Large-Scale Thin CsPbBr 3 Single-Crystal Film Grown on Sapphire via Chemical Vapor Deposition: Toward Laser Array Application
Yangguang Zhong,Kun Liao,Wenna Du,Jiangrui Zhu,Qiuyu Shang,Fan Zhou,Xianxin Wu,Xinyu Sui,Jianwei Shi,Shuai Yue,Qi Wang,Yanfeng Zhang,Qing Zhang,Xiaoyong Hu,Xinfeng Liu
DOI: https://doi.org/10.1021/acsnano.0c06380
IF: 17.1
2020-11-10
ACS Nano
Abstract:Single-crystal perovskites with excellent photophysical properties are considered to be ideal materials for optoelectronic devices, such as lasers, light-emitting diodes and photodetectors. However, the growth of large-scale perovskite single-crystal films (SCFs) with high optical gain by vapor-phase epitaxy remains challenging. Herein, we demonstrated a facile method to fabricate large-scale thin CsPbBr<sub>3</sub> SCFs (∼300 nm) on the <i>c</i>-plane sapphire substrate. High temperature is found to be the key parameter to control low reactant concentration and sufficient surface diffusion length for the growth of continuous CsPbBr<sub>3</sub> SCFs. Through the comprehensive study of the carrier dynamics, we clarify that the trapped-related exciton recombination has the main effect under low carrier density, while the recombination of excitons and free carriers coexist until free carriers plays the dominate role with increasing carrier density. Furthermore, an extremely low-threshold (∼8 μJ cm<sup>–2</sup>) amplified spontaneous emission was achieved at room temperature due to the high optical gain up to 1255 cm<sup>–1</sup> at a pump power of 20 times threshold (∼20 <i>P</i><sub>th</sub>). A microdisk array was prepared using a focused ion beam etching method, and a single-mode laser was achieved on a 3 μm diameter disk with the threshold of 1.6 μJ cm<sup>–2</sup>. Our experimental results not only present a versatile method to fabricate large-scale SCFs of CsPbBr<sub>3</sub> but also supply an arena to boost the optoelectronic applications of CsPbBr<sub>3</sub> with high performance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c06380?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c06380</a>.CsPbBr<sub>3</sub> SCFs growth experimental details, additional structure and optical property characterization of CsPbBr<sub>3</sub> SCFs with optical images, SEM images, XRD patterns, PL and TA spectra, ASE and optical gain analysis; microdisk array lasing performance; calculation of carrier density and Mott density, steady-state absorption spectrum analysis, carrier recombination models analysis and discussion (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c06380/suppl_file/nn0c06380_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology