Abstract:Research on Cr-coated Zircaloy (Zry) as the most near-term solution for Accident-Tolerant-Fuel (ATF) concept has been boosted in the last decade, while a great concern is addressed on the interfacial failure between coating and substrate. In this study, Cr-Zry bilayer plates were firstly prepared using the diffusion bonding method at different temperatures (1073 and 1273K), subsequently the tensile tests were performed at RT and 573K. The finite element method (FEM) was further applied to simulate the stress distribution and evolution in the Cr-Zry specimen during the tensile test by ABAQUS. The results show that the Cr-Zry bilayer specimens exhibit distinctly different deformation behaviors between RT and 573 K: a two-stage deformation is noted for RT test and no sudden mechanical response for 573 K test, which is attributed to the ductile-to-brittle-transition of Cr. Besides, the fractography reveals delamination and cracks near the Cr/Zry interface at 1273 K-bonded specimens, indicating weak bonding with a higher presence of ZrCr2. Cracks initiating at the interface propagate to the two layers when plastic deformation occurs, caused by the local stress concentration and the followed prefracture at the interface. The presence of interlaminar shear stress is confirmed by FEM simulation, which is due to the transverse stress difference between Cr and Zry layers in the vicinity of the interface, which is probably responsible for the delamination of the Cr-layer. The obtained insights from this study indicate that the Cr-Zircaloy-4 interface is a weak point for Cr-Zry system materials, which will be essential to understand the mechanical behavior of Cr-coated Zr-based ATF claddings in reactors.

Temperature-dependent Deformation and Cracking Behavior in Cr Coating for Accident Tolerant Fuel Cladding: an in Situ SEM Study

In-situ study on the microstructure and cracking behavior of annealed Cr coated Zr-4 alloy

In-situ study on the tensile property and fracture behavior of Cr coating for nuclear fuel cladding

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Mechanical property and cracking mechanism of Cr-coated Zr alloy under tensile and compressive loading

In situ X-ray computed micro-tomography imaging of failure processes in Cr-coated Zircaloy nuclear fuel cladding materials

INVESTIGATION OF THE DEFORMATION BEHAVIORS OF DIFFUSION-BONDED CR-ZIRCALOY BILAYER MATERIALS UNDER TENSILE TESTS

Expansion Deformation Mechanism and Cracking Behaviours of Chromium-Coated Zirconium Alloy Cladding at Room Temperature

Expansion deformation mechanism and cracking behaviors of chromium-coated zirconium alloy cladding at room temperature

High-Temperature Oxidation And Tensile Behaviors Of Cral Coating On Zirconium Alloy

Early-stage Diffusion and Oxidation Behavior of Cr-Nb Coated Zr Alloy Accident Tolerant Fuel Cladding Materials at 1200°C - 1500°C

Thermal Stability of the Cr-coated Zirconium Alloy Microstructure Prepared by Pulsed Laser Deposition

Tem Characterizations of a Zro2/Cr Composite Coating on Zr-1nb Alloy after 1200°C Steam Oxidation

Xe20+ ions irradiation and autoclave corrosion coupled with steam oxidation behaviors of FeCrAlMoSiY-coated Zr claddings

Cleavage Cracking of Ductile-Metal Substrates Induced by Brittle Coating Fracture

Review on chromium coated zirconium alloy accident tolerant fuel cladding

The high-temperature oxidation and mechanical properties of the Cr/Zr and CrN/Zr coating

Effect of temperature on the fretting wear behavior of Cr-coated Zircaloy cladding in high-temperature pressurized water

Micro-mechanical evaluations of adhesion properties for Cr-coated accident tolerant fuel cladding

Diffusion and Oxidation Behavior of Cr-Zrn Coated Zr Alloy Accident Tolerant Fuel Cladding Materials at High Temperature

Insights into 1200 °C steam oxidation behavior of Cr coatings with different microstructure on Zircaloy-4 alloys for enhanced accident tolerant fuel cladding