Microwave Synthesis of CaMoO 4 :Sm 3+ Orange Reddish-Emitting Phosphors and Its Photoluminescence Property
Yongqing Zhai,Ying Han,Xin Zhao,Shuai Yang,Han Liu,Pengfei Song,Guang Jia
DOI: https://doi.org/10.1007/s10854-017-7398-0
2017-01-01
Journal of Materials Science Materials in Electronics
Abstract:Rare-earth ion Sm3+-activated CaMoO4 phosphors were synthesized by a rapid microwave radiation method. The samples were characterized by means of X-ray powder diffractometer, scanning electron microscope, fourier transform infrared spectrum, fluorescence spectrometer, and diffused reflectance spectrum, respectively. The X-ray powder diffractometer results confirmed that the as-synthesized samples were pure tetragonal phase CaMoO4 when the microwave reaction time was 60 min. The sample consisted of many cubic particles and some irregular polyhedrons. The cubic particle was assembled by many closely packed quasi-spherical grains, and the grain size was about 0.2–2.0 μm. The emission spectrum contained a broad band centered at 305 nm attributing to the intrinsic emission of MoO4 2−, and three strong emission peaks located at ~562, 605 and 645 nm, originating from the intra-4f transitions of Sm3+ (4G5/2 → 6H J , J = 5/2, 7/2, 9/2), respectively. The quenching concentration of activator Sm3+ was x = 0.02, due to the dipole–dipole interaction and the cross-relaxation processes between Sm3+. Moreover, all the color coordinates of samples were located in orange–red region, showing potential applications for white LEDs, solid state lasers and fluorescent lamps.