Exploration of hot stamping heating parameters and mechanical properties for 38MnB5 hot-rolled steel plate

Guo Dongdong,Luo Jianbin,Zhai Shuji,Ma Qingxian

DOI: https://doi.org/10.13330/j.issn.1000-3940.2019.01.023

2019-01-01

Abstract:The lightweight development of military armored vehicles puts forward higher requirements for the forming process and material properties of high strength steel.In order to improve the armor protection performance of materials, the microstructure and grain size of38MnB5 hot-rolled steel plate with 8 mm thickness were studied under different heating temperatures and holding times to obtain suitable hot stamping heating parameters, and the mechanical properties of material were tested and analyzed by tensile, impact and armor piercing tests at room temperature.The results show that the suitable hot stamping heating temperature is 950℃, and the holding time is 12 min.Under this condition, the austenite transformation is complete, and the grain size is basically the same and evenly distributed.However, after water quenching, the plasticity and toughness of material are very poor, and the intergranular brittleness is serious.Furthermore, the hot stamping test is conducted by a flat die with cooling water, the tensile strength of the obtained steel plate is 1925 MPa, the elongation is 9.1％, the surface hardness is 52 HRC, and the plasticity and impact toughness are greatly improved.In the armor piercing failure test, the craters depths are 2-3 mm, and the back of craters on steel plate is flat without obvious protrusion which proves good bulletproof performance.