Abstract:Using granulated blast furnace slag (GGBS) as the volcanic ash material and fly ash (FA) as the supplementary material, the study was conducted to investigate the mix proportions of an alkali-activated solid waste cementitious material under the stimulating effect of alkali activator carbide slag (CS). This type of cementitious material could serve as a substitute for a portion of cement usage, contributing to resource conservation and mitigating environmental pollution caused by solid waste. This facilitates green and sustainable development. Firstly, an analysis of three raw materials was conducted, and the mix proportions were designed with reference to the CaO-Al 2 O 3 -SiO 2 system of Portland cement. Then 28 groups of specimens were prepared based on the designed mix proportions. The flowability and setting time of each group of specimens were tested. It was observed that an increase in the amount of CS and a decrease in the amount of GGBS resulted in decreased flowability and earlier setting times of the specimens. Additionally, FA exhibited a retarding effect on setting time. Compressive strength tests were conducted on these specimens, revealing that the optimal CS content ranged between 20 % and 40 %. Overall, FA had minimal impact on compressive strength, but it contributed to increased compressive strength in the specimens at later ages. Subsequently, microscopic characterization of the hydration products was performed using X-ray Diffraction (XRD), Fourier Transform Infrared (FTIR), Differential Thermal Analysis (DTA), Scanning Electron Microscope (SEM), and Energy Dispersive Spectrometer (EDS). The hydration products were identified as predominantly composed of calcium silicate hydrate. The quality and defects in the microstructure of gel products from various specimen formulations were compared to elucidate differences in macroscopic performance. Finally, the hydration process mechanism diagram of alkali-activated materials was presented to illustrate the stimulation and formation of gel products, primarily composed of C-S-H. This diagram revealed the principles behind the action of alkali-activated cementitious materials. The proposed design and testing methodology for the GGBS-FA-CS system in this study had certain reference significance for research in the direction of alkali-activated solid waste cementitious materials.

Synergistic Effect and Mechanism of Waste Glass on the Mechanical Properties and Autoclave Stability of Cementitious Materials Containing Steel Slag

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Enhanced hydration and mechanical properties of cement-based materials with steel slag modified by water glass

Performance of concrete with the incorporation of waste from the process of stoning and polishing of glass as partial replacement of cement

Assessing the modification efficiency of waste glass powder in hydraulic construction materials

Resource utilization of solid waste from steel industries in cement-based cementitious materials: Mechanical properties, hydration behaviors, and environmental impact

Effect of Steel Slag and Granulated Blast-furnace Slag on the Mechanical Strength and Pore Structure of Cement Composites

Study on the Alkali–Sulfur Co-Activation and Mechanical Properties of Low-Carbon Cementitious Composite Materials Based on Electrolytic Manganese Residue, Carbide Slag, and Granulated Blast-Furnace Slag

Effects of Waste Glass Powder on Rheological and Mechanical Properties of Calcium Carbide Residue Alkali-Activated Composite Cementitious Materials System

Reuse of urban and industrial waste glass as a novel activator for alkali-activated slag cement pastes: a case study

Synergistic Activation Mechanism and Long-Term Properties of a Solid Waste Cementitious Materials Based on Red Mud and Calcium Carbide Slag

Feasibility of Preparing Steel Slag–Ground Granulated Blast Furnace Slag Cementitious Materials: Synergistic Hydration, Fresh, and Hardened Properties

Feasibility of using Cr-containing vitrification product as cement admixture: Structural evolution and chromium immobilization

Analysis of Hydration Mechanism of Steel Slag-Based Cementitious Materials under Saline–Alkaline-Coupled Excitation

Mechanical properties and chemical microscopic characteristics of all-solid-waste composite cementitious materials prepared from phosphogypsum and granulated blast furnace slag

Molecular characterization of parthenogenic Fasciola sp. in Korea on the basis of DNA sequences of ribosomal ITS1 and mitochondrial NDI gene.

Study on the preparation, performance, and mechanism for solid waste cementitious materials

Performance of a steel slag-based supplementary cementitious material via the synergistic modification of binary fly ash and gypsum system

Preparation of steel slag-based cementitious materials compounded with GBFS and phosphogypsum: mix design, hydration, and microstructure characteristic

Effect of Waste Ceramic Powder on Properties of Alkali-Activated Blast Furnace Slag Paste and Mortar

Preparation of concrete from vitrified slag: process parameter optimization and characterization