Abstract:Dual phase (DP) steels are amongst the most widely used structural steels for automotive applications. It is essential to understand the damage initiation and damage growth in these high strength steels and further shed light on improving mechanical properties. In this work, two DP800 dual phase grades are investigated, which exhibit identical ultimate tensile stress but significantly different elongation in the uniaxial tensile test. To explain the difference in ductility, particularly described by uniform elongation, we investigate the damage initiation and growth mechanisms by analyzing microstructural changes upon deformation, such as voids, dislocation structures and the grain morphology. Furthermore, ferrite micropillars in pre-strained samples are tested in situ to capture the strain hardening capability of ferrite. We found that the DP steel with harder martensite and softer ferrite exhibits more damage initiation sites after deforming to an identical strain. However, void growth is much slower compared to the DP steel grade with fewer initiation sites. We explain the suppressed void growth by significant strain-hardening of ferrite surrounding the voids, which is observed in the micropillar compression experiments. The improved strain hardening of ferrite originates primarily from the difference in chromium content considering the negligible influence of dispersed particles.

Study on Bending Beam Delayed Cracking of Ultra High-strength DP Steel for Automotive Use

Delayed fracture property of 1180 MPa grade ultra high-strength steel sheet used for automotive

Study on Deep Drawing Delayed Fracture Properties of 980MPa Steel Thin Sheets for Automotive

Research on Microstructure and Property of Hot-Rolled 700MPa Grade Automobile Sheet

Study on Salt Spray Delayed Cracking Performance of Ultra-high Strength Martensitic Steel

Research and development of steel for ultra-light automotive

STUDY OF FAILURE CRITERION OF ADVANCED HIGH STRENGTH STEEL

Analysis of the delayed cracking mechanism of an industrial hot-dip galvanized DP1180GI steel coil

Shear Fracture of Advanced High Strength Steels

Fatigue crack initiation and competitive crack propagation behavior in 500 MPa grade automobile beam steel

Complex Deformation Behavior of GPa Grade Advanced High-strength Automotive Steel

Experimental and Numerical Study on Surface Damage of Dual-Phase Steel Sheet During Stamping

Effect of pre-strain on critical conditions for hydrogen-induced delayed cracking and crack nucleation characteristic of DP1180 steel

Understanding the damage initiation and growth mechanisms of two DP800 dual phase grades

Progress and Perspective of Ultra-High-Strength Martensitic Steels for Automobile

Design and Characterization of Ultrahigh Strength Dual-Phase Steel with Low Ratio of Yield Strength/Ultimate Tensile Strength

Failure Mode And Ductility Of Dual Phase Steel With Edge Crack

Microstructure and mechanical properties of thermal simulation CGHAZ of DP780 high strength steel

Assessment of the Hardening Behavior and Tensile Properties of a Cold-Rolled Bainitic-Ferritic Steel

Fracture of dual phase steel sheets under uniaxial tension (I): experimental study with dic techniques

Experimental Research of Prestrain Effects on Mechanical Behavior of Dual Phase Steel