Abstract:Ho3+-doped AlF3-TeO2-based glass fibers based on AlF3-BaF2-CaF2-YF3-SrF2-MgF2-TeO2 glasses are fabricated by using a rod-in-tube method. The glass rod including a core and a thick cladding layer is prepared by using a suction method, where the thick cladding layer is used to protect the core from the effect of surface crystallization during the fiber drawing. By inserting the glass rod into a glass tube, the glass fibers with relatively low loss (similar to 2.3 dB m(-1) @ 1560 nm) are prepared. By using a 38 cm long Ho3+-doped AlF3-TeO2-based glass fiber as the gain medium and a 1965 nm fiber laser as the pump source, 2065 nm lasing is obtained for a threshold pump power of similar to 220 mW. With further increasing the pump power to similar to 325 mW, the unsaturated output power of the 2065 nm laser is about 82 mW and the corresponding slope efficiency is up to 68.8%. The effects of the gain fiber length on the lasing threshold, the slope efficiency, and the operating wavelength are also investigated. Our experimental results show that Ho3(+-)doped AlF3-TeO2-based glass fibers are promising gain media for 2.1 mu m laser applications.

Tm3+ or Ho3+ Doped Fluorotellurite Microstructure Fiber for 2μm Lasing

Tm~(3+)/Ho~(3+) Co-doped Fluorotellurite Microstructure Fiber for 2.1 Μm Lasing

2.074- $\mu \text{m}$ Lasing from Ho 3+ -Doped Fluorotellurite Microstructured Fibers Pumped by a 1120-Nm Laser

Holmium-doped fluorotellurite microstructured fibers for 2.1 μm lasing

Tm3+-doped Fluorotellurite Glass Microsphere Resonator Laser at 2.3 Μm.

1887 Nm Lasing in Tm3+-doped TeO2-BaF2-Y2O3 Glass Microstructured Fibers

Tm~(3+) Doped Tellurite Microstructure Fiber Laser

Watt-level 815 Nm Lasing from Tm3+-doped Fluorotellurite Glass Fibers.

2.3 Μm Lasing in Tm3+ Doped Fluoroaluminate Glass Fibers with an Upconversion Pumping Scheme

Ho3+ Doped Fluoroaluminate Glass Fibers for 2.9 Mu M Lasing

Tm^3+ Doped Lead Silicate Glass Single Mode Fibers for 20 Μm Laser Applications

Tm 3+ doped lead silicate glass single mode fibers for 2.0 μm laser applications

High-Power Pulsed 2-Μ M Tm 3 +-Doped Fiber Laser

Femtosecond Laser Inscription of Bragg Gratings in Tm3+-doped Fluorotellurite Glass Fibers for Lasing at 2.3 Μm

Tm 3+ -doped tellurium germanate glass and its double-cladding fiber for 2μm laser

Ho3+-doped AlF3–TeO2-based Glass Fibers for 2.1µm Laser Applications

Er3+ doped low-hydroxyl fluorotellurite microstructured fibers for 2.7 µm laser applications

8.08 W Holmium Doped Fluorotellurite Fiber Laser at 2067 Nm

Triple-wavelength Lasing at 1.50 Μm, 1.84 Μm and 2.08 Μm in a Ho3+/Tm3+ Co-Doped Fluorozirconate Glass Microsphere

Efficient 2075-nm laser emission from Ho3+-doped fluorotellurite glass in a compact all-fiber structure

Controllable structural tailoring for enhanced ∼2 µm emission in heavily Tm3+-doped germanate glasses.