Structure, Microwave Properties and Low Temperature Sintering of Ta2O5 and Co2O3 Codoped Zn0.5Ti0.5NbO4 Ceramics
Hongyu Yang,Enzhu Li,Shuxin Duan,Hongcai He,Shuren Zhang
DOI: https://doi.org/10.1016/j.matchemphys.2017.06.025
IF: 4.778
2017-01-01
Materials Chemistry and Physics
Abstract:The crystal structure of (Zn1-xCox)(0.5)Ti-0.5(Nb1-yTay)O-4 microwave dielectric ceramics was determined by Rietveld refinement. The XRD results show orthorhombic structure of Zn0.5Ti0.5NbO4 and appearance of a second phase Zn0.7Nb0.33Ti0.5O2 with tetragonal structure. The relationships between the dielectric polarizability, the second phase content, bond length, bond strength, bond valence, packing fraction and microwave dielectric properties were systematically discussed. The er values decrease at first (x = 0, 0.1) because of the decreased polarizability and a lower relative density, while after x = 0.2, a second phase is formed, which increases the epsilon(r) to a great extent. The Q x f values drop are mainly ascribed to the decrease of packing fraction, grain size and the increase of the second phase content. With the decrease of bond valence of Ti-O and oxygen octahedron distortion, the tau(f) values increase. Excellent microwave properties of the ceramics sintered at 1175 degrees C were obtained for x = 0.2 and y = 0.3: epsilon(r) = 38.02, Q x f = 23,550 GHz, tau(f) = 4.62 ppm/degrees C.Furthermore, Li2O-B2O3-SiO2 (LBS) glass was used to lower the sintering temperature. The effects of LBS glass on the crystal structure, sintering behavior and activation energy were also discussed. These results indicate that LBS glass significantly lowers the activation energy and has no influence on the phase composition. The ceramics sintered at 900 degrees C for 4 h show great properties: epsilon(r) = 34.10, Q x f = 13,349 GHz, tau(f) = 7.12 ppm/degrees C, which is promising for LTCC application. (C) 2017 Elsevier B.V. All rights reserved.