structure for (Ag1‐2xCax)(Nb1‐xTax)O3 ceramics. The dielectric performances were also investigated, showing that increasing the content of Ca and Ta from 0.1 to 5 mol% gradually decreased the temperatures of the phase transition of monoclinic M1‐M2 and M2‐M3. This proved the enhanced antiferroelectricity stability associated with the enlarged low temperature phase transition region. The obtained (Ag0.90Ca0.05)(Nb0.95Ta0.05)O3 ceramics exhibit an enhanced recoverable energy storage density (3.36 J/cm3) and efficiency (58.3%) with good temperature and frequency stability. The same composition shows excellent charge and discharge properties with a discharge current as high as 91.5 A and fast discharge speed (150 ns discharge period). All these merits demonstrate that AgNbO3‐based antiferroelectric ceramics are competitive with other lead‐based and lead‐free dielectric capacitors, which are promising candidates for dielectric energy storage applications.

materials science, ceramics
The energy storage performance of Sm3+ and Hf4+ co-doped AgNbO3 lead-free antiferroelectric ceramic

N Zhang,Z F Zhang,J Y Wang,J R Jiang,Y H Wang,P P Jia,M M Zhu,H X Zhao,Y Y Guo,G L Song,Na Zhang,Z. F. Zhang,J. Y. Wang,J. R. Jiang,Y. H. Wang,P. P. Jia,M. M. Zhu,H. X. Zhao,Yanyan Guo,guilin song

DOI: https://doi.org/10.1088/1402-4896/ad1907

2023-12-28

Physica Scripta

Abstract:Antiferroelectrics with excellent energy storage density have attracted considerable attention due to their potential applications in electric vehicles, pulsed power weapons, etc. With the trend of environmental protection, the lead-free antiferroelectric AgNbO3 is a promising candidate for energy storage applications. However, the limited recoverable energy density (Wrec) of AgNbO3 severely restricts its application in high-power systems. To enhance the Wrec of AgNbO3, the A/B-site Sm3+/Hf4+ co-doping approach was adopted. It positively influenced the energy density and efficiency in AgNbO3 by simultaneously increasing the maximum polarization and breakdown strength. The optimized Wrec of 1.98 J/cm3 and high energy storage efficiency () of 64% were obtained in the MnO2-doped Ag0.97Sm0.01Nb0.99Hf0.01O2.995 ceramic at an electric field of 202 kV/cm. This work indicates that the A- and B-site substitution with donor and acceptor dopants and using MnO2 as a sintering aid is an effective strategy for developing high-performance ceramic capacitors for energy storage applications.

physics, multidisciplinary
High energy storage density in AgNbO3-based lead-free antiferroelectrics using A/B-site co-doping strategy

N. Zhang,J. R. Jiang,J. X. Zhang,J. Y. Wang,P. P. Jia,M. M. Zhu,Y. Y. Guo,S. Zhou,G. L. Song

DOI: https://doi.org/10.1063/5.0198962

IF: 4

2024-04-22

Applied Physics Letters

Abstract:Lead-free antiferroelectric AgNbO3 ceramics have garnered extensive attention due to their rapid charge/discharge capabilities and environmentally friendly nature, holding immense potential for energy storage applications. However, the practical utilization of AgNbO3 has been hindered by its low energy storage density. This study employed an A/B-site co-doping strategy, which yielded positive effects on the energy performance of AgNbO3 ceramics. By modifying the A/B-sites with equivalent amounts of Bi3+ and Y3+ ions, enhanced maximum polarization, improved breakdown field, and slimmer hysteresis loops were simultaneously achieved, as the combined effects of refined grain size, wider optical bandgap, and randomly distributed antiferroelectric nanodomains, which were verified through the scanning electron microscope, transmission electron microscope, and ultraviolet–visible spectrum. As a consequence, a high energy storage density of 5.40 J/cm3 accompanied by an energy storage efficiency of 56.5% was achieved in the Ag0.97Bi0.01Nb0.994Y0.01O3 ceramic under a relatively low electric field of 190 kV/cm. This study underscores the effectiveness of A/B-site aliovalent co-doping as a viable strategy for developing high-performance ceramic capacitors for energy storage applications.

physics, applied
Mechanism of enhanced energy storage density in AgNbO3-based lead-free antiferroelectrics

Zhilun Lu,Weichao Bao,Ge Wang,Shi-Kuan Sun,Linhao Li,Jinglei Li,Huijing Yang,Hongfen Ji,Antonio Feteira,Dejun Li,Fangfang Xu,Annette K. Kleppe,Dawei Wang,Shi-Yu Liu,Ian M. Reaney

DOI: https://doi.org/10.1016/j.nanoen.2020.105423

IF: 17.6

2021-01-01

Nano Energy

Abstract:The mechanisms underpinning high energy storage density in lead-free Ag1–3xNdxTayNb1-yO3 antiferroelectric (AFE) ceramics have been investigated. Rietveld refinements of in-situ synchrotron X-ray data reveal that the structure remains quadrupled and orthorhombic under electric field (E) but adopts a non-centrosymmetric space group, Pmc21, in which the cations exhibit a ferrielectric configuration. Nd and Ta doping both stabilize the AFE structure, thereby increasing the AFE-ferrielectric switching field from 150 to 350 kV cm−1. Domain size and correlation length of AFE/ferrielectric coupling reduce with Nd doping, leading to slimmer hysteresis loops. The maximum polarization (Pmax) is optimized through A-site aliovalent doping which also decreases electrical conductivity, permitting the application of a larger E. These effects combine to enhance energy storage density to give Wrec = 6.5 J cm−3 for Ag0.97Nd0.01Ta0.20Nb0.80O3.

materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology
Enhanced energy storage properties and antiferroelectric stability of Mn-doped NaNbO3-CaHfO3 lead-free ceramics: Regulating phase structure and tolerance factor

Yang Yin,Jing-Ru Yu,Yu-Cheng Tang,Ai-Zhen Song,Huan Liu,Dong Yang,Jing-Feng Li,Lei Zhao,Bo-Ping Zhang

DOI: https://doi.org/10.1016/j.jmat.2021.11.013

IF: 8.589

2021-11-01

Journal of Materiomics

Abstract:NaNbO3-based ceramics usually show ferroelectric-like P-E loops at room temperature due to the irreversible transformation of the antiferroelectric orthorhombic phase to ferroelectric orthorhombic phase, which is not conducive to energy storage applications. Our previous work found that incorporating CaHfO3 into NaNbO3 can stabilize its antiferroelectric phase by reducing the tolerance factor (t), as indicated by the appearance of characteristic double P-E loops. Furthermore, a small amount of MnO2 addition effectively regulate the phase structure and tolerance factor of 0.94NaNbO3-0.06CaHfO3 (0.94NN-0.06CH), which can further improve the stability of antiferroelectricity. The XRD and XPS results reveal that the Mn ions preferentially replace A-sites and then B-sites as increasing MnO2. The antiferroelectric orthorhombic phase first increases and then decreases, while the t shows the reversed trend, thus an enhanced antiferroelectricity and the energy storage density W rec of 1.69 J/cm3 at 240 kV/cm are obtained for 0.94NN-0.06CH-0.5%MnO2(in mass fraction). With the increase of Mn content to 1.0 % from 0.5 %, the efficiency increases to 81 % from 45 %, although the energy storage density decreases to 1.31 J/cm3 due to both increased tolerance factor and non-polar phase.

materials science, multidisciplinary,chemistry, physical,physics, applied
Enhanced antiferroelectric phase stability in La-doped AgNbO3: perspectives from the microstructure to energy storage properties

Jing Gao,Yichi Zhang,Lei Zhao,Kai-Yang Lee,Qing Liu,Andrew Studer,Manuel Hinterstein,Shujun Zhang,Jing-Feng Li

DOI: https://doi.org/10.1039/c8ta09353a

IF: 11.9

2019-01-01

Journal of Materials Chemistry A

Abstract:La-doped AgNbO3 lead-free ceramics were fabricated by conventional solid-state reaction, and the phase stability and energy storage properties were investigated. The temperature-and electric field-dependent dielectric constants show that the antiferroelectric (AFE) phase stability is enhanced via the La doping. Neutron diffraction was performed to obtain insights into the structural evolution with composition and temperature, where the local structural variation is found to involve subtle ion displacement as well as oxygen octahedral tilting, leading to the disruption of the long-range interactions, which is responsible for the enhanced AFE phase stability. As expected, the enhanced AFE phase stability, together with the improved breakdown strength, gives rise to a high energy density of 4.4 J cm(-3) and an improved efficiency of 70%, which are achieved in 2 mol% La-doped AgNbO3 ceramics. Our research opens a new way to tailor the macroscopic properties by tuning the microstructure of AgNbO3-based materials.
Antiferroelectric stability and energy storage properties of Co-doped AgNbO3 ceramics

Danni Feng,Huiling Du,Hongpei Ran,Tong Lu,Siyu Xia,Li Xu,Zhouxiang Wang,Cuiying Ma

DOI: https://doi.org/10.1016/j.jssc.2022.123081

IF: 3.3

2022-06-01

Journal of Solid State Chemistry

Abstract:AgNbO3 ceramics have attracted progressively more attention to high power energy storage in dielectric capacitors because of complicated in a series of phase transitions. In this work, Ag1-3x Bi x Nb1-3/5x Sc x O3 (x = 0, 0.005, 0.01, 0.02) ceramics were synthesized via a solid state reaction method in flowing oxygen. The microstructure, dielectric and energy storage properties of as-prepared samples were systematic characterized to evaluate the potential as high energy storage capacitors. A high recoverable energy storage density (3.65 J/cm3) and high efficiency (84.31%) were simultaneously obtained in a modified AgNbO3-based ceramic at 21.5 MV/m. The energy storage performance is improved by the ions doping that effectively interrupt the dipoles arrangement structure and stabilize the disordered antiferroelectric phase in the long-range order. Co-doping of Bi3+ on the A-site and Sc3+ on the B-site in AgNbO3 is an effective method to enhance the electric field intensity of field-induced phase transitions from antiferroelectric (AFE) to ferroelectric (FE) phases. The M1-M2 phase transition shifted to a lower temperature with an increase in the Bi/Sc amounts, which suppressed the ferroelectricity and obtained pinched-hysteresis loops in modified AgNbO3 ceramics. These results indicate that Bi/Sc co-doped AgNbO3 ceramics are highly efficient lead-free antiferroelectric materials for prospective application in high-performance energy storage capacitors.

chemistry, physical, inorganic & nuclear
Excellent Energy Storage Performance of Nd-Modified Lead-free AgNbO3 Ceramics Via Triple Collaborative Optimization

Yulong Yang,Jielin Zha,Xiaomei Lu,Fengzhen Huang,Xuenong Ying,Jinsong Zhu

DOI: https://doi.org/10.1016/j.nanoen.2024.110242

IF: 17.6

2024-01-01

Nano Energy

Abstract:Lead-free Dielectric capacitors that possess high power density as well as swift charging/discharging speed are in tremendous requirement in pulse/high power fields, but the lower recovery energy density and efficiency restrict their applications. Herein, via triple collaborative optimization, we designed Nd-modified AgNbO3 antiferroelectric ceramics with excellent energy storage performance. First, Nd3+ ions are smaller than Ag+ ions, which effectively inhibits cation displacements and the tilting of oxygen octahedra, leading to an optimized phase composition, the suppressed ferroelectricity and enhanced antiferroelectricity. Second, the valence of Nd3+ ions are higher than that of Ag+ ions, which help to lower the content of oxygen vacancies. Third, the random substitution of Nd3+, extrinsic ions, cause the chemical disorder, thus dwindling the grain size. Both of the latter could boost the breakdown field. Eventually, the synchronously boosted energy density of 7.16J/cm3 and efficiency of 72%, together with excellent frequency stability, temperature tolerance, ultrafast charging/discharging time of 45ns and superhigh power density of 354.2MW/cm3, are achieved in Ag0.91Nd0.03NbO3. All these merits manifest Nd- AgNbO3 as a promising candidate for lead-free high-power energy storage devices. Our work brings forward a good reference for developing the capabilities of antiferroelectric capacitors.
Aliovalent A-site engineered AgNbO3 lead-free antiferroelectric ceramics toward superior energy storage density

Nengneng Luo,Kai Han,Fangping Zhuo,Chao Xu,Guangzu Zhang,Laijun Liu,Xiyong Chen,Changzheng Hu,Huanfu Zhou,Yuezhou Wei

DOI: https://doi.org/10.1039/c9ta02053e

IF: 11.9

2019-01-01

Journal of Materials Chemistry A

Abstract:Lead-free dielectric capacitors with high energy storage density and temperature-insensitive performance are pivotal to pulsed power systems. In this work, a pronounced recoverable energy storage density (W-rec) was achieved in AgNbO3-based lead-free antiferroelectric ceramics, by aliovalent A-site Sm mediation. The Sm modification was found to alter the crystal structure and enhance the interaction among the ions by affecting the electronic structure, leading to improved antiferroelectricity. The Sm0.03Ag0.91NbO3 solid solution exhibited a superior W-rec of 5.2 J cm(-3) with a high energy storage efficiency (eta) of 68.5% at an applied electric field of 290 kV cm(-1). Excellent temperature stability of W-rec with a minimal variation of less than 4% from room temperature up to 140 degrees C was also observed. Meanwhile, the Sm0.03Ag0.91NbO3 ceramic also exhibited an ultrafast discharge speed (similar to 20 mu s) and high discharge energy density (4.2 J cm(-3)). Ginzburg-Landau-Devonshire (GLD) phenomenology revealed that the significantly stabilized antiferroelectricity and the cation disorder were responsible for the ultrahigh W-rec and eta. The extraordinary energy storage performance indicates the SmxAg1-3xNbO3 system a promising candidate for advanced pulsed power capacitors. More importantly, the results show that aliovalent A-site engineering is an effective way to achieve high energy storage density.

Lead-free AgNbO<sub>3</sub> anti-ferroelectric ceramics with an enhanced energy storage performance using MnO<sub>2</sub> modification

Lead-Free Agnbo3 Anti-Ferroelectric Ceramics With An Enhanced Energy Storage Performance Using Mno2 Modification

High energy density in Ag0.5Na0.5(Nb1-xTax)O3 antiferroelectric ceramics

High Energy Density in Ag 0.5 Na 0.5 (nb 1-X Ta X )O 3 Antiferroelectric Ceramics

Silver Niobate Lead-Free Antiferroelectric Ceramics: Enhancing Energy Storage Density by B-Site Doping.

Lead‐Free Antiferroelectric Silver Niobate Tantalate with High Energy Storage Performance

High energy-storage performance of lead-free AgNbO3 antiferroelectric ceramics fabricated via a facile approach

Antiferroelectric‐ferroelectric phase transition in lead‐free AgNbO3 ceramics for energy storage applications

Enhanced energy storage properties of silver niobate antiferroelectric ceramics with A-site Eu3+ substitution and their structural origin

Superior energy storage performance realized in antiferroelectric 0.10 wt% MnO2-AgNbO3 ceramics via Bi-doping induced phase engineering

Aliovalent A-site engineered AgNbO<sub>3</sub> lead-free antiferroelectric ceramics toward superior energy storage density

Enhanced energy storage properties and antiferroelectric stability of Mn-doped NaNbO<sub>3</sub>-CaHfO<sub>3</sub> lead-free ceramics: Regulating phase structure and tolerance factor

Enhanced energy storage density in Ca and Ta co‐doped AgNbO 3 antiferroelectric ceramics

The energy storage performance of Sm3+ and Hf4+ co-doped AgNbO3 lead-free antiferroelectric ceramic

High energy storage density in AgNbO3-based lead-free antiferroelectrics using A/B-site co-doping strategy

Mechanism of enhanced energy storage density in AgNbO3-based lead-free antiferroelectrics

Enhanced energy storage properties and antiferroelectric stability of Mn-doped NaNbO3-CaHfO3 lead-free ceramics: Regulating phase structure and tolerance factor

Enhanced antiferroelectric phase stability in La-doped AgNbO3: perspectives from the microstructure to energy storage properties

Antiferroelectric stability and energy storage properties of Co-doped AgNbO3 ceramics

Excellent Energy Storage Performance of Nd-Modified Lead-free AgNbO3 Ceramics Via Triple Collaborative Optimization

Aliovalent A-site engineered AgNbO3 lead-free antiferroelectric ceramics toward superior energy storage density