Influence of CO 2 subcritical and supercritical pressures on the protective properties of corrosion product scales formed on X65 steel
Tania Regina Schmitz de Azevedo Rodrigues,Juliane Bernardes Marcolino,Martimiano Krusciel de Moraes,Natália Feijó Lopes,Eleani Maria da Costa
DOI: https://doi.org/10.1016/j.supflu.2024.106184
IF: 3.9
2024-01-13
The Journal of Supercritical Fluids
Abstract:The effects of subcritical and supercritical pressures on CO 2 -corrosion and scale properties were investigated. The corrosion of the API5L X65 steel was carried out in wet CO 2 and CO 2 -saturated water environments at 50oC for periods of 168 and 360 h. Corrosion rates were quantified through weight loss, while scale properties were obtained by scanning electron microscopy, X-ray diffraction, linear potentiodynamic polarization (PP), and electrochemical impedance spectroscopy (EIS) techniques. Corrosion rates were higher in CO 2 -saturated water (0.59–5.09 mm/y) compared to the wet CO 2 environment (0.05–0.09 mm/y). Through a comprehensive analysis, it was observed that scales tended to become more compact with increasing pressure, decreasing the corrosion rate over time. Moreover, FeCO 3 scales formed under supercritical pressures and in CO 2 -saturated water demonstrated enhanced protective properties, as evidenced by the PP and EIS results. For these environmental conditions, the polarization and charge transfer resistances reached values of 3 × 10 6 to 6 × 10 6 and 3 × 10 6 to 1 × 10 7 Ω.cm 2 , respectively.
engineering, chemical,chemistry, physical