Abstract:SrMoO4: Sm3+ orange red-emitting phosphors for novel application in temperature measurement were prepared by solid-phase synthesis method. SrMoO4: Sm3+ phosphor with scheelite structure was assigned to tetragonal system and I41 /a space group. Sm3+ ions could occupy Sr2+ lattice sites of SrMoO4. SrMoO4: Sm3+ consisted of irregular microparticle with well-crystallized pomegranate seed-like morphology and Sm3+ ions can be evenly distributed in the SrMoO4 matrix. The band gap value of SrMoO4: 1.0%Sm3+ (∼4.228 eV) is less than that of SrMoO4 (∼4.267 eV), which is due to generation of defective energy levels in band gap. The appropriate quenching concentration of Sm3+ was 1.0%, the critical distance is ∼25.57 Å and θ is 7.1, close to 8, which was attributed to dipole−quadrupole interaction type of electric multipolar interaction. SrMoO4:1.0%Sm3+ had excellent thermal stability of the PL peak at 598 nm and 644 nm and anti-thermal quenching property of the PL peak at 530 nm and 563 nm. The activation energy based on the intensity of the PL peak at 598 nm is 0.318 eV. The new dual-model thermometry strategy base on exponential function and modified Boltzmann population distribution would be proposed. SrMoO4:Sm3+ phosphor had the absolute sensitivities of 0.108 K−1 based on exponential function and the relative sensitivities of 0.601% K−1 based on modified Boltzmann population distribution. The excellent anti-thermal quenching and good thermal stability of SrMoO4: Sm3+ phosphors indicate that it has a potential for applications as pc-WLEDs and optical thermometry.

Characterization and photoluminescence properties of SrMoO4 film chemical solution processing

Synthesis of Crystallized Strontium Molybdate Thin Films Through Chemical Solution Processing

Synthesis and photoluminescent properties of nanocrystalline CaMoO 4 thin film via chemical solution processing

Preparation and the Photoluminescence Properties of SrMoO_4 Powder Prepared by Chemical Solution Deposition

Experimental researches on the characteristics of SrMoO4 thin film prepared by electrochemical technique

Synthesis and Photoluminescent Properties of Nanocrystalline CaMoO<sub>4</sub> Thin Film via Chemical Solution Processing

Synthesis and Luminescence Properties of a Novel Red SrMoO4:Sm3+,R+ Phosphor

Temperature-dependent Optical Properties of Low-Loss Plasmonic SrMoO3 Thin Films

Solution-deposited and low temperature-annealed Eu3+/Tb3+-doped CaMoO4/SrMoO4 luminescent thin films

Preparation and growth characterization of crystallized Sr 1-xCaxMoO4 and Sr1-xBa xMoO4 films by chemical solution processing

High UV Transparent Conductivity of SrMoO3 Thin Films

Progress in SrMoO4-based Materials with Scheelite Structure

Crystallized Calcium Molybdate Films Prepared Through Chemical Solution Processing

Low-temperature preparation and characterization of strontium molybdate thin films

Experimental Researches on the Growth Characteristics of SrMoO4 Thin Film Prepared by Electrochemical Technique

Temperature dependence of scintillation properties of SrMoO4

Synthesis of Crystallized Barium Molybdate Film Via Chemical Solution Processing

Synthesis and characterization of calcium molybdate polycrystalline thin film

Phase evolution and photoluminescence behavior of MMoO4 (M = Mg, Ca, Sr) phosphors

Anti-thermal quenching behavior of Sm3+ doped SrMoO4 phosphor for new application in temperature sensing

Fabrication and Luminescence of Molybdate Films Prepared by Cell Electrochemical Method at Room Temperature