Interstitial nitrogen Atomic effect on the magnetic properties of Nd2Fe14B compound
Liang Zha,Zhongchong Lin,Fanggui Wang,Zhou Liu,Mingzhu Xue,Jie Yang,Wenyun Yang,Guang Tian,Jingzhi Han,Changsheng Wang,Honglin Du,Yingchang Yang,Jinbo Yang
DOI: https://doi.org/10.1016/j.jmmm.2020.167128
IF: 3.097
2020-11-01
Journal of Magnetism and Magnetic Materials
Abstract:The quaternary interstitial nitrides Nd2Fe14BNδ was synthesized through the gas-solid reaction of N2 gas and Nd2Fe14B powders. It was found that Nd2Fe14BNδ alloy maintains the tetragonal structure (space group P42/mnm) with an expansion of the unit cell. Structure analyses showed the nitrogen concentration (δ) is about 0.352(48) with the volume-expansion ratio (ΔV/V) of 0.6613% in the unit cell. Refinement of neutron diffraction data indicated that the N has a site occupation preference (8:3) for the 4e (0, 0, 0.0652) site over the 4f (0.1000, 0.1000, 0) site. The room temperature saturation magnetization and the magnetocrystalline anisotropy field of Nd2Fe14BNδ slightly decrease by about 6% and 5% as compared to the parent alloy, respectively. The Curie temperature of Nd2Fe14B compound increases from 312 °C to 331 °C after nitrogenation with such a subtle volume expansion, which provides a validation prediction that we may increase the volume-expansion ratio to improve Tc further. Therefore, Nd2Fe14BNδ, with better temperature stability could be obtained.
materials science, multidisciplinary,physics, condensed matter