Abstract:Single-crystal perovskites with excellent photophysical properties are considered to be ideal materials for optoelectronic devices, such as lasers, light-emitting diodes and photodetectors. However, the growth of large-scale perovskite single-crystal films (SCFs) with high optical gain by vapor-phase epitaxy remains challenging. Herein, we demonstrated a facile method to fabricate large-scale thin CsPbBr3 SCFs (∼300 nm) on the c-plane sapphire substrate. High temperature is found to be the key parameter to control low reactant concentration and sufficient surface diffusion length for the growth of continuous CsPbBr3 SCFs. Through the comprehensive study of the carrier dynamics, we clarify that the trapped-related exciton recombination has the main effect under low carrier density, while the recombination of excitons and free carriers coexist until free carriers plays the dominate role with increasing carrier density. Furthermore, an extremely low-threshold (∼8 μJ cm–2) amplified spontaneous emission was achieved at room temperature due to the high optical gain up to 1255 cm–1 at a pump power of 20 times threshold (∼20 Pth). A microdisk array was prepared using a focused ion beam etching method, and a single-mode laser was achieved on a 3 μm diameter disk with the threshold of 1.6 μJ cm–2. Our experimental results not only present a versatile method to fabricate large-scale SCFs of CsPbBr3 but also supply an arena to boost the optoelectronic applications of CsPbBr3 with high performance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c06380?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c06380</a>.CsPbBr3 SCFs growth experimental details, additional structure and optical property characterization of CsPbBr3 SCFs with optical images, SEM images, XRD patterns, PL and TA spectra, ASE and optical gain analysis; microdisk array lasing performance; calculation of carrier density and Mott density, steady-state absorption spectrum analysis, carrier recombination models analysis and discussion (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c06380/suppl_file/nn0c06380_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

CALCULATION OF RF PROPERTIES OF THE THIRD HARMONIC CAVITY

Periodic Organic–Inorganic Halide Perovskite Microplatelet Arrays on Silicon Substrates for Room‐Temperature Lasing

CsPbBr3 Microarrays with Tunable Periodicity, Optoelectronic and Field Emission Properties Using Self-Assembled Polystyrene Template and Co-Evaporation Method.

Microstructure‐Assisted Wafer‐Scale Fabrication of Perovskite Microlaser Arrays

Controllable Growth of Aligned Monocrystalline CsPbBr3 Microwire Arrays for Piezoelectric‐Induced Dynamic Modulation of Single‐Mode Lasing

Controlled on-chip fabrication of large-scale perovskite single crystal arrays for high-performance laser and photodetector integration

In Situ Low-Temperature Growth and Superior Luminescent Property of Well-Aligned, High-Quality Cubic CsPbBr3 Micrometer-Scale Single Crystal Arrays on Transparent Conductive Substrates.

Realizing CsPbBr3 Light-Emitting Diode Arrays Based on PDMS Template Confined Solution Growth of Single-Crystalline Perovskite.

High-Resolution In Situ Crystallization and Patterning of a CsPbBr 3 Film via Femtosecond Laser Printing

Direct Imprinting of Laser Field on Halide Perovskite Single Crystal for Advanced Photonic Applications

Large-Scale Thin CsPbBr3 Single-Crystal Film Grown on Sapphire Via Chemical Vapor Deposition: Toward Laser Array Application

On-site growth of perovskite nanocrystal arrays for integrated nanodevices

Mask-Free Patterned Perovskite Microcavity Arrays via Inkjet Printing Targeting Laser Emission

A general method for growth of perovskite single-crystal arrays for high performance photodetectors

High-Resolution in Situ Crystallization and Patterning of a CsPbBr3 Film Via Femtosecond Laser Printing

Pattern-Selective Molecular Epitaxial Growth of Single-Crystalline Perovskite Arrays toward Ultrasensitive and Ultrafast Photodetector

Femtosecond Laser Direct Ablating Micro/Nanostructures and Micropatterns on Ch3nh3pbi3 Single Crystal

Large-Scale Thin CsPbBr 3 Single-Crystal Film Grown on Sapphire via Chemical Vapor Deposition: Toward Laser Array Application

Precise In-Situ Modulation of Bandgap-Controlled Single-Crystalline Perovskite Microlasers

Self‐Healing Lithographic Patterning of Perovskite Nanocrystals for Large‐Area Single‐Mode Laser Array

Patterning All‐Inorganic Halide Perovskite with Adjustable Phase for High‐Resolution Color Filter and Photodetector Arrays