Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Influence of Dissolved Oxygen on the Corrosion of Mild Steel in a Simulated Cement Pore Solution under Supercritical Carbon Dioxide

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

The Impact of Oxygen Availability on Steel Corrosion Considering the Self-Balance Between Anodic and Cathodic Corrosion Cells

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

Effect of High-Concentration O2on Corrosion Behavior of X70 Steel in Water-Containing Supercritical CO2with SO2

Influence of the Dissolved Oxygen Concentration in Artificial Seawater on the Corrosion Behavior of Q235 Mild Steel

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Molecular Dynamics Simulation of Reinforcing Steel Corrosion when Subjected to Both Chloride Attack and Mechanical Loading

Impact of O2 Content on the Corrosion Behavior of X65 Mild Steel in Gaseous, Liquid and Supercritical CO2 Environments

Impact of SO2 Concentration on the Corrosion Rate of X70 Steel and Iron in Water-Saturated Supercritical CO2 Mixed with SO2

Effect of impurities on the corrosion behavior of CO2 transmission pipeline steel in supercritical CO2-water environments

Coupling Effects of pH and Dissolved Oxygen on the Corrosion Behavior and Mechanism of X80 Steel in Acidic Soil Simulated Solution

Dynamic Self-Balanced Electrochemical Model for Non-Uniform Corrosion of Steel Reinforcement in Concrete under Combined Effects of Heat-Moisture-chlorine-oxygen

Effect of Flow on the Corrosion Behavior of Pipeline Steel in Supercritical CO2 Environments with Impurities

Impact of residual cementite on inhibition of CO 2 corrosion of mild steel

Influence of oxygen partial pressure on the passivation and depassivation of super 13Cr stainless steel in high temperature and CO2 rich environment

Corrosion Behavior and Mechanism of Oil Casing Steel in CO2 Salt Solution

Research of CO_2 Corrosion Kinetics of Tubing and Casing Steel P110

Failure analysis of corrosion products formed during CO2 pre-corrosion of X70 and 3Cr steels: Effect of oxygen contamination

Effect of SO42− in aerobic/anaerobic environment and its interaction with HCO3− on corrosion behavior of carbon steel

Cross Impact of CO2 Phase and Impurities on the Corrosion Behavior for Stainless Steel and Carbon Steel in Water-Containing Dense CO2 Environments