Research on Ultra--high--strength--steel Hot Stamping Process of Automotive Anti--collision Beam

庄百亮,单忠德,姜超,戎文娟

DOI: https://doi.org/10.3969/j.issn.1004-132X.2012.02.022

2012-01-01

Abstract:Ultra--high--strength--steel hot stamping process of automotive anti--collision beam combining with numerical simulation and experiments were completed were completed. Through ana- lyzing the properties of the material BR1500HS, process parameters were optimized and a relational model among forming force, initial deformation temperature and pressing speed was built with the help of computer simulation as example of door beam,and the variation trend of forming ~orce was al- so shown clearly. The mechanical property testing shows that the hardness and thickness distribution of formed parts are uniformity; the average hardness is 47.6HRC and the largest thinning ratio is 17%, tensile strength of formed parts achieves 1545MPa which is 5 times as the maximum residual stress with little spring--back, and that microstructure of lath martensite is homogenous.